Cu/CeO2-ZrO2 catalysts for water-gas shift （WGS） reaction were prepared with co-precipitation method, and the influence of ZrO2 content on the catalytic structure and properties was investigated by the techniques of...Cu/CeO2-ZrO2 catalysts for water-gas shift （WGS） reaction were prepared with co-precipitation method, and the influence of ZrO2 content on the catalytic structure and properties was investigated by the techniques of N2 physical adsorption analysis, XRD and H2-TPR. The results indicate that the BET surface areas of the catalysts are increased in varying degrees due to the presence of ZrO2. With increasing ZrO2 content, the pore size distribution is centered on 1.9 nm. ZrO2 can efficiently restrain the growth of Cu crystal particles. The appropriate amount of ZrO2 in the Cu/CeO2 catalysts can help the catalyst keep better copper dispersion in the WGS reaction, which can lead to both higher catalytic activity and better thermal stability. When ZrO2 content is 10% （atom fraction）, Cu/CeO2-Zr02 catalyst reaches a CO conversion rate of 73.7% at the reaction temperature of 200℃.展开更多
The reduction of carbon emissions in the steel industry is a significant challenge,and utilizing CO_(2) from carbon intensive steel industry off-gases for methanol production is a promising strategy for decarbonizatio...The reduction of carbon emissions in the steel industry is a significant challenge,and utilizing CO_(2) from carbon intensive steel industry off-gases for methanol production is a promising strategy for decarbonization.However,steelwork off-gases typically contain various impurities,including H_(2)S,which can deactivate commercial methanol synthesis catalysts,Cu/ZnO/Al_(2)O_(3)(CZA).Reverse water-gas shift(RWGS)reaction is the predominant side reaction in CO_(2) hydrogenation to methanol which can occur at ambient pressure,enabling the decouple of RWGS from methanol production at high pressure.Then,a series of activated CZA catalysts has been in-situ pretreated in 400 ppm H_(2)S/Ar at 250℃and tested for both RWGS reaction at ambient pressure and CO_(2) hydrogenation to methanol at high pressure.An innovative decoupling strategy was employed to isolate the RWGS reaction from the methanol synthesis process,enabling the investigation of the evolution of active site structures and the poisoning mechanism through elemental analysis,X-ray Diffraction,X-ray Photoelectron Spectroscopy,Fourier Transform Infrared Spectroscopy,Temperature Programmed Reduction and CO_(2) Temperature Programmed Desorption.The results indicate that there are different dynamic migration behaviors of ZnO_(x) in the two reaction systems,leading to different poisoning mechanisms.These interesting findings are beneficial to develop sulfur resistant and durable highly efficient catalysts for CO_(2) hydrogenation to methanol,promoting the carbon emission reduction in steel industry.展开更多
Nickel and sulfate co-modified CeO2-ZrO2 catalysts were prepared by sol-gel method. The catalysts were characterized by XRD, FTIR, XPS, NH3 chemisorption and NH3-SCR activity tests. The results showed that the enhance...Nickel and sulfate co-modified CeO2-ZrO2 catalysts were prepared by sol-gel method. The catalysts were characterized by XRD, FTIR, XPS, NH3 chemisorption and NH3-SCR activity tests. The results showed that the enhanced acidity of CeO2-ZrO2 catalysts by nickel and sulfate co-modification was responsible for the broadened temperature window and improved the selectivity to N2 in NH3-SCR deNOx. The introduction of nickel to CeO2-ZrO2 solid solutions resulted in more Ce3+ on surface of catalyst, leading to an in...展开更多
CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were ...CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/ CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.展开更多
