The formation conditions of MgB2 in 2LiBH4 ＋ MgH2 system during dehydrogenation were investigated and its mechanism was discussed. The results show that direct decomposition of LiBH4 is suppressed under relative high...The formation conditions of MgB2 in 2LiBH4 ＋ MgH2 system during dehydrogenation were investigated and its mechanism was discussed. The results show that direct decomposition of LiBH4 is suppressed under relative higher initial dehydrogenation pressure of 4.0×10^5 Pa, wherein LiBH4 reacts with Mg to yield MgB2, and 9.16% （mass fraction） hydrogen is released within 9.6 h at 450 ℃. However, under relatively lower initial dehydrogenation pressure of 1.0×10^2 Pa, LiBH4 decomposes independently instead of reacting with Mg, resulting in no formation of MgB2, and 7.91% hydrogen is desorbed within 5.2 h at 450 ℃. It is found that the dehydrogenation of 2LiBH4 ＋ MgH2 system proceeds more completely and more hydrogen desorption amount can be obtained within a definite time by forming MgB2. Furthermore, it is proposed that the formation process of MgB2 includes incubation period and nucleus growth process. Experimental results show that the formation process of MgB2, especially the incubation period, is promoted by increasing initial dehydrogenation pressure at constant temperature, and the incubation period is also influenced greatly by dehydrogenation temperature.展开更多
A novel method,bath smelting process,was developed to treat molybdenite concentrate aiming at the existing problems of traditional process.To understand the dissolving behavior of MoS2 in white matte,the binary phase ...A novel method,bath smelting process,was developed to treat molybdenite concentrate aiming at the existing problems of traditional process.To understand the dissolving behavior of MoS2 in white matte,the binary phase diagram of Cu2S-Mo2S was measured by the cooling curve method.The result shows that this system is a simple binary eutectic with a eutectic temperature of（1117.0±3.0）℃ and a eutectic composition of（1.70±0.20）% MoS2 in mass fraction.When the MoS2 addition exceeds 4.48%,MoS2 and Cu2S can form the ternary compound containing CuMo2S3 or Cu2Mo6S8.In the temperature range of copper smelting,1200-1300℃,molybdenite can dissolve in the cuprous sulfide.At 1200℃,the solubility of molybdenite can reach 14.8%.展开更多
ZrO2-mullite nano-ceramics were fabricated by in-situ controlled crystallizing from SiO2-Al2O3-ZrO2 amorphous bulk. The thermal transformation sequences of the SiO2-Al2O3-ZrO2 amorphous bulk were investigated by X-ray...ZrO2-mullite nano-ceramics were fabricated by in-situ controlled crystallizing from SiO2-Al2O3-ZrO2 amorphous bulk. The thermal transformation sequences of the SiO2-Al2O3-ZrO2 amorphous bulk were investigated by X-ray diffraction, infrared spectrum, scanning electron microscope and differential scanning calorimetric. And the mechanical properties of the nano-ceramics were studied. The results show that the bulks are still in amorphous state at 900 ℃ and the t-ZrO2 forms at about 950 ℃ with a faint spinel-like phase which changes into mullite on further heating. ZrO2 and mullite become major phases at 1 100 ℃ and an amount of m-ZrO2 occur at the same time. The sample heated at 950 ℃ for 2 h and then at 1 100 ℃ for 1 h shows very dense and homogenous microstructure with ball-like grains in size of 20-50 nm. With the increase of crystallization temperature up to 1 350 ℃, the grains grow quickly and some grow into lath-shaped grains with major diameter of 5 μm. After two-step treatment the highest micro-hardness, flexural strength and fracture toughness of the samples are 13.72 GPa, 520 MPa and 5.13 MPa·m1/2, respectively.展开更多
ZnO-containing slags are common in pyrometallurgical processing of the base metals and steel.This caused the interest to the thermodynamics of the ZnO-SiO2 system.A complete literature survey,critical evaluation of th...ZnO-containing slags are common in pyrometallurgical processing of the base metals and steel.This caused the interest to the thermodynamics of the ZnO-SiO2 system.A complete literature survey,critical evaluation of the available experimental data and a thermodynamic optimization of the phase equilibria and thermodynamic properties of the system ZnO-SiO2 at 1.013×105 Pa are presented.The molten oxide was described as an associate solution.The properties of liquid were reassessed and enthalpy term of the Gibbs energy of solid Zn2SiO4 was re-fitted to be compatible with the new data in the willemite primary phase field.The thermodynamic data set agrees well with the recent experimental observations.It can be used for predicting,e.g.,the thermodynamic properties and the domains of the phase diagram,like critical point of the liquid miscibility gap,with a better accuracy than using the previous assessments.A set of optimized model parameters were obtained,reproducing the reliable thermodynamic and phase equilibrium data within their experimental errors from 298 K to liquidus temperatures,over the entire composition range.The created database can be used in a Gibbs energy minimization software to calculate the thermodynamic properties and the phase diagram sections of interest.展开更多
