The pinch instability theory with free surface and wave superposition principle was applied to understanding the critical disturbance wavelength and the theoretical bead width for the single weld pool formed during th...The pinch instability theory with free surface and wave superposition principle was applied to understanding the critical disturbance wavelength and the theoretical bead width for the single weld pool formed during the triple-electrode high speed CO2 welding. In addition, the reason for higher stability in the single weld pool was analyzed. Then single-, twin-, and triple-electrode overlaying experiments were conducted. It was found that triple-electrode CO2 welding can improve welding efficiency greatly without reducing the weld quality. The results indicated that the oscillation frequcncy of the weld pool increased, oscillation wavelength decreased, and bead width increased with the increase of welding electrodes under the same disturbance circumstances.展开更多
The occurrence of arc interference between the adjacent arcs becomes an important problem in triple-electrode high speed CO2 fillet welding. To clarify this problem, polarities effects on arc interference were investi...The occurrence of arc interference between the adjacent arcs becomes an important problem in triple-electrode high speed CO2 fillet welding. To clarify this problem, polarities effects on arc interference were investigated. The experimental results and theoretical analysis showed that the reverse magnetic field generated by the middle wire （ DCEN or DCEP ） decreased the arc deflection due to arc interference. The average arc voltage fluctuations induced by DCEP/DECN/DCEP and DCEN/DCEP/DCEN were smaller than those induced by the other polarities.展开更多
Laser multipass welding techniques for thick section steels have been developed using a new type of UV combined narrow groove. The shape and sizes at the bottom of groove are determined by analyzing the plasma behavio...Laser multipass welding techniques for thick section steels have been developed using a new type of UV combined narrow groove. The shape and sizes at the bottom of groove are determined by analyzing the plasma behavior using high speed photographic equipment. A stable autogenous CO2 laser welding process and greater penetration are generated at the root pass because of strong reduction of the plasma volume. According to the waveforms of welding current and arc voltage, and the interaction between the arc and the laser induced plasma, a suitable groove angle is obtained. Laser-double MIG hybrid welding process is studied and the optimum distances between the laser and two arcs are determined. By using autogenous CO2 laser welding, CO2 laser-MIG hybrid welding and laser-double MIG hybrid welding, 28 mm thick steel plates are welded with four passes. The welds produced are assessed by X-ray. No crack is found and there is only a small amount of pores. The experimental results show that the multipuss welding procedures proposed can realize the joining of thick section steels with high efficiency and good quality.展开更多
This paper introduced the basic theory and algorithm of the surrogate data method, which proposed a rigorous way to detect the random and seemingly stochastic characteristics in a system. The Gaussian data and the Ros...This paper introduced the basic theory and algorithm of the surrogate data method, which proposed a rigorous way to detect the random and seemingly stochastic characteristics in a system. The Gaussian data and the Rossler data were used to show the availability and effectivity of this method. According to the analysis by this method based on the short-circuiting current signals under the conditions of the same voltage and different wire feed speeds, it is demonstrated that the electrical signals time series exhibit apparently randomness when the welding parameters do not match. However, the electrical signals time series are deterministic when a match is found. The stability of short-circuiting transfer process could be judged exactly by the method of surrogate data.展开更多
A new kind of simple and flexible CO2 welding system was developed to carry out waveform control. The system consisted of IGBT inverter, PWM circuit and microprocessor unit （ MPU） , in which the output current of co...A new kind of simple and flexible CO2 welding system was developed to carry out waveform control. The system consisted of IGBT inverter, PWM circuit and microprocessor unit （ MPU） , in which the output current of constant current （CC） power supply could be changed according to transient physical state, and the variable down slope rate control could be used to ensure a stable welding process. The welding experiment results proved the effectiveness of this control approach.展开更多