Praseodymium （Pr） was impregnated to CeO2-ZrO2 solid solution by an impregnation method. The as-obtained Pr modi- fied CeO2-ZrO2 was impregnated with 1 wt.% Pd to prepare the catalysts. The structure and reducibilit...Praseodymium （Pr） was impregnated to CeO2-ZrO2 solid solution by an impregnation method. The as-obtained Pr modi- fied CeO2-ZrO2 was impregnated with 1 wt.% Pd to prepare the catalysts. The structure and reducibility of the fresh and hydrother- really aged catalysts were characterized by X-ray diffraction （XRD）, Raman, X-ray photoelectron spectroscopy （XPS）, CO chemi- sorption and H2 temperature-programmed reduction （H2-TPR）. The oxygen storage capacity （OSC） was evaluated with CO serving as probe gas. Effects of impregnated Pr on the structure and oxygen storage capacity of catalysts were investigated. The results showed that the aged Pr-impregnated samples had much higher OSC and better reducibility than the unmodified ones. The scheme of structural evolutions of the catalysts with and without Pr was also established. Partial of the impregnated Pr diffused into the bulk of CeO2-ZrO2 during ageing, which inhibited the sintering, and increased the amount of oxygen vacancies in CeO2-ZrO2 support. Furthermore, those impregnated Pr species which covered on the surface of the support obstructed the strong metal-support interaction between Pd and Ce so as to reduce the encapsulation of Pd as well as the back spill-over of the oxygen during the catalytic process.展开更多
A series of CeO2-ZrO2-WO3 catalysts for the selective catalytic reduction （SCR） of NO with NH3 were prepared by hydrothermal method. The influence of calcination temperature on the catalytic activity, microstructure...A series of CeO2-ZrO2-WO3 catalysts for the selective catalytic reduction （SCR） of NO with NH3 were prepared by hydrothermal method. The influence of calcination temperature on the catalytic activity, microstructure, surface acidity and redox behavior of CeO2-ZrO2-WO3 catalyst was investigated using various characterization methods. It was found that the CeO2-ZrO2-WO3 catalyst calcined at 600 ℃ showed the best catalytic performance and excellent N2 selectivity, and yielded more than 90% NO conversion in a wide temperature range of 250-500 ℃ with a space velocity （GHSV） of 60000 131. As the calcination temperature was increased from 400 to 600 ℃, the NO conversion obviously increased, but decreased at higher calcination temperature. The results implied that the higher surface area, the strongest synergistic interaction, the superior redox property and the highly dispersed or amorphous WO3 species contributed to the excellent SCR activity of the CeO2-ZrO2-WO3 catalyst calcined at 600℃.展开更多
Potassium-modified ceria-zirconia catalyst was synthesized by wetness impregnation method. The ageing treatment was performed in static air at 800℃ for 20 hr to evaluate the thermal stability of the catalyst. The cat...Potassium-modified ceria-zirconia catalyst was synthesized by wetness impregnation method. The ageing treatment was performed in static air at 800℃ for 20 hr to evaluate the thermal stability of the catalyst. The catalysts were characterized by X-ray diffraction, BET surface area, oxygen storage capacity, NOx-temperature programmed desorption and soot-temperature programmed oxidation measurements. By introduction of potassium, the maximum soot oxidation rate temperature （Tin） of the ceria-zirconia based catalyst decreased from 525 to 428℃ in the presence of NO under a loose contact mode. The shift of Tm of the K-modified catalyst after ageing is only 15℃. The enhanced activity of the aged catalyst mainly lies in the promotional effect of potassium on the NOx/oxygen storage capacity as well as the soot-catalyst contact.展开更多
Ce-Zr-Al-Nd2O3 （CZAN） support materials were prepared by co-precipitation and impregnation methods, respectively. They were characterized by X-ray diffTaction （XRD）, low temperature nitrogen adsorption-desorption,...Ce-Zr-Al-Nd2O3 （CZAN） support materials were prepared by co-precipitation and impregnation methods, respectively. They were characterized by X-ray diffTaction （XRD）, low temperature nitrogen adsorption-desorption, oxygen pulsing technique, H2-temperamre programmed reduction （H2-TPR） and X-ray photoelectron spectroscopy （XPS）. The Pd-only three-way catalysts （Pd-TWC） supported on these materials were prepared by incipient wetness method and studied by activity tests. The results demonstrated that the CZAN supports obtained by the two methods showed better structural, textural and redox properties than the CZA without Nd2O3, and the addition of Nd203 improved the catalytic activity of TWC. Especially, the CZAN-i support prepared by impregnation method had better thermal stability and redox property. Meanwhile, the Pd/CZAN-i catalyst exhibited the best catalytic performance. XPS measurements indicated that the Nd-modified samples possessed more Ce3＋ and oxygen vacancies on the surface of samples, which led to a better redox property. The excellent redox property of support materials helped to improve the catalytic activity of TWC.展开更多
