Aiming at the cracking phenomenon of the thin shell mould in the expendable pattern shell casting during the pattern removing process, some systemic researches are presented.The influence of the pattern removing metho...Aiming at the cracking phenomenon of the thin shell mould in the expendable pattern shell casting during the pattern removing process, some systemic researches are presented.The influence of the pattern removing method and temperature on the pattern removing were investigated.The shell mould cracking mechanism was analyzed by using thermo-gravimetric analysis (TGA), and combining the temperature field and the volume change of the expanded polystyrene (EPS) foam pattern being tested.The results indicated that the shell mould was not easily cracked when the pattern removing process was carried out with the furnace being heated little by little because of the shell slowly shrinking with dehydration and shell strength gradually increasing.The shell mould was soon destroyed when it was set directly into the furnace at above 400 oC because of the thin shell mould rapidly shrinking and the foam pattern hindering.However, the shell mould had no cracking when it had been preheated for a long time even if the furnace temperature was above 400 oC and the shell was put into the furnace directly.Moreover, when the shell mould was directly set into the furnace at lower temperatures, 250 to 300 ℃, the shell would shrink slowly and the foam pattern would stay at the maximum expansion stage temperature of 100 to 110 ℃ for a long time; and the shell mould would experience an expansion force from the foam pattern for a long time.The expansion force is related to the pattern removing temperature, holding time, foam pattern thickness and density.Therefore, the foam pattern with higher density could make the shell crack.展开更多
To refine the microstructure and improve the mechanical properties of AZ91 D alloy by expendable pattern shell casting(EPSC),the mechanical vibration method was applied in the solidification process of the alloy.The e...To refine the microstructure and improve the mechanical properties of AZ91 D alloy by expendable pattern shell casting(EPSC),the mechanical vibration method was applied in the solidification process of the alloy.The effects of amplitude and pouring temperature on microstructure and mechanical properties of AZ91 D magnesium alloy were studied.The results indicated that the mechanical vibration remarkably improved the sizes,morphologies and distributions of the primaryα-Mg phase andβ-Mg17 Al12 phase,and the densification and tensile properties of the AZ91 D alloy.With an increase in amplitude,the microstructures were gradually refined,resulting in a continuous increase in mechanical properties of the AZ91 D alloy.While,with the increase of pouring temperature,the microstructures were continuously coarsened,leading to an obvious decrease of the mechanical properties.The tensile strength and yield strength of the AZ91 D alloy with a vibration amplitude of 1.0 mm and a pouring temperature of 730℃were 60%and 38%higher than those of the alloy without vibration,respectively.展开更多
The influencing factors of surface alloying layer by evaporative pattern casting technology were investigated.A certain thickness alloying layer was formed on the surface of Mg-alloy matrix when the pouring temperatur...The influencing factors of surface alloying layer by evaporative pattern casting technology were investigated.A certain thickness alloying layer was formed on the surface of Mg-alloy matrix when the pouring temperature was 780°C with different vacuum degree and alloying powder size.The surface layer microstructure,micro area composition of the new phase formed on the matrix and the composition characteristics on the surface layer were examined by SEM and element scanning.The results show that the content of aluminum increases greatly on the surface layer.The micro-hardness of alloyed layer has a more obvious increase compared with that of the matrix.The size of alloying element and the vacuum degree are the key factors influencing the alloying layer,with the increase of element powder size from 0.074 to 0.15 mm and vacuum degree from 0.04 to 0.06 MPa,the surface alloying effect becomes better.展开更多
