Nanometer SnO2 particles were synthesized by sol-gel dialytic processes and used as a support to prepare CuO supported catalysts via a deposition-precipitation method. The samples were characterized by means of TG-DTA...Nanometer SnO2 particles were synthesized by sol-gel dialytic processes and used as a support to prepare CuO supported catalysts via a deposition-precipitation method. The samples were characterized by means of TG-DTA, XRD, H2-TPR and XPS. The catalytic activity of the CuO/TiO2-SnO2 catalysts was markedly depended on the loading of CuO, and the optimum CuO loading was 8 wt.% （Tloo = 80 ℃）. The CuO/TiO2-SnO2 catalysts exhibited much higher catalytic activity than the CuO/TiO2 and CuO/SnO2 catalysts. H2-TPR result indicated that a large amount of CuO formed the active site for CO oxidation in 8 wt.% CuO/TiO2-SnO2 catalyst.展开更多
In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for met...In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for methanol synthesis. In this work, the catalyst, whose activity increases with the reaction temperature and pressure, was studied at calcined, reduced, and reacted conditions. TEM and EDX images for the calcined and reduced catalysts showed that copper was distributed uniformly at both conditions. TPR profile revealed two reduction peaks at 165 and 195 °C for copper species in the calcined catalyst. QXAFS results demonstrated that the calcined form consisted mainly of a mixed Cu O and Zn O, and it was progressively transformed into Cu metal particles and dispersed Zn O species as the reduction treatment. It was demonstrated that activation of the catalyst precursor occurred via a Cu^+intermediate, and the active catalyst predominantly consisted of metallic Cu and Zn O evenunder higher pressures. Structure of the active catalyst did not change with the temperature or pressure, indicating that the role of the Zn was mainly to improve Cu dispersion.This indicates the potential of QXAFS method in studying the structure evolutions of catalysts in methanol synthesis.展开更多
The CuO/CeO2 catalysts were investigated by means of X-ray diffraction （XRD）, laser Raman spectroscopy （LRS）, X-ray photoelectronic spectroscopy （XPS）, temperature-programmed reduction （TPR）, in situ Fourier t...The CuO/CeO2 catalysts were investigated by means of X-ray diffraction （XRD）, laser Raman spectroscopy （LRS）, X-ray photoelectronic spectroscopy （XPS）, temperature-programmed reduction （TPR）, in situ Fourier transform infrared spectroscopy （FTIR） and NO＋CO reaction. The results revealed that the low temperature （〈150℃） catalytic performances were enhanced for CO pretreated samples. During CO pretreatment, the surface Cu＋/Cu0 and oxygen vacancies on ceria surface were present. The low va- lence copper species activated the adsorbed CO and surface oxygen vacancies facilitated the NO dissociation. These effects in turn led to higher activities of CuO/CeO2 for NO reduction. The current study provided helpful understandings of active sites and reaction mechanism in NO＋CO reaction.展开更多
CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were ...CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/ CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.展开更多
The CuO/γ-Al2O3/cordierite catalyst, after being sulfated by sulfur dioxide (SO2) at 673 K, exhibits high activities for selective catalytic reduction (SCR) of nitrogen oxide (NO) with ammonia (NH3) at 573-723 K. The...The CuO/γ-Al2O3/cordierite catalyst, after being sulfated by sulfur dioxide (SO2) at 673 K, exhibits high activities for selective catalytic reduction (SCR) of nitrogen oxide (NO) with ammonia (NH3) at 573-723 K. The intrinsic kinetics of SCR of NO with NH3 over CuO/γ-Al2O3/cordierite catalyst has been measured in a fixed-bed reactor in the absence of internal and external diffusions. The experimental results show that the reaction rate can be quantified by a first-order