The CuO/CeO2 catalysts were investigated by means of X-ray diffraction （XRD）, laser Raman spectroscopy （LRS）, X-ray photoelectronic spectroscopy （XPS）, temperature-programmed reduction （TPR）, in situ Fourier t...The CuO/CeO2 catalysts were investigated by means of X-ray diffraction （XRD）, laser Raman spectroscopy （LRS）, X-ray photoelectronic spectroscopy （XPS）, temperature-programmed reduction （TPR）, in situ Fourier transform infrared spectroscopy （FTIR） and NO＋CO reaction. The results revealed that the low temperature （〈150℃） catalytic performances were enhanced for CO pretreated samples. During CO pretreatment, the surface Cu＋/Cu0 and oxygen vacancies on ceria surface were present. The low va- lence copper species activated the adsorbed CO and surface oxygen vacancies facilitated the NO dissociation. These effects in turn led to higher activities of CuO/CeO2 for NO reduction. The current study provided helpful understandings of active sites and reaction mechanism in NO＋CO reaction.展开更多
The atomic structure of the active sites in Cu/CeO2 catalysts is intimately associated with the copper-ceria interaction. Both the shape of ceria and the loading of copper affect the chemical bonding of copper species...The atomic structure of the active sites in Cu/CeO2 catalysts is intimately associated with the copper-ceria interaction. Both the shape of ceria and the loading of copper affect the chemical bonding of copper species on ceria surfaces and the electronic and geometric character of the relevant interfaces. Nanostructured ceria, including particles(polyhedra), rods, and cubes, provides anchoring sites for the copper species. The atomic arrangements and chemical properties of the(111),(110) and(100) facets, preferentially exposed depending on the shape of ceria, govern the copper-ceria interactions and in turn determine their catalytic properties. Also, the metal loading significantly influences the dispersion of copper species on ceria with a specific shape, forming copper layers, clusters, and nanoparticles. Lower copper contents result in copper monolayers and/or bilayers while higher copper loadings lead to multi-layered clusters and faceted particles. The active sites are usually generated via interactions between the copper atoms in the metal species and the oxygen vacancies on ceria, which is closely linked to the number and density of surface oxygen vacancies dominated by the shape of ceria.展开更多
Composite supports CeO2-ZrO2-Al2O3（CZA） and CeO2-ZrO2-Al2O3-La2O3（CZALa） were prepared by co-precipitation method. Palladium catalysts were prepared by impregnation and their purification ability for CH4, CO and N...Composite supports CeO2-ZrO2-Al2O3（CZA） and CeO2-ZrO2-Al2O3-La2O3（CZALa） were prepared by co-precipitation method. Palladium catalysts were prepared by impregnation and their purification ability for CH4, CO and NOx in the mixture gas simulated the exhaust from natural gas vehicles （NGVs） operated under stoichiometric condition was investigated. The effect of La2O3 on the physicochemical properties of supports and catalysts was characterized by various techniques. The characterizations with X-ray diffraction （XRD） and Raman spectroscopy revealed that the doping of La2O3 restrained effectively the sintering of crystallite particles, maintained the crystallite particles in nanoscale and stabilized the crystal phase after calcination at 1000 ℃. The results of N2-adsorption, H2-temperatnre-programmed reduction （H2-TPR） and oxygen storage capacity （OSC） measurements indicated that La2O3 improved the textural properties, reducibility and OSC of composite supports. Activity testing results showed that the catalysts exhibit excellent activities for the simultaneous removal of methane, CO and NOx in the simulated exhaust gas. The catalysts supported on CZALa showed remarkable thermal stability and catalytic activity for the three pollutants, especially for NOx. The prepared palladium catalysts have high ability to remove NOx, CH4 and CO, and they can be used as excellent catalysts for the purification of exhaust from NGVs operated under stoichiometric condition. The catalysts reported in this work also have significant potential in industrial application because of their high performance and low cost.展开更多