The statistical probability and their variation regularity of the measurable characteristic parameters in the CO 2 arc welding droplet short circuiting transfer process have been studied. The statistical analysis sh...The statistical probability and their variation regularity of the measurable characteristic parameters in the CO 2 arc welding droplet short circuiting transfer process have been studied. The statistical analysis shows that the sensitivity of each characteristic parameter with regard to the variation of the short circuiting transfer process is different. The sensitivity of 4 kinds among these characteristic parameters is more intense than that of the short circuiting transfer frequency. In order to take account of the synthetic influence of these characteristic parameters, by means of the characteristic parameters synthetic value, a quantitative evaluation function is built up to describe and evaluate the short circuiting transfer process of CO 2 arc welding in real time. The testing shows that the evaluation function can give a suitable synthetic valuation for the short circuiting transfer process with a variety of welding variables.展开更多
In this paper, a high-speed camera and an optical emission monitor were used to study the behavior of vapor/ plasma during CO2 laser welding of SUS304 stainless steel. Results of optical emission from vapor/plasma sho...In this paper, a high-speed camera and an optical emission monitor were used to study the behavior of vapor/ plasma during CO2 laser welding of SUS304 stainless steel. Results of optical emission from vapor/plasma show that two characteristic frequency bands exist, 100 -500 Hz and 1 500 -3 500 Hz. At the same time, the changing images of vapor/ plasma and bottom pool also confirm that there are two different fluctuation frequency bands. One of the frequency bands represents the characteristic of vapor/plasma within the keyhole, and it is within 167 -500 Hz. Another frequency band is within 1 500 - 3 500 Hz, and it obviously derives from the shielding gas. Some factors may cause these frequency differences between the keyhole plasma and the shielding gas plasma. One of them is that the vapor/plasma pressure within the keyhole will increase slowly.展开更多
The CO2 laser welding of BT20 titanium alloy and Ti-23Al-17Nb titanium aluminide was conducted to investigate into the porosity in titanium alloy weld. The results show that there are two sorts of porosities observed ...The CO2 laser welding of BT20 titanium alloy and Ti-23Al-17Nb titanium aluminide was conducted to investigate into the porosity in titanium alloy weld. The results show that there are two sorts of porosities observed in welds of titanium alloy laser welding based on the microscopic characteristics of the porosities. One is the metallurgical porosity with round and smooth inner wall, which results from the surface contamination. The other is the processing porosity with irregular and rough inner wall that displays the trace of the pool flowing, which results from the ruffle on the keyhole wall gathering together locally and closing down the gas in the keyhole into bubbles because of the keyhole fluctuating. The CO2 laser welding could break down easily the surface oxide film and produce little metallurgical porosity, but produces easily processing porosity when partial penetration or unstable-full penetration laser welding is conducted, which always occurs in the center of weld.展开更多
Bead-on-plate CO2 laser welding of 1 000 MPa grade transformation induced plasticity （TRIP） steel was conducted under different welding powers, welding speeds and shield gases. The macrostructural and microstructura...Bead-on-plate CO2 laser welding of 1 000 MPa grade transformation induced plasticity （TRIP） steel was conducted under different welding powers, welding speeds and shield gases. The macrostructural and microstructural features of the welded joint were investigated. The increase of welding speed reduced the width of the weld bead and the porosities in the weld bead resulting from the different flow mode of melted metal in weld pool. The decrease of welding power or use of shield gas of helium also contributed to the reduction of porosity in the weld bead due to the alleviation of induced plasma formation, thus stabilizing the keyhole. The porosity formation intimately correlated with the evaporation of alloy element Mn in the base metal. The laser welded metal had same martensite microstructure as that of water-quenched base metal. The welding parameters which increased cooling rate all led to fine microstructures of the weld bead.展开更多
The technology of CO2 laser welding and joint properties of titanium alloy were investigated. The problem of molten pool protection was resolved by designing a shielding trailer and a special clamp. Joints with silver...The technology of CO2 laser welding and joint properties of titanium alloy were investigated. The problem of molten pool protection was resolved by designing a shielding trailer and a special clamp. Joints with silvery appearance were obtained, which have no pore and crack. In addition, the welding speed could reach 3 m/min for the plate of 1.5 mm thickness being penetrated. The reason of the porosity formation in partial penetration joints is that the keyholes can be easily cut apart in the radial direction, which makes the gas enclosed in the molten pool. The surface oxide of specimens can not affect the porosity formation in welds directly.展开更多