The sintering characteristics at 1350℃ and leaching property at 80℃ of calcium aluminate clinkers in the CaO-Al2O3-SiO2 （C-A-S） system with different additions of FeO and Fe2O3 were investigated. FeO inhibits the ...The sintering characteristics at 1350℃ and leaching property at 80℃ of calcium aluminate clinkers in the CaO-Al2O3-SiO2 （C-A-S） system with different additions of FeO and Fe2O3 were investigated. FeO inhibits the conversion of β-Ca2SiO4 to γ-Ca2SiO4 and makes the clinker not pulverizable. FeO and Fe2O3 inhibit the formation of CaAl2O4, but promote the formation of Ca12Al14O33. The interplanar spacing at （2 1 1） crystal face of Ca12 Al14O33 in the clinker increases with the increase of FeO addition, which indicates that FeO forms solid solutions in Ca12Al14O33. The clinkers with Fe2O3 addition form a new phase Ca2Fe2O5, and the amount of Ca2Fe2o5 increases with the in crease of Fe2O3 addition. Both FeO and Fe2O3 do not affect the Al2O3 leaching rate of calcium aluminate clinker in sodium carbonate solution, but they increase the molar ratio of caustic Na2O to Al2O3 in the leached liquor.展开更多
The phase diagram of the CsBr-CaBr2 system was re-determined by using differential thermal analysis and high ternperature and room ternperature X-ray diffraction analysis. It is concluded that there are three intermed...The phase diagram of the CsBr-CaBr2 system was re-determined by using differential thermal analysis and high ternperature and room ternperature X-ray diffraction analysis. It is concluded that there are three intermediate compounds in this system： a.congruently melting compound, CsCaBr3, with a melting point of 823℃ and two incongruently melting compounds, Cs2CaBr4 and Cs3Ca2Br7, whose peritectic points being 597℃ and 635℃, respectively. X-ray diffraction analysis indicated that compound CsCaBr3 is of slightly distorted perovskite structure.展开更多
Revised phase diagram of the CeO2-ZrO2 system is optimized and the lattice stability parameters of CeO2 of various phases as well as solution parameters of phases (liquid, cubic, tetragonal and monoclinic) are simulta...Revised phase diagram of the CeO2-ZrO2 system is optimized and the lattice stability parameters of CeO2 of various phases as well as solution parameters of phases (liquid, cubic, tetragonal and monoclinic) are simultaneously obtained by using the Kaufman and Nesor's model for describing the ceramic solutions and the Lukas program展开更多
In this paper,the authors used the Mixed Coordination EXAFS Analysis Method recently published and IR to study the mixed coordination of Ge in glasses of Li_2O-ZnO-GeO_2 system,a new kind of syperionic conductor.The r...In this paper,the authors used the Mixed Coordination EXAFS Analysis Method recently published and IR to study the mixed coordination of Ge in glasses of Li_2O-ZnO-GeO_2 system,a new kind of syperionic conductor.The results show that when the content of ZnO is fixed,the ratio of [GeO_6] units is increased with the addition of Li_2O until the content of Li_2O is about 15%,and then decreased.The relationship between the ratio of [GeO_6]and the content of Li_2O is consistent with those between n,d of glass and Li_2O content, Therefore the germanium abnormalty can be explained as the change of coordination number.展开更多
In order to study the relationship between thickness and residual stress in CaO-Al2O3-SiO2 glass-ceramics.The residual stress was measured in CaO-Al2O3-SiO2 system glass-ceramic with different thickness,and the format...In order to study the relationship between thickness and residual stress in CaO-Al2O3-SiO2 glass-ceramics.The residual stress was measured in CaO-Al2O3-SiO2 system glass-ceramic with different thickness,and the formation mechanism and characterization of residual stress in CAS system Glass-ceramic were analyzed by the X-ray diffraction analysis.The experimental results show the compressive residual stress increass with thickness of glass-ceramic increasing.展开更多