expression with activation energy Eá of 94.01 kJ·mol-1 and the corresponding p re-exponential factor A′ of 3.39×108 cm3·g-1·s-1 when NH3 is excessive. However, when NH3 is not enough, an E ley-Rideal kinetic model based on experimental data is derived with Ea of 105.79 kJ·mol-1, the corresponding A of 2 .94×109 cm3·g-1·s-1, heat of adsorption-Hads of 87.90 kJ·mol-1 and the corresponding Aads of 9.24 cm3·mol-1. The intrinsic kinetic model obtained was incorporated in a 3D mathematical model of monolithic reactor, and the agreement of the prediction with experimental data indicates that the present kinetic model is adequate for the reac-tor design and engineering scale-up.展开更多
Three series of CeO2/CuO samples were prepared by impregnation method and characterized by XRD, N2 adsorption-desorption, temperatureprogrammed reduction （TPR）, XPS and TEM techniques. In comparison with the samples...Three series of CeO2/CuO samples were prepared by impregnation method and characterized by XRD, N2 adsorption-desorption, temperatureprogrammed reduction （TPR）, XPS and TEM techniques. In comparison with the samples prepared with CuO as initial support, the samples with Cu（OH）2 as initial support have higher reducibilities and smaller relative TPR peak areas, and also larger specific surface areas at calcina- tion temperatures of 400 ℃--600 ℃. As a result, Cu（OH）2 is better than CuO as initial support for preferential oxidation of CO in excess H2 （CO-PROX）. The best catalytic performance was achieved on the sample calcined at 600 ℃ and with an atomic ratio of Ce/Cu at 40%. XPS analyses indicate that more interface linkages Ce-O-Cu could be formed when it was calcined at 600 ℃. And the atomic ratio of Ce/Cu at 40% led to a proper reducibility for the sample as illustrated by the TPR measurements.展开更多
The oxidative properties and characterization of CuO, CeO 2 and CuO/CeO 2 cata lysts were examined by means of a CO micro-reactor GC system, TPR, XPS and X-r ay diffraction Rietveld methods. The results show that ei...The oxidative properties and characterization of CuO, CeO 2 and CuO/CeO 2 cata lysts were examined by means of a CO micro-reactor GC system, TPR, XPS and X-r ay diffraction Rietveld methods. The results show that either CuO or CeO 2 ac tivity is quite low for CO oxidation. However, when CuO and CeO 2 are mixed, the oxidative activity of the catalyst increases significantly, probably owing to the valency status of copper species (Cu 2+ and Cu+) on the CeO 2 surfa ce, the dispersion and reducibility. XPS surface analysis shows that CuO loading is very important in forming of either Cu 2+ or Cu+. Rietveld analysis s hows that some CuO, which has smaller ion radius than Ce 4+, enters the Ce O 2 lattice after CuO and CeO 2 are mixed. When the CuO loading reaches 5.0%, the size of CuO crystals is a minimum (6.1 nm) and the micro-strain value i s a maximum (2.86×10 -3), resulting in high surface energy and the best ac tivity for CO oxidation.展开更多
Ce x Ti 1- x O 2 mixed oxides of different mole ratios ( x =0, 0.1, 0.2～0.9, 1.0) were prepared by co precipitation of TiCl 4 with Ce(NO 3) 3 and then loaded with different amounts of CuO. The effe...Ce x Ti 1- x O 2 mixed oxides of different mole ratios ( x =0, 0.1, 0.2～0.9, 1.0) were prepared by co precipitation of TiCl 4 with Ce(NO 3) 3 and then loaded with different amounts of CuO. The effects of CuO on NO+CO reaction were investigated, and the structure and reductive properties of various CuO/Ce x Ti 1- x O 2 were characterized by the methodologies of BET, TPR and XRD. The results show that different Ce/Ti mole ratios and calcination temperatures induce changes of structure and reductive properties of the Ce x Ti 1- x O 2 mixed oxides. When x =0.1～0.5, amorphous CeTi 2O 6 phase mainly forms at 650 ℃ compared to the formation of CeTi 2O 6 which crystallizes at 800 ℃. When x >0.6, some TiO 2 enters the CeO 2 lattice and a CeO 2 TiO 2 solid solution is formed. The activity of 6%CuO/Ce x Ti 1- x O 2 calcined at 650 ℃ is largely affected by the x values, which is the highest when x =0.3, 0.4 and 0.9. The NO conversion reaches 70% at a reaction temperature of 150 ℃. By comparison, the x values have little effect on the activity of 6%CuO/Ce x Ti 1- x O 2 calcined at 800 ℃ . There are strong interactions between CuO and CeTi 2O 6, i.e., formation of the CeTi 2O 6 phase shifts the CuO reduction peak temperature from 380 to 200 ℃, and CuO, in turn, shifts the CeTi 2O 6 reduction peak temperature from 600 to 300 ℃.