A general industrial CCD( ICCD) camera is redesigned to detect the weld pool without arc at the period of short circuiting, so that the interference of arc and spatter during CO2 short circuiting arc welding is elim...A general industrial CCD( ICCD) camera is redesigned to detect the weld pool without arc at the period of short circuiting, so that the interference of arc and spatter during CO2 short circuiting arc welding is eliminated. Through the analysis of weld pool image, both size parameters (such as weld pool area A, weld pool length L1, L2 and weld pool breadth b) and contour parameters (b, which describe the curves of weld pool boundany) ,which could indicate the shape features of weld pool, had been defined to express weld pool information quantitatively. The investigation of the relationships between weld pool shape parameters and welding process parameters may be beneficial to the quality control of CO2 welding.展开更多
590 MPa automobile beam steel strips are used mainly to manufacture the longitudinal beam of trucks.It’s welding properties are critical to the safety of truck.The microstructure and mechanical properties of welding ...590 MPa automobile beam steel strips are used mainly to manufacture the longitudinal beam of trucks.It’s welding properties are critical to the safety of truck.The microstructure and mechanical properties of welding joints processed by CO 2 arc welding with different welding parameters were studied.The results showed that the welding joints were weak when welding heat input were small and the non metal inclusions were found in the weld joints when welding heat input are big.The quality of the welding joints is good enough at 170A of the arc current and 24V of the arc voltage.Keeping the other welding parameters fixed,the incomplete fusion defect occurred in the welding joint with backward welding,but the quality of the welding joint is good with forward welding.展开更多
In continuous wave CO2 laser-TlG hybrid welding process, the laser energy is not fully utilized because of the absorption and defocusing by plasma in the arc space. Therefore, the optimal welding result can only be ac...In continuous wave CO2 laser-TlG hybrid welding process, the laser energy is not fully utilized because of the absorption and defocusing by plasma in the arc space. Therefore, the optimal welding result can only be achieved in a limited energy range. In order to improve the welding performance further, a novel hybrid welding method--pulse CO2 laser-TIG arc hybrid welding by coordinated control is proposed and investigated. The experimental results indicate that, compared with continuous wave CO2 laser-TIG hybrid welding, the absorption and defocusing of laser energy by plasma are decreased further, and at the same time, the availability ratio of laser and arc energy can be increased when a coordinated frequency is controlled. As a result, the weld appearance is also improved as well as the weld depth is deepened. Furthermore, the effect of frequency and phase of pulse laser and TIG arc on the arc images and welding characteristics is also studied. However, the novel hybrid method has great potentials in the application of industrials from views of techniques and economy.展开更多
A new simulation model of CO 2 short circuiting transfer welding may be employed to develop a new pattern of welding machine and to predict welding process parameters to obtain the optimum welding technology propert...A new simulation model of CO 2 short circuiting transfer welding may be employed to develop a new pattern of welding machine and to predict welding process parameters to obtain the optimum welding technology properties. In this paper, a new simulating model is developed according to the AWP (adapting welding physics process) waveform control method. Good agreement is shown between the predicted and experimentally determined results. The model will make an important promotion in the development of CO 2 arc welding technique.展开更多
A new current wave controlling method for short circuit transition CO 2 welding using saturable inductor is put forward in this paper. Theory analysis and experiment results prove that the inverter's dynamic char...A new current wave controlling method for short circuit transition CO 2 welding using saturable inductor is put forward in this paper. Theory analysis and experiment results prove that the inverter's dynamic characteristics is greatly improved, the declining speed of current during liquid bridge neck shrinking is quicker, subsequently the energy accumulated in the bridge and the radius of the bridge before rupturing is reduced thus the low spatter result is achieved.展开更多
A simulation system used in the arc welding short circuit transfer process and current waveform control process was developed in this paper. The simulation results are basically consistent with welding technical exper...A simulation system used in the arc welding short circuit transfer process and current waveform control process was developed in this paper. The simulation results are basically consistent with welding technical experiments. The simulation system can be used to simulate and test the current waveform control parameters with welding variables. By this simulation system, the influence regularities of the current waveform control parameters in the CO 2 arc welding droplet short circuit transfer process can be got. Moreover, the basic mode of real time current waveform control can be also established by the simulation testing.展开更多