This paper studies the asymptotic behavior of the diffractive interaction of pulses with two linear phases of length ε ≤ 1 in 2 × 2 semilinear strictly hyperbolic system with constant coefficiients. By a formal...This paper studies the asymptotic behavior of the diffractive interaction of pulses with two linear phases of length ε ≤ 1 in 2 × 2 semilinear strictly hyperbolic system with constant coefficiients. By a formal analysis, it derives problems of profiles in the expansion of the pulse like solution with respect to the length s, and obtains that the leading profile satisfies a nonlinear Schrodinger type system. The problems of profiles are solved, and the formal expansion is justified. It is observed that there is interaction between two phases starting at the third order profiles.展开更多
The magnetic phase diagram (x,T) of the SmMn2(Ge1-xSix)2 system has been studied by susceptibility and magnetization measurement. With increasing silicon concentration the temperature region of ferromagnetic ordering ...The magnetic phase diagram (x,T) of the SmMn2(Ge1-xSix)2 system has been studied by susceptibility and magnetization measurement. With increasing silicon concentration the temperature region of ferromagnetic ordering decreases on the phaae diagram.展开更多
The characteristics of water quality had significant effects on the oxidative degradation of O_3/H_2O_2 system.In this study,iron supported on activated carbon catalyst was prepared firstly,and then the treatment of l...The characteristics of water quality had significant effects on the oxidative degradation of O_3/H_2O_2 system.In this study,iron supported on activated carbon catalyst was prepared firstly,and then the treatment of landfill leachate by O_3/H_2O_2/catalyst system was analyzed,especially the roles of H_2O_2 in the oxidation of landfill leachate by O_3/H_2O_2 system.The results showed that at room temperature,when the dosage of the catalyst was 1.0g,the removal rate of COD from the landfill leachate reached 79.8% after 50 ml of the landfill leachate(pH=3)was oxidized by O_3(its flow rate was 5g/h)for 50 min.If 0.3ml of H_2O_2 was added to the landfill leachate,the removal rate of COD increased from 79.8%to 88.7%.It showed that the landfill leachate with the characteristics of complex composition and difficult biodegradation could be effectively degraded by the O_3/H_2O_2 system.展开更多
Eriochrome black T and Nitrosulfophenol S were advocated as the chemical models of carcinogenic non-aminoazo compounds. The main products of their oxidative cleavage in horseradish peroxidase/H2O2 system was identifie...Eriochrome black T and Nitrosulfophenol S were advocated as the chemical models of carcinogenic non-aminoazo compounds. The main products of their oxidative cleavage in horseradish peroxidase/H2O2 system was identified as the benezenediazonium ion, the ultimate carcinogens, which could bind to DNA. The reaction conditions were investigated preliminarily. Some inhibitors and inducers of the reaction were discovered.展开更多
The promoting effect of ethanol on the synthesis of N-（2-methylphenyl）hydroxylamine from o-nitrotoluene in Zn/H2O/CO2 system was observed.By adding appropriate amount of ethanol,the selectivity of N-（2-methylphenyl...The promoting effect of ethanol on the synthesis of N-（2-methylphenyl）hydroxylamine from o-nitrotoluene in Zn/H2O/CO2 system was observed.By adding appropriate amount of ethanol,the selectivity of N-（2-methylphenyl）hydroxylamine increased from 71%to 90%when the reduction was carried out at 25℃under normal pressure of CO2.展开更多
The pyrite-type FeO2 H-Fe O2 system has been experimentally confirmed to be stable in Earth's lowermost mantle but there is limited information about its physical properties at high pressures constraining our unde...The pyrite-type FeO2 H-Fe O2 system has been experimentally confirmed to be stable in Earth's lowermost mantle but there is limited information about its physical properties at high pressures constraining our understanding of its potential geophysical implications for the deep Earth.Here,static calculations demonstrate that the pyrite-type FeO2 H-FeO2 system has a high density and Poisson's ratio and ultra-low seismic velocities at conditions of Earth's lowermost mantle.It provides a plausible mechanism for the origin of ultra-low velocity zones at Earth's D″layer.The incorporation of hydrogen in the pyrite-type FeO2H-FeO2 system tends to decrease the S wave velocity(VS)but increase the bulk sound velocity(VΦ),and can potentially explain the observed anti-correlation of VS and VΦin the lowermost mantle.Additionally,FeO2 H exhibits nearly isotropic whereas Fe O2 is highly anisotropic,which may help understand some seismic anisotropies at the core-mantle boundary.展开更多