展开更多
In this work, we have reported the influence of the addition of base （KOH） on the physicochemical property of ceria synthesized by alcohothermal process, and the alcohothermal mechanism was also put forward. Further...In this work, we have reported the influence of the addition of base （KOH） on the physicochemical property of ceria synthesized by alcohothermal process, and the alcohothermal mechanism was also put forward. Furthermore, the prepared CeO2 was used as the support to prepare CuO/CeO2 catalysts via the wet impregnation method. The samples were characterized by N2 adsorption-desorption, X-ray powder diffraction （XRD）, high resolution transmission electron microscopy （HRTEM）, and temperatureprogrammed reduction by H2 （H2-TPR）. The catalytic properties of the CuO/CeO2 catalysts for lowtemperature CO oxidation were studied using a microreactor-GC system. The crystal size of CeO2-A was much smaller than that of CeO2-B, and the corresponding copper oxide catalysts exhibited higher catalytic activity than that of the CeO2-B-supported catalysts under the same reaction conditions. The alcohothermal mechanism indicated that KOH plays a key role in determining the physicochemical and catalytic properties of ceria-based materials.展开更多
To understand the dispersion behavior of metal oxides on composite oxide supports and with the expectation of developing more feasible catalysts for soot oxidation,CuO/La_(2)Sn_(2)O_(7)samples containing varied CuO lo...To understand the dispersion behavior of metal oxides on composite oxide supports and with the expectation of developing more feasible catalysts for soot oxidation,CuO/La_(2)Sn_(2)O_(7)samples containing varied CuO loadings were fabricated and characterized by different techniques and density functional theory calculations.In these catalysts,a spontaneous dispersion of CuO on the La_(2)Sn_(2)O_(7)pyrochlore support formed,having a monolayer dispersion capacity of 1.90 mmol CuO/100 m^(2) La_(2)Sn_(2)O_(7)surface.When loaded below this capacity,CuO exists in a sub-monolayer or monolayer state.X-ray photoelectron spectroscopy(XPS),Raman spectroscopy,and Bader charge and density of states analyses indicate that there are strong interactions between the sub-monolayer/monolayer CuO and the La_(2)Sn_(2)O_(7)support,mainly through the donation of electrons from Cu to Sn at the B-sites of the structure.In contrast,Cu has negligible interactions with La at the A-sites.This suggests that,in composite oxide supports containing multiple metals,the supported metal oxide interacts preferentially with one kind of metal cation in the support.The Raman,in situ diffuse reflectance infrared Fourier transform spectroscopy,and XPS results confirmed the formation of both O2^(-)and O2^(2-)as the active sites on the surfaces of the CuO/La_(2)Sn_(2)O_(7)catalysts,and the concentration of these active species determines the soot combustion activity.The number of active oxygen anions increased with increase in CuO loading until the monolayer dispersion capacity was reached.Above the monolayer dispersion capacity,microsized CuO crystallites formed,and these had a negative effect on the generation of active surface oxygen sites.In summary,a highly active catalyst can be prepared by covering the surface of the La_(2)Sn_(2)O_(7)support with a CuO monolayer.展开更多