Conventional fusion arc welding of high-strength quenched and tempered steel can be improved through the use of non-conventional laser beam welding. This article presents the investigations of autogenous bead on plate...Conventional fusion arc welding of high-strength quenched and tempered steel can be improved through the use of non-conventional laser beam welding. This article presents the investigations of autogenous bead on plate and butt CO<sub>2</sub> Laser Welding (LW) of 7 mm thick high-strength quenched and tempered low alloy SM570 (JIS) steel plates. The influence of laser welding parameters, mainly welding speed, defocusing distance and shielding gas flow rate on the weld profile, i.e., weld zone penetration depth and width, microstructure and mechanical properties of welded joints was determined. All welded joints showed smooth and uniform weld beads free from superficial porosity and undercuts. The selected best welding conditions were a laser power of 5.0 kW, welding speed of 500 mm/min, argon gas shielding flow rate of 30 L/min and a defocusing distance of -0.5 mm. It was observed that these conditions gave complete penetration and minimized the width of the weld bead. The microstructure of the welded joints was evaluated by light optical microscopy. The weld metal (WM) and heat-affected zone (HAZ) near weld metal achieved maximum hardness (355 HV). The tensile fractured samples showed the ductile mode of failure and ultimate tensile strength of 580 MPa.展开更多
In order to improve the weldability of duplex stainless steels,obtaining more secondary austenite in the weld metal is an effective way.Therefore,optimizing the secondary austenite by changing its morphology,volume fr...In order to improve the weldability of duplex stainless steels,obtaining more secondary austenite in the weld metal is an effective way.Therefore,optimizing the secondary austenite by changing its morphology,volume fraction and stability may be expected to enhance the ductility of the weld.The secondary austenite morphologies in the fusion zone of the laser continuously heat treated welds of 2205 duplex stainless steel were investigated.The secondary austenite morphologies were found to be influenced by different laser power level.The secondary austenite with penniform,freely grown and dendritic shape appeared in the course of 4,6 and 8 kW continuous heat treatment,respectively.It was found that there were three kinds of morphologies of secondary austenite in the fusion zone treated by different power,i.e.,widmannst¨atten austenite,grain boundary austenite and intragranular austenite.The results demonstrated that the mechanism of the secondary austenite formation was a displacement mechanism during the initial austenite lath formation and a diffusion mechanism during cooling.The nitrides provided the nitrogen for the transformation and at the same time acted as nucleation sites for the secondary austenite.展开更多
Waveform control method was commonly adopted to reduce the spatter of CO2 arc welding and improve the weld formation. It certainly would reduce the self-regulation ability of arc due to the adoption of segmented const...Waveform control method was commonly adopted to reduce the spatter of CO2 arc welding and improve the weld formation. It certainly would reduce the self-regulation ability of arc due to the adoption of segmented constant current control which especially led to arc＂ blowout with the abrupt change oat＂ arc＂ length or downward welding. Therefore alterative wire-feed system based on arc voltage negative feedback was put forward to improve the .stability of arc＂ length in this paper. Double closed-loop and double fuzzy P1 regulation were adopted in this system. Fuzzy control of induced voltage was adopted in the inner-loop which improved the stability and fast response of wire-feed system. Fuzz）＂ control of arc＂ voltage negative feedback was used in the outer-loop whose output .served as the input of negative feedback regulation of inner-loop induced voltage. This method could remain arc＂ length and weld penetration unchan, ged on the basils of reducing spatter and improving formation and it was proved by downward welding tests.展开更多
文摘The pinch instability theory with free surface and wave superposition principle was applied to understanding the critical disturbance wavelength and the theoretical bead width for the single weld pool formed during the triple-electrode high speed CO2 welding. In addition, the reason for higher stability in the single weld pool was analyzed. Then single-, twin-, and triple-electrode overlaying experiments were conducted. It was found that triple-electrode CO2 welding can improve welding efficiency greatly without reducing the weld quality. The results indicated that the oscillation frequcncy of the weld pool increased, oscillation wavelength decreased, and bead width increased with the increase of welding electrodes under the same disturbance circumstances.