The Pd-only catalysts for motorcycle were prepared by impregnating CeO2-ZrO2-Al2O3 and CeO2-ZrO2+Al2O3 with PdCl2 aqueous solution and characterized by X-ray diffraction (XRD), oxygen storage capacity (OSC) and H2-tem...The Pd-only catalysts for motorcycle were prepared by impregnating CeO2-ZrO2-Al2O3 and CeO2-ZrO2+Al2O3 with PdCl2 aqueous solution and characterized by X-ray diffraction (XRD), oxygen storage capacity (OSC) and H2-temperature-programmed reduction (H2-TPR) methods. The XRD result indicated that the CeO2-ZrO2-Al2O3 compound prepared by co-precipitation formed a single solid solution and had good thermal stability, and Pd phase was not observed in all catalysts. The TPR results showed that the reduction temperature of Pd/CeO2-ZrO2-Al2O3 catalyst was lower than that of Pd/CeO2-ZrO2+Al2O3 catalyst whether they were fresh or aged catalysts. The Pd/CeO2-ZrO2-Al2O3 exhibited high three-way catalytic activity at low temperature, high thermal stability, and wide working window, suggesting a great potential for applications.展开更多
The nanometer CeO2 powder was prepared by the method of microwave-assisted heating hydrolysis,and the nanometer CeO2-supported or ordinary CeO2-supported vanadia catalysts with different vanadium loadings(atomic ratio...The nanometer CeO2 powder was prepared by the method of microwave-assisted heating hydrolysis,and the nanometer CeO2-supported or ordinary CeO2-supported vanadia catalysts with different vanadium loadings(atomic ratios:100V/Ce=0.1,1,4,10,and 20) were prepared by an incipient-wetness impregnation method.Spectroscopic techniques(XRD,FT-IR,Raman and UV-Vis DRS) were utilized to characterize the structures of VOx/CeO2 catalysts.The results showed that the structures of CeO2-supported vanadium oxide catalysts de...展开更多
文摘Cu/CeO2-ZrO2 catalysts for water-gas shift （WGS） reaction were prepared with co-precipitation method, and the influence of ZrO2 content on the catalytic structure and properties was investigated by the techniques of N2 physical adsorption analysis, XRD and H2-TPR. The results indicate that the BET surface areas of the catalysts are increased in varying degrees due to the presence of ZrO2. With increasing ZrO2 content, the pore size distribution is centered on 1.9 nm. ZrO2 can efficiently restrain the growth of Cu crystal particles. The appropriate amount of ZrO2 in the Cu/CeO2 catalysts can help the catalyst keep better copper dispersion in the WGS reaction, which can lead to both higher catalytic activity and better thermal stability. When ZrO2 content is 10% （atom fraction）, Cu/CeO2-Zr02 catalyst reaches a CO conversion rate of 73.7% at the reaction temperature of 200℃.
基金supported by the National Natural Science Foundation of China(Nos.22276060 and 21976059)Guangdong Basic and Applied Basic Research Foundation(No.2024A1515012636)China Scholarship Council Scholarship(No.201906155006)。
文摘The reduction of carbon emissions in the steel industry is a significant challenge,and utilizing CO_(2) from carbon intensive steel industry off-gases for methanol production is a promising strategy for decarbonization.However,steelwork off-gases typically contain various impurities,including H_(2)S,which can deactivate commercial methanol synthesis catalysts,Cu/ZnO/Al_(2)O_(3)(CZA).Reverse water-gas shift(RWGS)reaction is the predominant side reaction in CO_(2) hydrogenation to methanol which can occur at ambient pressure,enabling the decouple of RWGS from methanol production at high pressure.Then,a series of activated CZA catalysts has been in-situ pretreated in 400 ppm H_(2)S/Ar at 250℃and tested for both RWGS reaction at ambient pressure and CO_(2) hydrogenation to methanol at high pressure.An innovative decoupling strategy was employed to isolate the RWGS reaction from the methanol synthesis process,enabling the investigation of the evolution of active site structures and the poisoning mechanism through elemental analysis,X-ray Diffraction,X-ray Photoelectron Spectroscopy,Fourier Transform Infrared Spectroscopy,Temperature Programmed Reduction and CO_(2) Temperature Programmed Desorption.The results indicate that there are different dynamic migration behaviors of ZnO_(x) in the two reaction systems,leading to different poisoning mechanisms.These interesting findings are beneficial to develop sulfur resistant and durable highly efficient catalysts for CO_(2) hydrogenation to methanol,promoting the carbon emission reduction in steel industry.