Raman peaks of various hydrates in the H20-NaCl-CaCl2 system have been previously identified, but a quantitative relationship between the Raman peaks and XNaCl （i.e.,NaCl/ （NaCl＋CaCl2）） has not been established, ...Raman peaks of various hydrates in the H20-NaCl-CaCl2 system have been previously identified, but a quantitative relationship between the Raman peaks and XNaCl （i.e.,NaCl/ （NaCl＋CaCl2）） has not been established, mainly due to the difficulty to freeze the solutions. This problem was solved by adding alumina powder to the solutions to facilitate nucleation of crystals. Cryogenic （-185℃） Raman spectroscopic studies of alumina-spiced solutions indicate that XNaCl is linearly correlated with the total peak area fraction of hydrohalite. Capsules of solutions made from silica capillary were prepared to simulate fluid inclusions. Most of these artificial fluid inclusions could not be totally frozen even at temperatures as low as -185℃, and the total peak area fraction of hydrohalite is not correlated linearly with XNaCI. However, the degree of deviation （△XNaCl） from the linear correlation established earlier is related to the amount of residual solution, which is reflected by the ratio （r） of the baseline ＂bump＂ area, resulting from the interstitial unfrozen brine near 3435 cm^-1, and the total hydrate peak area between 3350 and 3600 cm^-1. A linear correlation between △XNaCl and r is established to estimate XNaCl from cryogenic Raman spectroscopic analysis for fluid inclusions.展开更多
Fe3O4 magnetic nanoparticles(MNPs) were synthesised, characterised, and used as a peroxidase mimetic to accelerate levofloxacin sono-degradation in an ultrasound(US)/H2O2 system. The Fe3O4 MNPs were in nanometre scale...Fe3O4 magnetic nanoparticles(MNPs) were synthesised, characterised, and used as a peroxidase mimetic to accelerate levofloxacin sono-degradation in an ultrasound(US)/H2O2 system. The Fe3O4 MNPs were in nanometre scale with an average diameter of approximately 12 to 18 nm. The introduction of Fe3O4 MNPs increased levofloxacin sono-degradation in the US/H2O2 system. Experimental parameters, such as Fe3O4 MNP dose, initial solution p H, and H2O2 concentration, were investigated by a one-factor-at-a-time approach. The results showed that Fe3O4 MNPs enhanced levofloxacin removal in the p H range from 4.0 to 9.0. Levofloxacin removal ratio increased with Fe3O4 MNP dose up to 1.0 g·L-1and with H2O2 concentration until reaching the maximum. Moreover, three main intermediate compounds were identified by HPLC with electrospray ionisation tandem mass spectrometry, and a possible degradation pathway was proposed. This study suggests that combination of H2O2, Fe3O4 MNPs and US is a good way to improve the degradation efficiency of antibiotics.展开更多
CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning ...CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.展开更多
Previous cryogenic Raman spectroscopic analysis of H_2O-NaCl-CaCl_2 solutions has identified the Raman peaks of various hydrates of NaCl and CaCl_2,and established a linear relationship between Raman band intensity of...Previous cryogenic Raman spectroscopic analysis of H_2O-NaCl-CaCl_2 solutions has identified the Raman peaks of various hydrates of NaCl and CaCl_2,and established a linear relationship between Raman band intensity of the hydrates and the composition of the solution（NaCl/（NaCl＋CaCl_2） molar ratio,or X_（NaC1）） using synthetic fluids,which created the opportunity to quantitatively determine the solute composition of aqueous fluid inclusions with cryogenic Raman spectroscopy.This paper aims to test the feasibility of this newly established method with natural fluid inclusions.Twenty-five fluid inclusions in quartz from various occurrences which show a high degree of freezing during the cooling processes were carefully chosen for cryogenic Raman analysis.X_（Na）Cl was calculated using their spectra and an equation established in a previous study.These inclusions were then analyzed with the thermal decrepitation-SEM-EDS method.The X_（NaCl） values estimated from the two methods show a 1：1 correlation,indicating that the new,non-destructive cryogenic Raman spectroscopic analysis method can indeed be used for fluid inclusion compositional study.展开更多