PbO-ZnO-Na20 ceramic coating was fabricated on the AZ91D Mg-alloy substrate surface by using of evaporated pattern casting （EPC） process. The ceramic coating was characterized through scanning electron microscopy （...PbO-ZnO-Na20 ceramic coating was fabricated on the AZ91D Mg-alloy substrate surface by using of evaporated pattern casting （EPC） process. The ceramic coating was characterized through scanning electron microscopy （SEM） observation, energy dispersive X-ray spectrometer （EDS） and so on. The research was emphasized on the formation process of ceramic coating and the interface bonding conditions between ceramic coating and the substrate. Results show that the glass powder （PbO-ZnO-NazO） melts when contacts with the high temperature liquid metal, and solidifies on the surface of the substrate with the decrease of temperature. Therefore, the ceramic coating was successfully prepared with the formation of the bonding interface with the substrate, Beside the influence of coating layer thickness, the vacuum level was also investigated. Further analysis indicates that oxide inclusions and decomposition products of foam pattern had a significant effect on the bonding interface： To obtain a good bonding interface between the ceramic coating and the substrate, the metal liquid oxidation and inclusions must be decreased and the decomposition products of foam pattern should be exhausted from the EPC coating completely.展开更多
The influences of two kinds of casting modules of metal casting （MC） and expandable pattern casting （EPC） on the corrosion behavior of Mg-11Gd-3Y alloy were studied by electrochemical measurements, scanning electr...The influences of two kinds of casting modules of metal casting （MC） and expandable pattern casting （EPC） on the corrosion behavior of Mg-11Gd-3Y alloy were studied by electrochemical measurements, scanning electron microscopy （SEM） observation, X-ray diffractometry （XRD） and X-ray photoelectron spectroscopy （XPS） analysis. It is found that the quantity of the Mg 24 （Gd, Y） 5 phase in MC is more than that in EPC due to the cooling rate. There is more alloying element dissolved in the matrix compared with MC. For EPC, the galvanic corrosion effect between the matrix and the Mg 24 （Gd, Y） 5 phase decreases and the corrosion resistance increases compared with the MC. The chief corrosion mode for Mg-11Gd-3Y alloy is pitting corrosion because most of the alloying elements are transformed into intermetallic phases. The average corrosion rate of the MC alloy in the immersion test is five times higher than that of EPC alloy and yttrium is present in the product film, which will provide increased protection for Mg-11Gd-3Y alloy. The electrochemical measurements and immersion test show that the EPC process increases the corrosion resistance compared with the MC Mg-11Gd-3Y alloy.展开更多
Selective laser sintering(SLS),as a kind of additive manufacturing technology,which uses a laser beam to scan and heat powder material layer by layer to form parts(models),is widely used in the field of casting,mainly...Selective laser sintering(SLS),as a kind of additive manufacturing technology,which uses a laser beam to scan and heat powder material layer by layer to form parts(models),is widely used in the field of casting,mainly for preparing casting coated sand cores,investment casting patterns,etc.The SLS technique facilitates rapid casting and shortens the casting production periods by eliminating mold preparation.In this study,we reached conclusions for the basic principles and characteristics of SLS methods,and focused on the research status,key technology and development trend of SLS in the fields of forming coated sand-casting molds and investment casting patterns.展开更多
The effective surface treatment method for steel insert composited with Al base metal by expendable pattern casting （EPC） process and the bonding interface between steel insert and Al base metal were investigated.It...The effective surface treatment method for steel insert composited with Al base metal by expendable pattern casting （EPC） process and the bonding interface between steel insert and Al base metal were investigated.It was found that Zn plating on steel insert was effective on improving the bonding property between steel insert and Al base metal in EPC process.Zn is thought to promote the formation of diffusion layer.But almost none content of Zn was observed in the boundary which had been plated on the steel insert.A diffusion layer consisting of Al,Si and Fe was formed at the insert/alloy interface and its hardness was higher than the steel insert as matter of course Al base metal.This layer turned out to be intermetallic compounds of Al-Si-Fe system.Higher pouring temperature promoted the diffusion of Fe into Al alloy,so Fe content in intermetallic layers increased at higher pouring temperature.The layer nearest to steel disappeared due to applied pressure.展开更多