Using TiO2 and Ti0.5Zr0.5O2 as carriers, the CuO/TiO2 and CuO/Ti0.5Zr0.5O2 catalystswere prepared by the impregnation method with Cu(NO3)2 as active component. The catalyticactivities in NO+CO reaction were investigat...Using TiO2 and Ti0.5Zr0.5O2 as carriers, the CuO/TiO2 and CuO/Ti0.5Zr0.5O2 catalystswere prepared by the impregnation method with Cu(NO3)2 as active component. The catalyticactivities in NO+CO reaction were investigated using a microreactor-GC system, and structure andreducibility of catalysts were characterized by means of physical adsorption, TPR, XRD, NO-TPDtechnologies. It was found that the activity of CuO/Ti0.5Zr0.5O2 catalyst was higher than that ofCuO/TiO2, probably due to the large specific surface area of Ti0.5Zr0.5O2 that played an importantrole in NO+CO reaction.展开更多
This paper presented a study on the role of yttrium addition to CuO/CeO2 catalyst for water-gas shift reaction. A single-step co-precipitation method was used for preparation of a series of yttrium doped CuO/CeO2 cata...This paper presented a study on the role of yttrium addition to CuO/CeO2 catalyst for water-gas shift reaction. A single-step co-precipitation method was used for preparation of a series of yttrium doped CuO/CeO2 catalysts with yttrium content in the range of 0-5wt.%. Properties of the obtained samples were characterized and analyzed by X-ray diffraction （XRD）, Raman spectroscopy, H2-TPR, cyclic voltammetry （CV） and the BET method. The results revealed that catalytic activity was increased with the yttrium content at first, but then decreased with the further increase of yttrium content. Herein, CuO/CeO2 catalyst doped with 2wt.% of yttrium showed the highest catalytic activity （CO conversion reaches 93.4% at 250 ℃） and thermal stability for WGS reaction. The catalytic activity was correlated with the surface area, the area of peak γ of H2-TPR profile （i.e., the reduction of surface copper oxide （crystalline forms） interacted with surface oxygen vacancies on ceria）, and the area of peak C2 and A1 （Cu^0→←Cu^2＋ in cyclic voltammetry process）, respectively. Besides, Raman spectra provided evidences for a synergistic Cu-Ovacancy interaction, and it was indicated that doping yttrium may facilitate the formation of oxygen vacancies on ceria.展开更多
Effect of the addition of Sm 2O 3 on CuO γ Al 2O 3 catalyst for CO oxidation reaction was investigated. The result shows that the right amount of Sm 2O 3 can promote the adsorption of the surface oxygen a...Effect of the addition of Sm 2O 3 on CuO γ Al 2O 3 catalyst for CO oxidation reaction was investigated. The result shows that the right amount of Sm 2O 3 can promote the adsorption of the surface oxygen and recovery of CuO γ Al 2O 3 catalyst. Sm 2O 3 plays an important role in change of γ Al 2O 3 phase into θ Al 2O 3 phase. In addition, the right amount of Sm 2O 3(5%) can improve the oxidation activity of the CuO γ Al 2O 3 catalyst. Whereas an excess of Sm 2O 3(10%) makes the CuO crystal in CuO γ Al 2O 3 catalyst become bigger and restrain the oxidation activity of the CuO γ Al 2O 3 catalyst.展开更多
基金supported by the National Natural Science Foundation of China (20771061 and 20871071)the 973 Program (2005CB623607)Science and Technology Commission Foundation of Tianjin (08JCYBJC00100 and 09JCYBJC03600)
文摘Nanometer SnO2 particles were synthesized by sol-gel dialytic processes and used as a support to prepare CuO supported catalysts via a deposition-precipitation method. The samples were characterized by means of TG-DTA, XRD, H2-TPR and XPS. The catalytic activity of the CuO/TiO2-SnO2 catalysts was markedly depended on the loading of CuO, and the optimum CuO loading was 8 wt.% （Tloo = 80 ℃）. The CuO/TiO2-SnO2 catalysts exhibited much higher catalytic activity than the CuO/TiO2 and CuO/SnO2 catalysts. H2-TPR result indicated that a large amount of CuO formed the active site for CO oxidation in 8 wt.% CuO/TiO2-SnO2 catalyst.
