The CeTi 2O 6, which is formed above 1300 ℃ by ceramic method, was obtained at 700 ℃ using sol gel synthesis method. XRD analysis shows that there is 8% deficient of Ce in the structure. The chemical formula is C...The CeTi 2O 6, which is formed above 1300 ℃ by ceramic method, was obtained at 700 ℃ using sol gel synthesis method. XRD analysis shows that there is 8% deficient of Ce in the structure. The chemical formula is Ce 0.92 Ti 2O 5.84 , which has a monoclinic structure with space group of C 2/ m . Its cell parameters are a =0.9811(8) nm, b =0.3726(3) nm, c =0.6831(6) nm, and β =118.84°. After being treated at 1300 ℃ for 3 h, the system keeps stable but the deficient disappears, while the chemical formula change to the normal CeTi 2O 6, and the cell parameters are a =0.9813(3) nm, b =0.3752(4) nm, c =0.6883(5) nm, β =119.05°. The key to synthesis the precursors of CeTi 2O 6 is that Ti 4+ and Ce 3+ ions must reach the atomistic distributing state and prevent the oxidation of Ce 3+ during sol gel process.展开更多
文摘The CeTi 2O 6, which is formed above 1300 ℃ by ceramic method, was obtained at 700 ℃ using sol gel synthesis method. XRD analysis shows that there is 8% deficient of Ce in the structure. The chemical formula is Ce 0.92 Ti 2O 5.84 , which has a monoclinic structure with space group of C 2/ m . Its cell parameters are a =0.9811(8) nm, b =0.3726(3) nm, c =0.6831(6) nm, and β =118.84°. After being treated at 1300 ℃ for 3 h, the system keeps stable but the deficient disappears, while the chemical formula change to the normal CeTi 2O 6, and the cell parameters are a =0.9813(3) nm, b =0.3752(4) nm, c =0.6883(5) nm, β =119.05°. The key to synthesis the precursors of CeTi 2O 6 is that Ti 4+ and Ce 3+ ions must reach the atomistic distributing state and prevent the oxidation of Ce 3+ during sol gel process.