Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichua...Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichuan, China展开更多
CeO2-ZrO2-Al2O3 ternary oxides were successfully prepared by a green route of supercritical anti-solvent precipitation with supercritical CO2 as anti-solvent and methanol as solvent. The structures and oxygen storage ...CeO2-ZrO2-Al2O3 ternary oxides were successfully prepared by a green route of supercritical anti-solvent precipitation with supercritical CO2 as anti-solvent and methanol as solvent. The structures and oxygen storage capacities of these ternary oxides were characterized by XRD, Raman spectra and oxygen storage capacity measurements. It was found that Al3＋ and Zr4＋ inserted into CeO2 lattice, forming CeO2-ZrO2-Al2O3 solid solution. The concentration of aluminium isopropoxide in the solution affected the concentration of oxygen vacancy and the distortion of oxygen sublattice which were responsible for the oxygen storage capacity. The rapidest oxygen uptake/release rate and maximum total oxygen storage capacity （122.0 mmolO2/molCeO2） were obtained with the aluminitun isopropoxide concentration at 0.2 wt.% in the solution.展开更多
The catalytic behaviors of Pd （1.4 wt.%） catalysts supported on CeO2-ZrO2 promoted with La2O3 were investigated for methanol decomposition. The measurements of inductively coupled plasma emission spectroscopy （ICP...The catalytic behaviors of Pd （1.4 wt.%） catalysts supported on CeO2-ZrO2 promoted with La2O3 were investigated for methanol decomposition. The measurements of inductively coupled plasma emission spectroscopy （ICP）, N2 adsorption-desorption （BET）, powder X-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS）, temperature-programmed reduction （TPR） and oxygen storage capacity （OSC） were used to characterize the properties of catalysts. The catalysts＇ activities were tested in a fixed bed continuous flow reactor operating under atmospheric pressure. The Pd/Ce0.8Zr0.2O2-5 wt.%La2O3 catalyst exhibited the best activity. The reasons for this were twofold： （1） doping of La improved effectively textural properties of CeO2-ZrO2 oxygen storage materials, and （2） Pd/Ce0.8Zr0.2O2-5 wt.%La2O3 possessed super oxygen storage property and reducibility due to the existence of lattice defect oxygen or mobile oxygen, which helped to re-oxidize zerovalent Pd0 to a partly oxidized Pdδ＋. By introducing 5 wt.%La2O3, the specific surface area of the sample increased, but declined if further increasing the content of La2O3 to 10 wt.%.展开更多
基金the National Natural Science Foundation of China (20773090)the Specialized Research Fund for the Doctoral Program of Higher Education of China (20070610026, 200806100009)
文摘Hairong Wang, Yaoqiang Chen, Qiulin Zhang, Qingchao Zhu, Maochu Gong, Ming Zhao（ Key Laboratory of Green Chemistry ＆ Technology of Ministry Education, College of Chemistry, Sichuan University, Chengdu 610064, Sichuan, China
基金National Natural Science Foundation of China(20976120)the Natural Science Foundation of Tianjin(09JCYBJC06200)
文摘CeO2-ZrO2-Al2O3 ternary oxides were successfully prepared by a green route of supercritical anti-solvent precipitation with supercritical CO2 as anti-solvent and methanol as solvent. The structures and oxygen storage capacities of these ternary oxides were characterized by XRD, Raman spectra and oxygen storage capacity measurements. It was found that Al3＋ and Zr4＋ inserted into CeO2 lattice, forming CeO2-ZrO2-Al2O3 solid solution. The concentration of aluminium isopropoxide in the solution affected the concentration of oxygen vacancy and the distortion of oxygen sublattice which were responsible for the oxygen storage capacity. The rapidest oxygen uptake/release rate and maximum total oxygen storage capacity （122.0 mmolO2/molCeO2） were obtained with the aluminitun isopropoxide concentration at 0.2 wt.% in the solution.
基金Project supported by the Programs Foundation of Ministry of Education of China (20070610026)the National Natural Science Foundation of China (20773090, 20803049)
文摘The catalytic behaviors of Pd （1.4 wt.%） catalysts supported on CeO2-ZrO2 promoted with La2O3 were investigated for methanol decomposition. The measurements of inductively coupled plasma emission spectroscopy （ICP）, N2 adsorption-desorption （BET）, powder X-ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS）, temperature-programmed reduction （TPR） and oxygen storage capacity （OSC） were used to characterize the properties of catalysts. The catalysts＇ activities were tested in a fixed bed continuous flow reactor operating under atmospheric pressure. The Pd/Ce0.8Zr0.2O2-5 wt.%La2O3 catalyst exhibited the best activity. The reasons for this were twofold： （1） doping of La improved effectively textural properties of CeO2-ZrO2 oxygen storage materials, and （2） Pd/Ce0.8Zr0.2O2-5 wt.%La2O3 possessed super oxygen storage property and reducibility due to the existence of lattice defect oxygen or mobile oxygen, which helped to re-oxidize zerovalent Pd0 to a partly oxidized Pdδ＋. By introducing 5 wt.%La2O3, the specific surface area of the sample increased, but declined if further increasing the content of La2O3 to 10 wt.%.