基金Project supported by the "863 Project" (2009AA06Z304 and 2009AA064801)
文摘Nickel and sulfate co-modified CeO2-ZrO2 catalysts were prepared by sol-gel method. The catalysts were characterized by XRD, FTIR, XPS, NH3 chemisorption and NH3-SCR activity tests. The results showed that the enhanced acidity of CeO2-ZrO2 catalysts by nickel and sulfate co-modification was responsible for the broadened temperature window and improved the selectivity to N2 in NH3-SCR deNOx. The introduction of nickel to CeO2-ZrO2 solid solutions resulted in more Ce3+ on surface of catalyst, leading to an in...
基金Projected supported by the National Natural Science Foundation of China (20271028) and Tianjin Natural Science Foundation(033602511)
文摘CeO2 was synthesized via sol-gel process and used as supporter to prepare CuO/CeO2, Cu/CeO2 catalysts by impregnation method. The catalytic properties and characterization of CeO2, CuO/CeO2 and Cu/CeO2 catalysts were examined by means of a microreactor-GC system, HRTEM, XRD, TPR and XPS techniques. The results show that CuO has not catalytic activity and the activity of CeO2 is quite low for CO oxidation. However, the catalytic activity of CuO/CeO2 and Cu/ CeO2 catalysts increases significantly. Furthermore, the activity of CuO/CeO2 is higher than that of Cu/CeO2 catalysts.
基金supported by National Natural Science Foundation of China(51202116)Ministry of Science and Technology,China(2010CB732304,2013AA065302)
文摘Praseodymium （Pr） was impregnated to CeO2-ZrO2 solid solution by an impregnation method. The as-obtained Pr modi- fied CeO2-ZrO2 was impregnated with 1 wt.% Pd to prepare the catalysts. The structure and reducibility of the fresh and hydrother- really aged catalysts were characterized by X-ray diffraction （XRD）, Raman, X-ray photoelectron spectroscopy （XPS）, CO chemi- sorption and H2 temperature-programmed reduction （H2-TPR）. The oxygen storage capacity （OSC） was evaluated with CO serving as probe gas. Effects of impregnated Pr on the structure and oxygen storage capacity of catalysts were investigated. The results showed that the aged Pr-impregnated samples had much higher OSC and better reducibility than the unmodified ones. The scheme of structural evolutions of the catalysts with and without Pr was also established. Partial of the impregnated Pr diffused into the bulk of CeO2-ZrO2 during ageing, which inhibited the sintering, and increased the amount of oxygen vacancies in CeO2-ZrO2 support. Furthermore, those impregnated Pr species which covered on the surface of the support obstructed the strong metal-support interaction between Pd and Ce so as to reduce the encapsulation of Pd as well as the back spill-over of the oxygen during the catalytic process.
基金Project supported by the National Natural Science Foundation of China(21377048,21307047)the Opening Project of Key Laboratory of Green Catalysis of Sichuan Institutes of High Education(LYJ1309)
文摘A series of CeO2-ZrO2-WO3 catalysts for the selective catalytic reduction （SCR） of NO with NH3 were prepared by hydrothermal method. The influence of calcination temperature on the catalytic activity, microstructure, surface acidity and redox behavior of CeO2-ZrO2-WO3 catalyst was investigated using various characterization methods. It was found that the CeO2-ZrO2-WO3 catalyst calcined at 600 ℃ showed the best catalytic performance and excellent N2 selectivity, and yielded more than 90% NO conversion in a wide temperature range of 250-500 ℃ with a space velocity （GHSV） of 60000 131. As the calcination temperature was increased from 400 to 600 ℃, the NO conversion obviously increased, but decreased at higher calcination temperature. The results implied that the higher surface area, the strongest synergistic interaction, the superior redox property and the highly dispersed or amorphous WO3 species contributed to the excellent SCR activity of the CeO2-ZrO2-WO3 catalyst calcined at 600℃.