GdF3 was synthesized with Gd2O3 and NH4HF2 under atmospheric pressure and vacuum. The effects of pressure,temperature,and reactant ratio on the reaction process were investigated. A new mechanism for the synthesis of ...GdF3 was synthesized with Gd2O3 and NH4HF2 under atmospheric pressure and vacuum. The effects of pressure,temperature,and reactant ratio on the reaction process were investigated. A new mechanism for the synthesis of GdF3 was proposed. Powdered Gd2O3 started to react with NH4HF2 at low temperature,and the products were GdNH4F4,NH4F,NH3,and H2O. GdNH4F4 decomposed to GdF3 and NH4F after further high-temperature treatment,accompanying the volatilization and decomposition of NH4F. The whole process could be divided into three steps： synthesis,decomposition,and deamination. The initial and final reaction temperatures decreased under vacuum condition. An optimized process for the preparation of GdF3 was obtained： synthesis under atmospheric pressure at low temperature and decomposition and deamination under vacuum at high temperature.展开更多
基金Project (2010CB631300) supported by the National Basic Research Program of China Project (50631020) supported by the National Natural Science Foundation of China+1 种基金 Project (NCET-07-0741) supported by the Program for New Century Excellent Talents in Universities, ChinaProject (20090101110050) supported by the University Doctoral Foundation of the Ministry of Education, China
文摘The formation conditions of MgB2 in 2LiBH4 ＋ MgH2 system during dehydrogenation were investigated and its mechanism was discussed. The results show that direct decomposition of LiBH4 is suppressed under relative higher initial dehydrogenation pressure of 4.0×10^5 Pa, wherein LiBH4 reacts with Mg to yield MgB2, and 9.16% （mass fraction） hydrogen is released within 9.6 h at 450 ℃. However, under relatively lower initial dehydrogenation pressure of 1.0×10^2 Pa, LiBH4 decomposes independently instead of reacting with Mg, resulting in no formation of MgB2, and 7.91% hydrogen is desorbed within 5.2 h at 450 ℃. It is found that the dehydrogenation of 2LiBH4 ＋ MgH2 system proceeds more completely and more hydrogen desorption amount can be obtained within a definite time by forming MgB2. Furthermore, it is proposed that the formation process of MgB2 includes incubation period and nucleus growth process. Experimental results show that the formation process of MgB2, especially the incubation period, is promoted by increasing initial dehydrogenation pressure at constant temperature, and the incubation period is also influenced greatly by dehydrogenation temperature.
基金Project(50974137)supported by the National Natural Science Foundation of China
文摘A novel method,bath smelting process,was developed to treat molybdenite concentrate aiming at the existing problems of traditional process.To understand the dissolving behavior of MoS2 in white matte,the binary phase diagram of Cu2S-Mo2S was measured by the cooling curve method.The result shows that this system is a simple binary eutectic with a eutectic temperature of（1117.0±3.0）℃ and a eutectic composition of（1.70±0.20）% MoS2 in mass fraction.When the MoS2 addition exceeds 4.48%,MoS2 and Cu2S can form the ternary compound containing CuMo2S3 or Cu2Mo6S8.In the temperature range of copper smelting,1200-1300℃,molybdenite can dissolve in the cuprous sulfide.At 1200℃,the solubility of molybdenite can reach 14.8%.
基金Project(2003AA332040) supported by the National High Technology Research and Development Program of China
文摘ZrO2-mullite nano-ceramics were fabricated by in-situ controlled crystallizing from SiO2-Al2O3-ZrO2 amorphous bulk. The thermal transformation sequences of the SiO2-Al2O3-ZrO2 amorphous bulk were investigated by X-ray diffraction, infrared spectrum, scanning electron microscope and differential scanning calorimetric. And the mechanical properties of the nano-ceramics were studied. The results show that the bulks are still in amorphous state at 900 ℃ and the t-ZrO2 forms at about 950 ℃ with a faint spinel-like phase which changes into mullite on further heating. ZrO2 and mullite become major phases at 1 100 ℃ and an amount of m-ZrO2 occur at the same time. The sample heated at 950 ℃ for 2 h and then at 1 100 ℃ for 1 h shows very dense and homogenous microstructure with ball-like grains in size of 20-50 nm. With the increase of crystallization temperature up to 1 350 ℃, the grains grow quickly and some grow into lath-shaped grains with major diameter of 5 μm. After two-step treatment the highest micro-hardness, flexural strength and fracture toughness of the samples are 13.72 GPa, 520 MPa and 5.13 MPa·m1/2, respectively.
