A series of macroporous CuO-ZnO-ZrO2 （CZZ） catalysts with different Zn/Zr ratios were successfully prepared by template method and characterized by X-ray diffraction （XRD）, N2 adsorption, reactive N2O adsorption, ...A series of macroporous CuO-ZnO-ZrO2 （CZZ） catalysts with different Zn/Zr ratios were successfully prepared by template method and characterized by X-ray diffraction （XRD）, N2 adsorption, reactive N2O adsorption, scanning electron microscopy （SEM）, H2 temperature-pro- grammed reduction （H2-TPR）, and transmission electron microscopy （TEM）. The activity of the catalysts was tested for methanol synthesis from CO2 hydrogenation. It is found that the increase in the Zn/Zr ratio could lead to the sintering of the catalysts, destroying the macroporous structure integrity. The macroporous CZZ catalysts own lower Zn/Zr ratio, exhibiting a better morphology and activity. For comparison, the conventional nonporous CZZ catalysts were also investigated. The results show that the CZZ catalysts with macroporous structure own smaller particles, higher CO2 conversion, and CH3OH yield. It reveals that the macroporous structure could inhibit the growth of the par- ticle size, and the special porous structure is favorable for diffusion and penetration of CO2, which could improve the catalytic activities.展开更多
In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for met...In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for methanol synthesis. In this work, the catalyst, whose activity increases with the reaction temperature and pressure, was studied at calcined, reduced, and reacted conditions. TEM and EDX images for the calcined and reduced catalysts showed that copper was distributed uniformly at both conditions. TPR profile revealed two reduction peaks at 165 and 195 °C for copper species in the calcined catalyst. QXAFS results demonstrated that the calcined form consisted mainly of a mixed Cu O and Zn O, and it was progressively transformed into Cu metal particles and dispersed Zn O species as the reduction treatment. It was demonstrated that activation of the catalyst precursor occurred via a Cu^+intermediate, and the active catalyst predominantly consisted of metallic Cu and Zn O evenunder higher pressures. Structure of the active catalyst did not change with the temperature or pressure, indicating that the role of the Zn was mainly to improve Cu dispersion.This indicates the potential of QXAFS method in studying the structure evolutions of catalysts in methanol synthesis.展开更多
基金financially supported by the National Key Technologies Research & Development Program of China(No.2011BAC01B03)the National Natural Science Foundation of China(No.51304099)+1 种基金the Applied Basic Research Program of Yunnan Province(No.2013FZ035)the Testing and Analyzing Foundation of Kunming University of Science and Technology(No. 2010213)
文摘A series of macroporous CuO-ZnO-ZrO2 （CZZ） catalysts with different Zn/Zr ratios were successfully prepared by template method and characterized by X-ray diffraction （XRD）, N2 adsorption, reactive N2O adsorption, scanning electron microscopy （SEM）, H2 temperature-pro- grammed reduction （H2-TPR）, and transmission electron microscopy （TEM）. The activity of the catalysts was tested for methanol synthesis from CO2 hydrogenation. It is found that the increase in the Zn/Zr ratio could lead to the sintering of the catalysts, destroying the macroporous structure integrity. The macroporous CZZ catalysts own lower Zn/Zr ratio, exhibiting a better morphology and activity. For comparison, the conventional nonporous CZZ catalysts were also investigated. The results show that the CZZ catalysts with macroporous structure own smaller particles, higher CO2 conversion, and CH3OH yield. It reveals that the macroporous structure could inhibit the growth of the par- ticle size, and the special porous structure is favorable for diffusion and penetration of CO2, which could improve the catalytic activities.
基金supported by the National Basic Research Program of China(973 Program,2013CB933104)the National Natural Science Foundation of China(Nos.11275258 and 11135008)
文摘In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for methanol synthesis. In this work, the catalyst, whose activity increases with the reaction temperature and pressure, was studied at calcined, reduced, and reacted conditions. TEM and EDX images for the calcined and reduced catalysts showed that copper was distributed uniformly at both conditions. TPR profile revealed two reduction peaks at 165 and 195 °C for copper species in the calcined catalyst. QXAFS results demonstrated that the calcined form consisted mainly of a mixed Cu O and Zn O, and it was progressively transformed into Cu metal particles and dispersed Zn O species as the reduction treatment. It was demonstrated that activation of the catalyst precursor occurred via a Cu^+intermediate, and the active catalyst predominantly consisted of metallic Cu and Zn O evenunder higher pressures. Structure of the active catalyst did not change with the temperature or pressure, indicating that the role of the Zn was mainly to improve Cu dispersion.This indicates the potential of QXAFS method in studying the structure evolutions of catalysts in methanol synthesis.