文摘The occurrence of arc interference between the adjacent arcs becomes an important problem in triple-electrode high speed CO2 fillet welding. To clarify this problem, polarities effects on arc interference were investigated. The experimental results and theoretical analysis showed that the reverse magnetic field generated by the middle wire （ DCEN or DCEP ） decreased the arc deflection due to arc interference. The average arc voltage fluctuations induced by DCEP/DECN/DCEP and DCEN/DCEP/DCEN were smaller than those induced by the other polarities.
文摘Laser multipass welding techniques for thick section steels have been developed using a new type of UV combined narrow groove. The shape and sizes at the bottom of groove are determined by analyzing the plasma behavior using high speed photographic equipment. A stable autogenous CO2 laser welding process and greater penetration are generated at the root pass because of strong reduction of the plasma volume. According to the waveforms of welding current and arc voltage, and the interaction between the arc and the laser induced plasma, a suitable groove angle is obtained. Laser-double MIG hybrid welding process is studied and the optimum distances between the laser and two arcs are determined. By using autogenous CO2 laser welding, CO2 laser-MIG hybrid welding and laser-double MIG hybrid welding, 28 mm thick steel plates are welded with four passes. The welds produced are assessed by X-ray. No crack is found and there is only a small amount of pores. The experimental results show that the multipuss welding procedures proposed can realize the joining of thick section steels with high efficiency and good quality.
基金supported by the Young Scientists Fund of the National Natural Science Foundation of China(Grant No.51205283)
文摘This paper introduced the basic theory and algorithm of the surrogate data method, which proposed a rigorous way to detect the random and seemingly stochastic characteristics in a system. The Gaussian data and the Rossler data were used to show the availability and effectivity of this method. According to the analysis by this method based on the short-circuiting current signals under the conditions of the same voltage and different wire feed speeds, it is demonstrated that the electrical signals time series exhibit apparently randomness when the welding parameters do not match. However, the electrical signals time series are deterministic when a match is found. The stability of short-circuiting transfer process could be judged exactly by the method of surrogate data.
基金Supported by Research Project of Henan Science and Technology Foundation(0124110209,0211061900).
文摘A new kind of simple and flexible CO2 welding system was developed to carry out waveform control. The system consisted of IGBT inverter, PWM circuit and microprocessor unit （ MPU） , in which the output current of constant current （CC） power supply could be changed according to transient physical state, and the variable down slope rate control could be used to ensure a stable welding process. The welding experiment results proved the effectiveness of this control approach.
文摘The statistical probability and their variation regularity of the measurable characteristic parameters in the CO 2 arc welding droplet short circuiting transfer process have been studied. The statistical analysis shows that the sensitivity of each characteristic parameter with regard to the variation of the short circuiting transfer process is different. The sensitivity of 4 kinds among these characteristic parameters is more intense than that of the short circuiting transfer frequency. In order to take account of the synthetic influence of these characteristic parameters, by means of the characteristic parameters synthetic value, a quantitative evaluation function is built up to describe and evaluate the short circuiting transfer process of CO 2 arc welding in real time. The testing shows that the evaluation function can give a suitable synthetic valuation for the short circuiting transfer process with a variety of welding variables.
文摘In this paper, a high-speed camera and an optical emission monitor were used to study the behavior of vapor/ plasma during CO2 laser welding of SUS304 stainless steel. Results of optical emission from vapor/plasma show that two characteristic frequency bands exist, 100 -500 Hz and 1 500 -3 500 Hz. At the same time, the changing images of vapor/ plasma and bottom pool also confirm that there are two different fluctuation frequency bands. One of the frequency bands represents the characteristic of vapor/plasma within the keyhole, and it is within 167 -500 Hz. Another frequency band is within 1 500 - 3 500 Hz, and it obviously derives from the shielding gas. Some factors may cause these frequency differences between the keyhole plasma and the shielding gas plasma. One of them is that the vapor/plasma pressure within the keyhole will increase slowly.
