Sb-doped SnO2(ATO)-(CeO2-TiO2)thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low...Sb-doped SnO2(ATO)-(CeO2-TiO2)thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low-temperature hydrothermal process.The mixed molar ratio of ATO to(CeO2-TiO2)vs the properties of CeO2-TiO2 thin film was investigated.The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra,the sheet resistance of ATO particles and films were measured by rubber sheeter(MYI-50)and four-point probe(HisuperGroup Inc,SDY-5),the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction(XRD),respectively.The results showed that the ATO precursor solution lost weight completely at about 500 oC,and the ATO particles was obtained,which indicated the same rutile lattice structure as SnO2.The glass substrates coated with ATO-(CeO2-TiO2)thin films showed better properties in antistatic electricity(104-106Ω/),shielding UV(almost 100%),visible light transmission(70%)and infrared reflection(】30%).展开更多
60CeO2-40TiO2 thin films were deposited on soda-lime silicate glass substrates by R.F. magnetron sputtering. The effects of heat-treatment on the UV-absorption of the thin films were studied on the 60CeO2-40TiO2 thin ...60CeO2-40TiO2 thin films were deposited on soda-lime silicate glass substrates by R.F. magnetron sputtering. The effects of heat-treatment on the UV-absorption of the thin films were studied on the 60CeO2-40TiO2 thin film with the largest UV cut-off wavelength. The sample films with CeO2：TiO2=60：40 were heated at 773 K, 873 K, 973 K for 30 min. These films are characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and X-ray photoelectron spectroscopy and spectrometer （XPS）. XRD analysis proves that the addition of TiO2 to CeO2 changed the crystalline state of CeO2. But the UV absorption effect of CeO2-TiO2 films with CeO2 crystallite phase is inferior to that of the amorphous phase CeO2-TiO2 films. XPS analysis also indicates that the amorphous phase CeO2-TiO2 films have the most Ce3＋ content in these films. Amorphous phase and crystalline phase of the CeO2-TiO2 films have different effects on UV absorption of the thin films.展开更多
CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets wit...CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets with different molar ratio of CeO2 to TiO2 （CeO2：TiO2-0：1.0; 0.1：0.9; 0.2：0.8; 0.3：0.7; 0.4：0.6; 0.5：0.5; 0.6：0.4; 0.7：0.3; 0.8：0.2; 0.9：0.1; 1.0：0）. The films are characterized by UV-visible transmission and infrared reflection spectra, scanning electron microscopy （SEM）, Raman spectroscopy, X-ray photoelectron spectroscopy （XPS） and X-ray diffraction （XRD）, respectively. The obtained results show that the amorphous phases composed of CeO2-TiO2 play an important role in absorbing UV, there are Ce^3-, Ce^4- and Ti^4- on the surface of the films; the glass substrates coated with CeO2-TiO2 （Ce/Ti=0.5：0.5; 0.6：0.4）/SnO2：Sb（6 mol%） double films show high absorbing UV（〉99）, high visible light transmission （75%） and good infrared reflection （〉70%）. The sheet resistance of the films is 30-50 Ω/□. The glass substrates coated with the double functional films can be used as window glass of buildings, automobile and so on.展开更多
基金Project supported by the Changjiang Scholars and Innovative Research Team in University
文摘Sb-doped SnO2(ATO)-(CeO2-TiO2)thin Films were deposited on glass substrates using the mixed solution including CeO2-TiO2 precursor and ATO particles by sol-gel dip coating process.ATO particles were prepared using low-temperature hydrothermal process.The mixed molar ratio of ATO to(CeO2-TiO2)vs the properties of CeO2-TiO2 thin film was investigated.The optical properties of the films were characterized by UV-visible transmission and infrared reflection spectra,the sheet resistance of ATO particles and films were measured by rubber sheeter(MYI-50)and four-point probe(HisuperGroup Inc,SDY-5),the surface morphology and structure of the films were analyzed using 3D Digitale Mikroskop and X-ray diffraction(XRD),respectively.The results showed that the ATO precursor solution lost weight completely at about 500 oC,and the ATO particles was obtained,which indicated the same rutile lattice structure as SnO2.The glass substrates coated with ATO-(CeO2-TiO2)thin films showed better properties in antistatic electricity(104-106Ω/),shielding UV(almost 100%),visible light transmission(70%)and infrared reflection(】30%).
基金the National Natural Science Foundation of China(No.51032005)the Fundamental Research Funds for the Central Universities(Wuhan University of Technology)+1 种基金the China Postdoctoral Science Foundation(No.2012M511285)the Fund for the Young Innovative Team(Hubei University of Education)(No.2012KQ05)
文摘60CeO2-40TiO2 thin films were deposited on soda-lime silicate glass substrates by R.F. magnetron sputtering. The effects of heat-treatment on the UV-absorption of the thin films were studied on the 60CeO2-40TiO2 thin film with the largest UV cut-off wavelength. The sample films with CeO2：TiO2=60：40 were heated at 773 K, 873 K, 973 K for 30 min. These films are characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and X-ray photoelectron spectroscopy and spectrometer （XPS）. XRD analysis proves that the addition of TiO2 to CeO2 changed the crystalline state of CeO2. But the UV absorption effect of CeO2-TiO2 films with CeO2 crystallite phase is inferior to that of the amorphous phase CeO2-TiO2 films. XPS analysis also indicates that the amorphous phase CeO2-TiO2 films have the most Ce3＋ content in these films. Amorphous phase and crystalline phase of the CeO2-TiO2 films have different effects on UV absorption of the thin films.
基金the program for Changjiang Scholars and Innovative Research Team in University (No.IRT0547
文摘CeO2-TiO2 films and CeO2-TiO/SnO2：Sb （6 mol%） double films were deposited on glass substrates by radio-frequency magnetron sputtering （R.F. Sputtering）, using SnO2：Sb（6 mol%） target, and CeO2- TiO2 targets with different molar ratio of CeO2 to TiO2 （CeO2：TiO2-0：1.0; 0.1：0.9; 0.2：0.8; 0.3：0.7; 0.4：0.6; 0.5：0.5; 0.6：0.4; 0.7：0.3; 0.8：0.2; 0.9：0.1; 1.0：0）. The films are characterized by UV-visible transmission and infrared reflection spectra, scanning electron microscopy （SEM）, Raman spectroscopy, X-ray photoelectron spectroscopy （XPS） and X-ray diffraction （XRD）, respectively. The obtained results show that the amorphous phases composed of CeO2-TiO2 play an important role in absorbing UV, there are Ce^3-, Ce^4- and Ti^4- on the surface of the films; the glass substrates coated with CeO2-TiO2 （Ce/Ti=0.5：0.5; 0.6：0.4）/SnO2：Sb（6 mol%） double films show high absorbing UV（〉99）, high visible light transmission （75%） and good infrared reflection （〉70%）. The sheet resistance of the films is 30-50 Ω/□. The glass substrates coated with the double functional films can be used as window glass of buildings, automobile and so on.