基金supported by the Ministry of Science and Technology,China (No.2009AA064801,2010CB732304)
文摘Potassium-modified ceria-zirconia catalyst was synthesized by wetness impregnation method. The ageing treatment was performed in static air at 800℃ for 20 hr to evaluate the thermal stability of the catalyst. The catalysts were characterized by X-ray diffraction, BET surface area, oxygen storage capacity, NOx-temperature programmed desorption and soot-temperature programmed oxidation measurements. By introduction of potassium, the maximum soot oxidation rate temperature （Tin） of the ceria-zirconia based catalyst decreased from 525 to 428℃ in the presence of NO under a loose contact mode. The shift of Tm of the K-modified catalyst after ageing is only 15℃. The enhanced activity of the aged catalyst mainly lies in the promotional effect of potassium on the NOx/oxygen storage capacity as well as the soot-catalyst contact.
基金Project supported by National Natural Science Foundation of China (20773090, 20803049)the Specialized Research Fund for the Doctoral Program of Higher Education (20070610026, 200806100009)
文摘Ce-Zr-Al-Nd2O3 （CZAN） support materials were prepared by co-precipitation and impregnation methods, respectively. They were characterized by X-ray diffTaction （XRD）, low temperature nitrogen adsorption-desorption, oxygen pulsing technique, H2-temperamre programmed reduction （H2-TPR） and X-ray photoelectron spectroscopy （XPS）. The Pd-only three-way catalysts （Pd-TWC） supported on these materials were prepared by incipient wetness method and studied by activity tests. The results demonstrated that the CZAN supports obtained by the two methods showed better structural, textural and redox properties than the CZA without Nd2O3, and the addition of Nd203 improved the catalytic activity of TWC. Especially, the CZAN-i support prepared by impregnation method had better thermal stability and redox property. Meanwhile, the Pd/CZAN-i catalyst exhibited the best catalytic performance. XPS measurements indicated that the Nd-modified samples possessed more Ce3＋ and oxygen vacancies on the surface of samples, which led to a better redox property. The excellent redox property of support materials helped to improve the catalytic activity of TWC.
基金supported by National Basic Research Program of China(2010CB732300)National Natural Science Foundation of China(21273110,20973091)Natural Science Foundation for the Youth(21203091)
文摘The CuO/CeO2 catalysts were investigated by means of X-ray diffraction （XRD）, laser Raman spectroscopy （LRS）, X-ray photoelectronic spectroscopy （XPS）, temperature-programmed reduction （TPR）, in situ Fourier transform infrared spectroscopy （FTIR） and NO＋CO reaction. The results revealed that the low temperature （〈150℃） catalytic performances were enhanced for CO pretreated samples. During CO pretreatment, the surface Cu＋/Cu0 and oxygen vacancies on ceria surface were present. The low va- lence copper species activated the adsorbed CO and surface oxygen vacancies facilitated the NO dissociation. These effects in turn led to higher activities of CuO/CeO2 for NO reduction. The current study provided helpful understandings of active sites and reaction mechanism in NO＋CO reaction.
文摘The atomic structure of the active sites in Cu/CeO2 catalysts is intimately associated with the copper-ceria interaction. Both the shape of ceria and the loading of copper affect the chemical bonding of copper species on ceria surfaces and the electronic and geometric character of the relevant interfaces. Nanostructured ceria, including particles(polyhedra), rods, and cubes, provides anchoring sites for the copper species. The atomic arrangements and chemical properties of the(111),(110) and(100) facets, preferentially exposed depending on the shape of ceria, govern the copper-ceria interactions and in turn determine their catalytic properties. Also, the metal loading significantly influences the dispersion of copper species on ceria with a specific shape, forming copper layers, clusters, and nanoparticles. Lower copper contents result in copper monolayers and/or bilayers while higher copper loadings lead to multi-layered clusters and faceted particles. The active sites are usually generated via interactions between the copper atoms in the metal species and the oxygen vacancies on ceria, which is closely linked to the number and density of surface oxygen vacancies dominated by the shape of ceria.