The influence of a key process variable on the mold filling characteristics of AZ91 Mg-alloy was studied in the low pressure EPC process.The applied flow quantity of insert gas from 1 to 5 m~3/h associated with the pr...The influence of a key process variable on the mold filling characteristics of AZ91 Mg-alloy was studied in the low pressure EPC process.The applied flow quantity of insert gas from 1 to 5 m~3/h associated with the pressurizing rate in the low pressure EPC casting process was considered for rectangle and L-shape plate casting. The experimental results show that there is an optimal flow quantity of insert gas for good mold filling characteristics in AZ91 Mg-alloy low-pressure EPC process. The optimal flow quantity of insert gas for the specimens is 3 to 4 m~3/h. Either less or higher than the optimal flow quantity of insert gas would lead to misrun defects or folds, blisters and porosity defects. The practice of hub casting confirmed that the low-pressure EPC process with an optimal processing variable exemplified as 4 m~3/h gas flow quantity was capable of producing complicated magnesium castings without misrun defects.展开更多
基金supported by the National High Technology Research and Development Program of China (No.2007AA03Z113)
文摘Aiming at the cracking phenomenon of the thin shell mould in the expendable pattern shell casting during the pattern removing process, some systemic researches are presented.The influence of the pattern removing method and temperature on the pattern removing were investigated.The shell mould cracking mechanism was analyzed by using thermo-gravimetric analysis (TGA), and combining the temperature field and the volume change of the expanded polystyrene (EPS) foam pattern being tested.The results indicated that the shell mould was not easily cracked when the pattern removing process was carried out with the furnace being heated little by little because of the shell slowly shrinking with dehydration and shell strength gradually increasing.The shell mould was soon destroyed when it was set directly into the furnace at above 400 oC because of the thin shell mould rapidly shrinking and the foam pattern hindering.However, the shell mould had no cracking when it had been preheated for a long time even if the furnace temperature was above 400 oC and the shell was put into the furnace directly.Moreover, when the shell mould was directly set into the furnace at lower temperatures, 250 to 300 ℃, the shell would shrink slowly and the foam pattern would stay at the maximum expansion stage temperature of 100 to 110 ℃ for a long time; and the shell mould would experience an expansion force from the foam pattern for a long time.The expansion force is related to the pattern removing temperature, holding time, foam pattern thickness and density.Therefore, the foam pattern with higher density could make the shell crack.
基金the financial support from the State Key Laboratory of Materials Processing and Die&Mould Technology,Huazhong University of Science and Technology(P2020-05)。
文摘To refine the microstructure and improve the mechanical properties of AZ91 D alloy by expendable pattern shell casting(EPSC),the mechanical vibration method was applied in the solidification process of the alloy.The effects of amplitude and pouring temperature on microstructure and mechanical properties of AZ91 D magnesium alloy were studied.The results indicated that the mechanical vibration remarkably improved the sizes,morphologies and distributions of the primaryα-Mg phase andβ-Mg17 Al12 phase,and the densification and tensile properties of the AZ91 D alloy.With an increase in amplitude,the microstructures were gradually refined,resulting in a continuous increase in mechanical properties of the AZ91 D alloy.While,with the increase of pouring temperature,the microstructures were continuously coarsened,leading to an obvious decrease of the mechanical properties.The tensile strength and yield strength of the AZ91 D alloy with a vibration amplitude of 1.0 mm and a pouring temperature of 730℃were 60%and 38%higher than those of the alloy without vibration,respectively.
基金Project(50775085)supported by the National Natural Science Foundation of China
文摘The influencing factors of surface alloying layer by evaporative pattern casting technology were investigated.A certain thickness alloying layer was formed on the surface of Mg-alloy matrix when the pouring temperature was 780°C with different vacuum degree and alloying powder size.The surface layer microstructure,micro area composition of the new phase formed on the matrix and the composition characteristics on the surface layer were examined by SEM and element scanning.The results show that the content of aluminum increases greatly on the surface layer.The micro-hardness of alloyed layer has a more obvious increase compared with that of the matrix.The size of alloying element and the vacuum degree are the key factors influencing the alloying layer,with the increase of element powder size from 0.074 to 0.15 mm and vacuum degree from 0.04 to 0.06 MPa,the surface alloying effect becomes better.