文摘The CO2 laser welding of BT20 titanium alloy and Ti-23Al-17Nb titanium aluminide was conducted to investigate into the porosity in titanium alloy weld. The results show that there are two sorts of porosities observed in welds of titanium alloy laser welding based on the microscopic characteristics of the porosities. One is the metallurgical porosity with round and smooth inner wall, which results from the surface contamination. The other is the processing porosity with irregular and rough inner wall that displays the trace of the pool flowing, which results from the ruffle on the keyhole wall gathering together locally and closing down the gas in the keyhole into bubbles because of the keyhole fluctuating. The CO2 laser welding could break down easily the surface oxide film and produce little metallurgical porosity, but produces easily processing porosity when partial penetration or unstable-full penetration laser welding is conducted, which always occurs in the center of weld.
文摘Bead-on-plate CO2 laser welding of 1 000 MPa grade transformation induced plasticity （TRIP） steel was conducted under different welding powers, welding speeds and shield gases. The macrostructural and microstructural features of the welded joint were investigated. The increase of welding speed reduced the width of the weld bead and the porosities in the weld bead resulting from the different flow mode of melted metal in weld pool. The decrease of welding power or use of shield gas of helium also contributed to the reduction of porosity in the weld bead due to the alleviation of induced plasma formation, thus stabilizing the keyhole. The porosity formation intimately correlated with the evaporation of alloy element Mn in the base metal. The laser welded metal had same martensite microstructure as that of water-quenched base metal. The welding parameters which increased cooling rate all led to fine microstructures of the weld bead.
文摘The technology of CO2 laser welding and joint properties of titanium alloy were investigated. The problem of molten pool protection was resolved by designing a shielding trailer and a special clamp. Joints with silvery appearance were obtained, which have no pore and crack. In addition, the welding speed could reach 3 m/min for the plate of 1.5 mm thickness being penetrated. The reason of the porosity formation in partial penetration joints is that the keyholes can be easily cut apart in the radial direction, which makes the gas enclosed in the molten pool. The surface oxide of specimens can not affect the porosity formation in welds directly.
基金This project is supported by National 863 project( No.412-9913-02)and National Natural Science Foundation of China(No.599750
文摘A general industrial CCD( ICCD) camera is redesigned to detect the weld pool without arc at the period of short circuiting, so that the interference of arc and spatter during CO2 short circuiting arc welding is eliminated. Through the analysis of weld pool image, both size parameters (such as weld pool area A, weld pool length L1, L2 and weld pool breadth b) and contour parameters (b, which describe the curves of weld pool boundany) ,which could indicate the shape features of weld pool, had been defined to express weld pool information quantitatively. The investigation of the relationships between weld pool shape parameters and welding process parameters may be beneficial to the quality control of CO2 welding.
文摘590 MPa automobile beam steel strips are used mainly to manufacture the longitudinal beam of trucks.It’s welding properties are critical to the safety of truck.The microstructure and mechanical properties of welding joints processed by CO 2 arc welding with different welding parameters were studied.The results showed that the welding joints were weak when welding heat input were small and the non metal inclusions were found in the weld joints when welding heat input are big.The quality of the welding joints is good enough at 170A of the arc current and 24V of the arc voltage.Keeping the other welding parameters fixed,the incomplete fusion defect occurred in the welding joint with backward welding,but the quality of the welding joint is good with forward welding.
文摘In continuous wave CO2 laser-TlG hybrid welding process, the laser energy is not fully utilized because of the absorption and defocusing by plasma in the arc space. Therefore, the optimal welding result can only be achieved in a limited energy range. In order to improve the welding performance further, a novel hybrid welding method--pulse CO2 laser-TIG arc hybrid welding by coordinated control is proposed and investigated. The experimental results indicate that, compared with continuous wave CO2 laser-TIG hybrid welding, the absorption and defocusing of laser energy by plasma are decreased further, and at the same time, the availability ratio of laser and arc energy can be increased when a coordinated frequency is controlled. As a result, the weld appearance is also improved as well as the weld depth is deepened. Furthermore, the effect of frequency and phase of pulse laser and TIG arc on the arc images and welding characteristics is also studied. However, the novel hybrid method has great potentials in the application of industrials from views of techniques and economy.
基金ThisresearchissupportedbytheNationalNatureScienceFoundation (No .5 9975068)andTianjinNatureScienceFoundation (No .993 60 2 911)
文摘A new simulation model of CO 2 short circuiting transfer welding may be employed to develop a new pattern of welding machine and to predict welding process parameters to obtain the optimum welding technology properties. In this paper, a new simulating model is developed according to the AWP (adapting welding physics process) waveform control method. Good agreement is shown between the predicted and experimentally determined results. The model will make an important promotion in the development of CO 2 arc welding technique.