基金supported by the National Basic Research Program of China(973 Program,2013CB933104)the National Natural Science Foundation of China(Nos.11275258 and 11135008)
文摘In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for methanol synthesis. In this work, the catalyst, whose activity increases with the reaction temperature and pressure, was studied at calcined, reduced, and reacted conditions. TEM and EDX images for the calcined and reduced catalysts showed that copper was distributed uniformly at both conditions. TPR profile revealed two reduction peaks at 165 and 195 °C for copper species in the calcined catalyst. QXAFS results demonstrated that the calcined form consisted mainly of a mixed Cu O and Zn O, and it was progressively transformed into Cu metal particles and dispersed Zn O species as the reduction treatment. It was demonstrated that activation of the catalyst precursor occurred via a Cu^+intermediate, and the active catalyst predominantly consisted of metallic Cu and Zn O evenunder higher pressures. Structure of the active catalyst did not change with the temperature or pressure, indicating that the role of the Zn was mainly to improve Cu dispersion.This indicates the potential of QXAFS method in studying the structure evolutions of catalysts in methanol synthesis.
基金supported by National Basic Research Program of China(2010CB732300)National Natural Science Foundation of China(21273110,20973091)Natural Science Foundation for the Youth(21203091)
文摘The CuO/CeO2 catalysts were investigated by means of X-ray diffraction （XRD）, laser Raman spectroscopy （LRS）, X-ray photoelectronic spectroscopy （XPS）, temperature-programmed reduction （TPR）, in situ Fourier transform infrared spectroscopy （FTIR） and NO＋CO reaction. The results revealed that the low temperature （〈150℃） catalytic performances were enhanced for CO pretreated samples. During CO pretreatment, the surface Cu＋/Cu0 and oxygen vacancies on ceria surface were present. The low va- lence copper species activated the adsorbed CO and surface oxygen vacancies facilitated the NO dissociation. These effects in turn led to higher activities of CuO/CeO2 for NO reduction. The current study provided helpful understandings of active sites and reaction mechanism in NO＋CO reaction.
基金Projected supported by the National Natural Science Foundation of China (20271028) and Tianjin Natural Science Foundation(033602511)
文摘CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/ CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.
基金Supported by the National Natural Science Foundation of China （20821004 20736001 21076008） the Research Fund for the Doctoral Program of Higher Education of China （2090010110002）
文摘The CuO/γ-Al2O3/cordierite catalyst, after being sulfated by sulfur dioxide (SO2) at 673 K, exhibits high activities for selective catalytic reduction (SCR) of nitrogen oxide (NO) with ammonia (NH3) at 573-723 K. The intrinsic kinetics of SCR of NO with NH3 over CuO/γ-Al2O3/cordierite catalyst has been measured in a fixed-bed reactor in the absence of internal and external diffusions. The experimental results show that the reaction rate can be quantified by a first-order expression with activation energy Eá of 94.01 kJ·mol-1 and the corresponding p re-exponential factor A′ of 3.39×108 cm3·g-1·s-1 when NH3 is excessive. However, when NH3 is not enough, an E ley-Rideal kinetic model based on experimental data is derived with Ea of 105.79 kJ·mol-1, the corresponding A of 2 .94×109 cm3·g-1·s-1, heat of adsorption-Hads of 87.90 kJ·mol-1 and the corresponding Aads of 9.24 cm3·mol-1. The intrinsic kinetic model obtained was incorporated in a 3D mathematical model of monolithic reactor, and the agreement of the prediction with experimental data indicates that the present kinetic model is adequate for the reac-tor design and engineering scale-up.
文摘Three series of CeO2/CuO samples were prepared by impregnation method and characterized by XRD, N2 adsorption-desorption, temperatureprogrammed reduction （TPR）, XPS and TEM techniques. In comparison with the samples prepared with CuO as initial support, the samples with Cu（OH）2 as initial support have higher reducibilities and smaller relative TPR peak areas, and also larger specific surface areas at calcina- tion temperatures of 400 ℃--600 ℃. As a result, Cu（OH）2 is better than CuO as initial support for preferential oxidation of CO in excess H2 （CO-PROX）. The best catalytic performance was achieved on the sample calcined at 600 ℃ and with an atomic ratio of Ce/Cu at 40%. XPS analyses indicate that more interface linkages Ce-O-Cu could be formed when it was calcined at 600 ℃. And the atomic ratio of Ce/Cu at 40% led to a proper reducibility for the sample as illustrated by the TPR measurements.
