Enhancement of post-annealing stability in Co/ Ni multilayers with perpendicular magnetic anisotropy （PMA） was obtained by inserting Au layers into Ni/Co interfaces. After annealing at 350 ℃, the effective mag- net...Enhancement of post-annealing stability in Co/ Ni multilayers with perpendicular magnetic anisotropy （PMA） was obtained by inserting Au layers into Ni/Co interfaces. After annealing at 350 ℃, the effective mag- netic anisotropy density （Kef0 for Ta（3）/Pt（2）/[Co（0.3）/ Ni（0.6）/Au（0.3）]× 3/Co（0.3）/Pt（1）/Ta（3） （in nm） keeps at 0.48 × 105 J·m^-3. Scanning transmission electron micro- scopy-high-angle annular dark field （STEM-HAADF） analysis shows that the diffusion between Ni and Co layers is obstructed by the Au insertion layers among them, which is responsible for the post-annealing stability enhancement of the multilayers. Multilayers with Pt insertion layers were also investigated as reference samples in this work. Com- pared with Pt-layer-inserted Co/Ni multilayers, the Au insertion layers are found to bring seldom interfacial PMA to the multilayers, making it competitive in being employed to enhance the post-annealing stability of PMA Co/Ni multilayers which are used for magnetic random access memory devices （MRAM）.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.51101012, 51271211,51331002,51371025,51371027,51471028 and 51571017)the National Key Scientific Research Projects of China(No. 2015CB921502)+1 种基金the Beijing Nova Program(No.Z141103001814039)the Fundamental Research Funds for the Central Universities(No. FRF-TP-14-002C1)
文摘Enhancement of post-annealing stability in Co/ Ni multilayers with perpendicular magnetic anisotropy （PMA） was obtained by inserting Au layers into Ni/Co interfaces. After annealing at 350 ℃, the effective mag- netic anisotropy density （Kef0 for Ta（3）/Pt（2）/[Co（0.3）/ Ni（0.6）/Au（0.3）]× 3/Co（0.3）/Pt（1）/Ta（3） （in nm） keeps at 0.48 × 105 J·m^-3. Scanning transmission electron micro- scopy-high-angle annular dark field （STEM-HAADF） analysis shows that the diffusion between Ni and Co layers is obstructed by the Au insertion layers among them, which is responsible for the post-annealing stability enhancement of the multilayers. Multilayers with Pt insertion layers were also investigated as reference samples in this work. Com- pared with Pt-layer-inserted Co/Ni multilayers, the Au insertion layers are found to bring seldom interfacial PMA to the multilayers, making it competitive in being employed to enhance the post-annealing stability of PMA Co/Ni multilayers which are used for magnetic random access memory devices （MRAM）.