文摘A new current wave controlling method for short circuit transition CO 2 welding using saturable inductor is put forward in this paper. Theory analysis and experiment results prove that the inverter's dynamic characteristics is greatly improved, the declining speed of current during liquid bridge neck shrinking is quicker, subsequently the energy accumulated in the bridge and the radius of the bridge before rupturing is reduced thus the low spatter result is achieved.
文摘A simulation system used in the arc welding short circuit transfer process and current waveform control process was developed in this paper. The simulation results are basically consistent with welding technical experiments. The simulation system can be used to simulate and test the current waveform control parameters with welding variables. By this simulation system, the influence regularities of the current waveform control parameters in the CO 2 arc welding droplet short circuit transfer process can be got. Moreover, the basic mode of real time current waveform control can be also established by the simulation testing.
文摘Conventional fusion arc welding of high-strength quenched and tempered steel can be improved through the use of non-conventional laser beam welding. This article presents the investigations of autogenous bead on plate and butt CO<sub>2</sub> Laser Welding (LW) of 7 mm thick high-strength quenched and tempered low alloy SM570 (JIS) steel plates. The influence of laser welding parameters, mainly welding speed, defocusing distance and shielding gas flow rate on the weld profile, i.e., weld zone penetration depth and width, microstructure and mechanical properties of welded joints was determined. All welded joints showed smooth and uniform weld beads free from superficial porosity and undercuts. The selected best welding conditions were a laser power of 5.0 kW, welding speed of 500 mm/min, argon gas shielding flow rate of 30 L/min and a defocusing distance of -0.5 mm. It was observed that these conditions gave complete penetration and minimized the width of the weld bead. The microstructure of the welded joints was evaluated by light optical microscopy. The weld metal (WM) and heat-affected zone (HAZ) near weld metal achieved maximum hardness (355 HV). The tensile fractured samples showed the ductile mode of failure and ultimate tensile strength of 580 MPa.
基金support from the National Basic Research Program of China(973 Program,No. 2010CB630800)the Shanghai Municipal Science and Technology Commission Foundation of China (Grant No. 0852nm02500)
文摘In order to improve the weldability of duplex stainless steels,obtaining more secondary austenite in the weld metal is an effective way.Therefore,optimizing the secondary austenite by changing its morphology,volume fraction and stability may be expected to enhance the ductility of the weld.The secondary austenite morphologies in the fusion zone of the laser continuously heat treated welds of 2205 duplex stainless steel were investigated.The secondary austenite morphologies were found to be influenced by different laser power level.The secondary austenite with penniform,freely grown and dendritic shape appeared in the course of 4,6 and 8 kW continuous heat treatment,respectively.It was found that there were three kinds of morphologies of secondary austenite in the fusion zone treated by different power,i.e.,widmannst¨atten austenite,grain boundary austenite and intragranular austenite.The results demonstrated that the mechanism of the secondary austenite formation was a displacement mechanism during the initial austenite lath formation and a diffusion mechanism during cooling.The nitrides provided the nitrogen for the transformation and at the same time acted as nucleation sites for the secondary austenite.
文摘Waveform control method was commonly adopted to reduce the spatter of CO2 arc welding and improve the weld formation. It certainly would reduce the self-regulation ability of arc due to the adoption of segmented constant current control which especially led to arc＂ blowout with the abrupt change oat＂ arc＂ length or downward welding. Therefore alterative wire-feed system based on arc voltage negative feedback was put forward to improve the .stability of arc＂ length in this paper. Double closed-loop and double fuzzy P1 regulation were adopted in this system. Fuzzy control of induced voltage was adopted in the inner-loop which improved the stability and fast response of wire-feed system. Fuzz）＂ control of arc＂ voltage negative feedback was used in the outer-loop whose output .served as the input of negative feedback regulation of inner-loop induced voltage. This method could remain arc＂ length and weld penetration unchan, ged on the basils of reducing spatter and improving formation and it was proved by downward welding tests.