基金supported by the National Natural Science Foundation of China (Grant No.50775085)
文摘PbO-ZnO-Na20 ceramic coating was fabricated on the AZ91D Mg-alloy substrate surface by using of evaporated pattern casting （EPC） process. The ceramic coating was characterized through scanning electron microscopy （SEM） observation, energy dispersive X-ray spectrometer （EDS） and so on. The research was emphasized on the formation process of ceramic coating and the interface bonding conditions between ceramic coating and the substrate. Results show that the glass powder （PbO-ZnO-NazO） melts when contacts with the high temperature liquid metal, and solidifies on the surface of the substrate with the decrease of temperature. Therefore, the ceramic coating was successfully prepared with the formation of the bonding interface with the substrate, Beside the influence of coating layer thickness, the vacuum level was also investigated. Further analysis indicates that oxide inclusions and decomposition products of foam pattern had a significant effect on the bonding interface： To obtain a good bonding interface between the ceramic coating and the substrate, the metal liquid oxidation and inclusions must be decreased and the decomposition products of foam pattern should be exhausted from the EPC coating completely.
基金Project(2007CB613705)supported by the National Basic Research Program of China
文摘The influences of two kinds of casting modules of metal casting （MC） and expandable pattern casting （EPC） on the corrosion behavior of Mg-11Gd-3Y alloy were studied by electrochemical measurements, scanning electron microscopy （SEM） observation, X-ray diffractometry （XRD） and X-ray photoelectron spectroscopy （XPS） analysis. It is found that the quantity of the Mg 24 （Gd, Y） 5 phase in MC is more than that in EPC due to the cooling rate. There is more alloying element dissolved in the matrix compared with MC. For EPC, the galvanic corrosion effect between the matrix and the Mg 24 （Gd, Y） 5 phase decreases and the corrosion resistance increases compared with the MC. The chief corrosion mode for Mg-11Gd-3Y alloy is pitting corrosion because most of the alloying elements are transformed into intermetallic phases. The average corrosion rate of the MC alloy in the immersion test is five times higher than that of EPC alloy and yttrium is present in the product film, which will provide increased protection for Mg-11Gd-3Y alloy. The electrochemical measurements and immersion test show that the EPC process increases the corrosion resistance compared with the MC Mg-11Gd-3Y alloy.
基金supported by the National Key R&D Program of China(2020YFB2008300,2020YFB2008304)the National Natural Science Foundation of China(51775204,51375190,59635040)。
文摘Selective laser sintering(SLS),as a kind of additive manufacturing technology,which uses a laser beam to scan and heat powder material layer by layer to form parts(models),is widely used in the field of casting,mainly for preparing casting coated sand cores,investment casting patterns,etc.The SLS technique facilitates rapid casting and shortens the casting production periods by eliminating mold preparation.In this study,we reached conclusions for the basic principles and characteristics of SLS methods,and focused on the research status,key technology and development trend of SLS in the fields of forming coated sand-casting molds and investment casting patterns.
文摘The effective surface treatment method for steel insert composited with Al base metal by expendable pattern casting （EPC） process and the bonding interface between steel insert and Al base metal were investigated.It was found that Zn plating on steel insert was effective on improving the bonding property between steel insert and Al base metal in EPC process.Zn is thought to promote the formation of diffusion layer.But almost none content of Zn was observed in the boundary which had been plated on the steel insert.A diffusion layer consisting of Al,Si and Fe was formed at the insert/alloy interface and its hardness was higher than the steel insert as matter of course Al base metal.This layer turned out to be intermetallic compounds of Al-Si-Fe system.Higher pouring temperature promoted the diffusion of Fe into Al alloy,so Fe content in intermetallic layers increased at higher pouring temperature.The layer nearest to steel disappeared due to applied pressure.
文摘The influence of a key process variable on the mold filling characteristics of AZ91 Mg-alloy was studied in the low pressure EPC process.The applied flow quantity of insert gas from 1 to 5 m~3/h associated with the pressurizing rate in the low pressure EPC casting process was considered for rectangle and L-shape plate casting. The experimental results show that there is an optimal flow quantity of insert gas for good mold filling characteristics in AZ91 Mg-alloy low-pressure EPC process. The optimal flow quantity of insert gas for the specimens is 3 to 4 m~3/h. Either less or higher than the optimal flow quantity of insert gas would lead to misrun defects or folds, blisters and porosity defects. The practice of hub casting confirmed that the low-pressure EPC process with an optimal processing variable exemplified as 4 m~3/h gas flow quantity was capable of producing complicated magnesium castings without misrun defects.