基金supported by the National Natural Science Foundation of China (No. 20773090, 20803049)the National High Technology Researchand Development Program of China (863 Program, No. 2006AA06Z347)the Specialized Research Fund for the Doctoral Program of Higher Education(20070610026)
文摘Composite supports CeO2-ZrO2-Al2O3（CZA） and CeO2-ZrO2-Al2O3-La2O3（CZALa） were prepared by co-precipitation method. Palladium catalysts were prepared by impregnation and their purification ability for CH4, CO and NOx in the mixture gas simulated the exhaust from natural gas vehicles （NGVs） operated under stoichiometric condition was investigated. The effect of La2O3 on the physicochemical properties of supports and catalysts was characterized by various techniques. The characterizations with X-ray diffraction （XRD） and Raman spectroscopy revealed that the doping of La2O3 restrained effectively the sintering of crystallite particles, maintained the crystallite particles in nanoscale and stabilized the crystal phase after calcination at 1000 ℃. The results of N2-adsorption, H2-temperatnre-programmed reduction （H2-TPR） and oxygen storage capacity （OSC） measurements indicated that La2O3 improved the textural properties, reducibility and OSC of composite supports. Activity testing results showed that the catalysts exhibit excellent activities for the simultaneous removal of methane, CO and NOx in the simulated exhaust gas. The catalysts supported on CZALa showed remarkable thermal stability and catalytic activity for the three pollutants, especially for NOx. The prepared palladium catalysts have high ability to remove NOx, CH4 and CO, and they can be used as excellent catalysts for the purification of exhaust from NGVs operated under stoichiometric condition. The catalysts reported in this work also have significant potential in industrial application because of their high performance and low cost.
基金Project supported by the National High Technology Research and Development Program of China (863 Program,2006AA06Z347)the Specialized Research Fund for the Doctoral Program of Higher Education (20070610026)
文摘The Pd-only catalysts for motorcycle were prepared by impregnating CeO2-ZrO2-Al2O3 and CeO2-ZrO2+Al2O3 with PdCl2 aqueous solution and characterized by X-ray diffraction (XRD), oxygen storage capacity (OSC) and H2-temperature-programmed reduction (H2-TPR) methods. The XRD result indicated that the CeO2-ZrO2-Al2O3 compound prepared by co-precipitation formed a single solid solution and had good thermal stability, and Pd phase was not observed in all catalysts. The TPR results showed that the reduction temperature of Pd/CeO2-ZrO2-Al2O3 catalyst was lower than that of Pd/CeO2-ZrO2+Al2O3 catalyst whether they were fresh or aged catalysts. The Pd/CeO2-ZrO2-Al2O3 exhibited high three-way catalytic activity at low temperature, high thermal stability, and wide working window, suggesting a great potential for applications.
基金supported by the National Natural Science Foundation of China (20803093,20833011,20525621)the Doctor Select Foundation for the University of State Education Ministry (200804251016)+1 种基金the Beijing Outstanding Ph.D.Thesis Foundation (YB 20091141401)the Hi-Tech Research and Development Program (863) of China (SQ2009AA06Z3488052)
文摘The nanometer CeO2 powder was prepared by the method of microwave-assisted heating hydrolysis,and the nanometer CeO2-supported or ordinary CeO2-supported vanadia catalysts with different vanadium loadings(atomic ratios:100V/Ce=0.1,1,4,10,and 20) were prepared by an incipient-wetness impregnation method.Spectroscopic techniques(XRD,FT-IR,Raman and UV-Vis DRS) were utilized to characterize the structures of VOx/CeO2 catalysts.The results showed that the structures of CeO2-supported vanadium oxide catalysts de...