文摘The oxidative properties and characterization of CuO, CeO 2 and CuO/CeO 2 cata lysts were examined by means of a CO micro-reactor GC system, TPR, XPS and X-r ay diffraction Rietveld methods. The results show that either CuO or CeO 2 ac tivity is quite low for CO oxidation. However, when CuO and CeO 2 are mixed, the oxidative activity of the catalyst increases significantly, probably owing to the valency status of copper species (Cu 2+ and Cu+) on the CeO 2 surfa ce, the dispersion and reducibility. XPS surface analysis shows that CuO loading is very important in forming of either Cu 2+ or Cu+. Rietveld analysis s hows that some CuO, which has smaller ion radius than Ce 4+, enters the Ce O 2 lattice after CuO and CeO 2 are mixed. When the CuO loading reaches 5.0%, the size of CuO crystals is a minimum (6.1 nm) and the micro-strain value i s a maximum (2.86×10 -3), resulting in high surface energy and the best ac tivity for CO oxidation.
文摘Ce x Ti 1- x O 2 mixed oxides of different mole ratios ( x =0, 0.1, 0.2～0.9, 1.0) were prepared by co precipitation of TiCl 4 with Ce(NO 3) 3 and then loaded with different amounts of CuO. The effects of CuO on NO+CO reaction were investigated, and the structure and reductive properties of various CuO/Ce x Ti 1- x O 2 were characterized by the methodologies of BET, TPR and XRD. The results show that different Ce/Ti mole ratios and calcination temperatures induce changes of structure and reductive properties of the Ce x Ti 1- x O 2 mixed oxides. When x =0.1～0.5, amorphous CeTi 2O 6 phase mainly forms at 650 ℃ compared to the formation of CeTi 2O 6 which crystallizes at 800 ℃. When x >0.6, some TiO 2 enters the CeO 2 lattice and a CeO 2 TiO 2 solid solution is formed. The activity of 6%CuO/Ce x Ti 1- x O 2 calcined at 650 ℃ is largely affected by the x values, which is the highest when x =0.3, 0.4 and 0.9. The NO conversion reaches 70% at a reaction temperature of 150 ℃. By comparison, the x values have little effect on the activity of 6%CuO/Ce x Ti 1- x O 2 calcined at 800 ℃ . There are strong interactions between CuO and CeTi 2O 6, i.e., formation of the CeTi 2O 6 phase shifts the CuO reduction peak temperature from 380 to 200 ℃, and CuO, in turn, shifts the CeTi 2O 6 reduction peak temperature from 600 to 300 ℃.
文摘In this work, we have reported the influence of the addition of base （KOH） on the physicochemical property of ceria synthesized by alcohothermal process, and the alcohothermal mechanism was also put forward. Furthermore, the prepared CeO2 was used as the support to prepare CuO/CeO2 catalysts via the wet impregnation method. The samples were characterized by N2 adsorption-desorption, X-ray powder diffraction （XRD）, high resolution transmission electron microscopy （HRTEM）, and temperatureprogrammed reduction by H2 （H2-TPR）. The catalytic properties of the CuO/CeO2 catalysts for lowtemperature CO oxidation were studied using a microreactor-GC system. The crystal size of CeO2-A was much smaller than that of CeO2-B, and the corresponding copper oxide catalysts exhibited higher catalytic activity than that of the CeO2-B-supported catalysts under the same reaction conditions. The alcohothermal mechanism indicated that KOH plays a key role in determining the physicochemical and catalytic properties of ceria-based materials.
