An organic-inorganic hybrid sealing agent was fabricated and used in the plasma sprayed Al_(2)O_(3)-13 wt%TiO_(2)coating,and conventional silicone agent was also used for comparison.Protection performance of the coati...An organic-inorganic hybrid sealing agent was fabricated and used in the plasma sprayed Al_(2)O_(3)-13 wt%TiO_(2)coating,and conventional silicone agent was also used for comparison.Protection performance of the coatings was comprehensively evaluated based on both anti-corrosion and anti-biofouling properties.The results reveal that the sealing treatment is remarkably useful to decrease the porosity of the coating,and the porosity of the coating sealed with the hybrid agent is only 0.035%.Immersion corrosion test and Tafel polarization test reveal that the sealed coating with the hybrid agent exhibits a better corrosion resistance by compared with the coating sealed with silicone agent.The corrosion current density i_(corr) of the hybrid agent sealed coating is only 0.7×10^(-6)A·cm^(-2).Moreover,anti-biofouling tests both in the outdoor analogue hydraulic environment and in the natural marine environment prove that the mentioned novel coating presents a better combination of corrosion resistance and anti-biofouling property by compared with the other coatings,and it could be used as a protection of metal components in the marine environment.展开更多
The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing...The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing are investigated by using X-ray diffractometry （XRD） , scanning electron microsopy （SEM） and energy dis- persive spectroscopy （EDS）. Moreover, the microhardness of the substrate and the coating are investigated using Vickers mierohardness tester, the friction and wear behaviors of the substrate and the coating are investigated by using a block-on-ring tribometer under dry sliding conditions with the load of 245 N. The results show that both γ-Al2O3 and α-Al2O3 phases are observed in the as-sprayed coatings, the mian phase is γ-Al2O3. There are white particulates Al2O3 on its surface. The Al2O3-13 wt. % TiO2 coating possesses higher mierohardness which is about 1018HV and 1.6 times that of the substrate. The wear performance of coating is better than that of the substrate. In a practical application, the life of the extrusion wheel which is plasma sprayed Al2O3-13 wt. % TiO2 coating on the surface is 1.2 times that of the conventional extrusion wheel, and the life is about 330 h.展开更多
基金the National Natural Science Foundation of China(No.51379070)the Graduate Research and Innovation Projects of Jiangsu Province(No.KYCX21_0463)。
文摘An organic-inorganic hybrid sealing agent was fabricated and used in the plasma sprayed Al_(2)O_(3)-13 wt%TiO_(2)coating,and conventional silicone agent was also used for comparison.Protection performance of the coatings was comprehensively evaluated based on both anti-corrosion and anti-biofouling properties.The results reveal that the sealing treatment is remarkably useful to decrease the porosity of the coating,and the porosity of the coating sealed with the hybrid agent is only 0.035%.Immersion corrosion test and Tafel polarization test reveal that the sealed coating with the hybrid agent exhibits a better corrosion resistance by compared with the coating sealed with silicone agent.The corrosion current density i_(corr) of the hybrid agent sealed coating is only 0.7×10^(-6)A·cm^(-2).Moreover,anti-biofouling tests both in the outdoor analogue hydraulic environment and in the natural marine environment prove that the mentioned novel coating presents a better combination of corrosion resistance and anti-biofouling property by compared with the other coatings,and it could be used as a protection of metal components in the marine environment.
文摘The conventional Al2O3-13 wt. % TiO2 composite ceramic coatings are fabricated by plasma spraying on the surface of extrusion wheel. The microstrueture, morphology and phase compositions of the substrate and coat- ing are investigated by using X-ray diffractometry （XRD） , scanning electron microsopy （SEM） and energy dis- persive spectroscopy （EDS）. Moreover, the microhardness of the substrate and the coating are investigated using Vickers mierohardness tester, the friction and wear behaviors of the substrate and the coating are investigated by using a block-on-ring tribometer under dry sliding conditions with the load of 245 N. The results show that both γ-Al2O3 and α-Al2O3 phases are observed in the as-sprayed coatings, the mian phase is γ-Al2O3. There are white particulates Al2O3 on its surface. The Al2O3-13 wt. % TiO2 coating possesses higher mierohardness which is about 1018HV and 1.6 times that of the substrate. The wear performance of coating is better than that of the substrate. In a practical application, the life of the extrusion wheel which is plasma sprayed Al2O3-13 wt. % TiO2 coating on the surface is 1.2 times that of the conventional extrusion wheel, and the life is about 330 h.