The effect of Al_(2)O_(3)/SiO_(2) mass ratio and CaO content on the viscosity and structure of the CaO-Al_(2)O_(3)-SiO_(2)-6MgO-1.5ZrO_(2)-1.5CeO_(2) slag was investigated.The results show that with the increase in Al...The effect of Al_(2)O_(3)/SiO_(2) mass ratio and CaO content on the viscosity and structure of the CaO-Al_(2)O_(3)-SiO_(2)-6MgO-1.5ZrO_(2)-1.5CeO_(2) slag was investigated.The results show that with the increase in Al_(2)O_(3)/SiO_(2) mass ratio,the viscous flow units within the slag gradually change from Si-O-Si to Al-O-Al and Al-O-Si.Furthermore,the substitution of Al_(2)O_(3) for SiO_(2) leads to the transformation of Si-O bonds towards weaker Al-O bonds,which weaken the bond strength of the aluminosilicate networks,thus leading to a decrease in the viscosity of slag.The increase in CaO content effectively promotes the depolymerization of the aluminosilicate networks,resulting in a significant decrease in the viscosity of the slag.The slag with Al_(2)O_(3)/SiO_(2) of 0.7-1.5 and CaO of 30 wt.%shows promise as the reference slag system for the Fe-collection smelting of spent automotive catalysts due to its good comprehensive performance.展开更多
The phase composition and microstructure of alkaline vanadium slag were characterized using scanning electron microscopy and energy-dispersive X-ray spectroscopy(SEM-EDS)and X-ray diffraction(XRD).A crystallization mo...The phase composition and microstructure of alkaline vanadium slag were characterized using scanning electron microscopy and energy-dispersive X-ray spectroscopy(SEM-EDS)and X-ray diffraction(XRD).A crystallization model of spinel was established to calculate the effects of basicity(the mass ratio of CaO to SiO_(2))and P_(2)O_(5) on crystal growth rates and precipitation patterns.Based on the crystal size distribution(CSD)theory,the size distribution and growth mechanisms of spinel crystals in alkaline vanadium slag at different temperatures were investigated.The results revealed that,at a cooling rate of 5 K/min,the mean grain size of spinel increased from 12.77 to 21.52μm as the temperature decreased from 1748 to 1598 K,with spinel growth being controlled by the interface.At 1548 K,the spinel particle size reached 31.04μm,indicating a supply-controlled growth mechanism as the temperature decreased from 1598 to 1548 K.Increased P_(2)O_(5) content hindered the crystal growth,while an increase in basicity promoted nucleation and growth.Furthermore,MnCr_(2)O_(4) preferentially crystallized and grew in alkaline vanadium slag.展开更多
基金supported by the National Natural Science Foundation of China(No.52374409)the National Key Research and Development Program of China(No.2022YFB3504304).
文摘The effect of Al_(2)O_(3)/SiO_(2) mass ratio and CaO content on the viscosity and structure of the CaO-Al_(2)O_(3)-SiO_(2)-6MgO-1.5ZrO_(2)-1.5CeO_(2) slag was investigated.The results show that with the increase in Al_(2)O_(3)/SiO_(2) mass ratio,the viscous flow units within the slag gradually change from Si-O-Si to Al-O-Al and Al-O-Si.Furthermore,the substitution of Al_(2)O_(3) for SiO_(2) leads to the transformation of Si-O bonds towards weaker Al-O bonds,which weaken the bond strength of the aluminosilicate networks,thus leading to a decrease in the viscosity of slag.The increase in CaO content effectively promotes the depolymerization of the aluminosilicate networks,resulting in a significant decrease in the viscosity of the slag.The slag with Al_(2)O_(3)/SiO_(2) of 0.7-1.5 and CaO of 30 wt.%shows promise as the reference slag system for the Fe-collection smelting of spent automotive catalysts due to its good comprehensive performance.
基金supported by the National Natural Science Foundation of China(No.51974047)the Natural Science Foundation of Chongqing,China(No.cstc2022ycjh-bgzxm0003)the Large Instrument Foundation of Chongqing University,China(No.202303150239)。
文摘The phase composition and microstructure of alkaline vanadium slag were characterized using scanning electron microscopy and energy-dispersive X-ray spectroscopy(SEM-EDS)and X-ray diffraction(XRD).A crystallization model of spinel was established to calculate the effects of basicity(the mass ratio of CaO to SiO_(2))and P_(2)O_(5) on crystal growth rates and precipitation patterns.Based on the crystal size distribution(CSD)theory,the size distribution and growth mechanisms of spinel crystals in alkaline vanadium slag at different temperatures were investigated.The results revealed that,at a cooling rate of 5 K/min,the mean grain size of spinel increased from 12.77 to 21.52μm as the temperature decreased from 1748 to 1598 K,with spinel growth being controlled by the interface.At 1548 K,the spinel particle size reached 31.04μm,indicating a supply-controlled growth mechanism as the temperature decreased from 1598 to 1548 K.Increased P_(2)O_(5) content hindered the crystal growth,while an increase in basicity promoted nucleation and growth.Furthermore,MnCr_(2)O_(4) preferentially crystallized and grew in alkaline vanadium slag.