文摘To understand the dispersion behavior of metal oxides on composite oxide supports and with the expectation of developing more feasible catalysts for soot oxidation,CuO/La_(2)Sn_(2)O_(7)samples containing varied CuO loadings were fabricated and characterized by different techniques and density functional theory calculations.In these catalysts,a spontaneous dispersion of CuO on the La_(2)Sn_(2)O_(7)pyrochlore support formed,having a monolayer dispersion capacity of 1.90 mmol CuO/100 m^(2) La_(2)Sn_(2)O_(7)surface.When loaded below this capacity,CuO exists in a sub-monolayer or monolayer state.X-ray photoelectron spectroscopy(XPS),Raman spectroscopy,and Bader charge and density of states analyses indicate that there are strong interactions between the sub-monolayer/monolayer CuO and the La_(2)Sn_(2)O_(7)support,mainly through the donation of electrons from Cu to Sn at the B-sites of the structure.In contrast,Cu has negligible interactions with La at the A-sites.This suggests that,in composite oxide supports containing multiple metals,the supported metal oxide interacts preferentially with one kind of metal cation in the support.The Raman,in situ diffuse reflectance infrared Fourier transform spectroscopy,and XPS results confirmed the formation of both O2^(-)and O2^(2-)as the active sites on the surfaces of the CuO/La_(2)Sn_(2)O_(7)catalysts,and the concentration of these active species determines the soot combustion activity.The number of active oxygen anions increased with increase in CuO loading until the monolayer dispersion capacity was reached.Above the monolayer dispersion capacity,microsized CuO crystallites formed,and these had a negative effect on the generation of active surface oxygen sites.In summary,a highly active catalyst can be prepared by covering the surface of the La_(2)Sn_(2)O_(7)support with a CuO monolayer.
文摘Using TiO2 and Ti0.5Zr0.5O2 as carriers, the CuO/TiO2 and CuO/Ti0.5Zr0.5O2 catalystswere prepared by the impregnation method with Cu(NO3)2 as active component. The catalyticactivities in NO+CO reaction were investigated using a microreactor-GC system, and structure andreducibility of catalysts were characterized by means of physical adsorption, TPR, XRD, NO-TPDtechnologies. It was found that the activity of CuO/Ti0.5Zr0.5O2 catalyst was higher than that ofCuO/TiO2, probably due to the large specific surface area of Ti0.5Zr0.5O2 that played an importantrole in NO+CO reaction.
基金supported by the National Natural Science Foundation of China (20771025)A-type Science and Technology Projects of Fujian Provincial Department of Education (JA08021)
文摘This paper presented a study on the role of yttrium addition to CuO/CeO2 catalyst for water-gas shift reaction. A single-step co-precipitation method was used for preparation of a series of yttrium doped CuO/CeO2 catalysts with yttrium content in the range of 0-5wt.%. Properties of the obtained samples were characterized and analyzed by X-ray diffraction （XRD）, Raman spectroscopy, H2-TPR, cyclic voltammetry （CV） and the BET method. The results revealed that catalytic activity was increased with the yttrium content at first, but then decreased with the further increase of yttrium content. Herein, CuO/CeO2 catalyst doped with 2wt.% of yttrium showed the highest catalytic activity （CO conversion reaches 93.4% at 250 ℃） and thermal stability for WGS reaction. The catalytic activity was correlated with the surface area, the area of peak γ of H2-TPR profile （i.e., the reduction of surface copper oxide （crystalline forms） interacted with surface oxygen vacancies on ceria）, and the area of peak C2 and A1 （Cu^0→←Cu^2＋ in cyclic voltammetry process）, respectively. Besides, Raman spectra provided evidences for a synergistic Cu-Ovacancy interaction, and it was indicated that doping yttrium may facilitate the formation of oxygen vacancies on ceria.
文摘Effect of the addition of Sm 2O 3 on CuO γ Al 2O 3 catalyst for CO oxidation reaction was investigated. The result shows that the right amount of Sm 2O 3 can promote the adsorption of the surface oxygen and recovery of CuO γ Al 2O 3 catalyst. Sm 2O 3 plays an important role in change of γ Al 2O 3 phase into θ Al 2O 3 phase. In addition, the right amount of Sm 2O 3(5%) can improve the oxidation activity of the CuO γ Al 2O 3 catalyst. Whereas an excess of Sm 2O 3(10%) makes the CuO crystal in CuO γ Al 2O 3 catalyst become bigger and restrain the oxidation activity of the CuO γ Al 2O 3 catalyst.
基金supported by the National Natural Science Foundation of China(20976162,21103149,20906079)Natural Science Foundation of Zhejiang Province,China(R5100266)Significant Science and Technology Project of Zhejiang Province,China(2010C13001)~~