基金the financial support of Tekes, Fimecc Oy (SIMP program),Finnish, Metals Producers FundCIMO (Centre for International Movement, an agency of Finnish Ministry of Education and Culture)
文摘ZnO-containing slags are common in pyrometallurgical processing of the base metals and steel.This caused the interest to the thermodynamics of the ZnO-SiO2 system.A complete literature survey,critical evaluation of the available experimental data and a thermodynamic optimization of the phase equilibria and thermodynamic properties of the system ZnO-SiO2 at 1.013×105 Pa are presented.The molten oxide was described as an associate solution.The properties of liquid were reassessed and enthalpy term of the Gibbs energy of solid Zn2SiO4 was re-fitted to be compatible with the new data in the willemite primary phase field.The thermodynamic data set agrees well with the recent experimental observations.It can be used for predicting,e.g.,the thermodynamic properties and the domains of the phase diagram,like critical point of the liquid miscibility gap,with a better accuracy than using the previous assessments.A set of optimized model parameters were obtained,reproducing the reliable thermodynamic and phase equilibrium data within their experimental errors from 298 K to liquidus temperatures,over the entire composition range.The created database can be used in a Gibbs energy minimization software to calculate the thermodynamic properties and the phase diagram sections of interest.
基金Item Sponsored by National Natural Science Foundation of China(51174054,51104041,51374065)
文摘The sintering characteristics at 1350℃ and leaching property at 80℃ of calcium aluminate clinkers in the CaO-Al2O3-SiO2 （C-A-S） system with different additions of FeO and Fe2O3 were investigated. FeO inhibits the conversion of β-Ca2SiO4 to γ-Ca2SiO4 and makes the clinker not pulverizable. FeO and Fe2O3 inhibit the formation of CaAl2O4, but promote the formation of Ca12Al14O33. The interplanar spacing at （2 1 1） crystal face of Ca12 Al14O33 in the clinker increases with the increase of FeO addition, which indicates that FeO forms solid solutions in Ca12Al14O33. The clinkers with Fe2O3 addition form a new phase Ca2Fe2O5, and the amount of Ca2Fe2o5 increases with the in crease of Fe2O3 addition. Both FeO and Fe2O3 do not affect the Al2O3 leaching rate of calcium aluminate clinker in sodium carbonate solution, but they increase the molar ratio of caustic Na2O to Al2O3 in the leached liquor.
文摘The phase diagram of the CsBr-CaBr2 system was re-determined by using differential thermal analysis and high ternperature and room ternperature X-ray diffraction analysis. It is concluded that there are three intermediate compounds in this system： a.congruently melting compound, CsCaBr3, with a melting point of 823℃ and two incongruently melting compounds, Cs2CaBr4 and Cs3Ca2Br7, whose peritectic points being 597℃ and 635℃, respectively. X-ray diffraction analysis indicated that compound CsCaBr3 is of slightly distorted perovskite structure.
文摘Revised phase diagram of the CeO2-ZrO2 system is optimized and the lattice stability parameters of CeO2 of various phases as well as solution parameters of phases (liquid, cubic, tetragonal and monoclinic) are simultaneously obtained by using the Kaufman and Nesor's model for describing the ceramic solutions and the Lukas program
文摘In this paper,the authors used the Mixed Coordination EXAFS Analysis Method recently published and IR to study the mixed coordination of Ge in glasses of Li_2O-ZnO-GeO_2 system,a new kind of syperionic conductor.The results show that when the content of ZnO is fixed,the ratio of [GeO_6] units is increased with the addition of Li_2O until the content of Li_2O is about 15%,and then decreased.The relationship between the ratio of [GeO_6]and the content of Li_2O is consistent with those between n,d of glass and Li_2O content, Therefore the germanium abnormalty can be explained as the change of coordination number.
文摘In order to study the relationship between thickness and residual stress in CaO-Al2O3-SiO2 glass-ceramics.The residual stress was measured in CaO-Al2O3-SiO2 system glass-ceramic with different thickness,and the formation mechanism and characterization of residual stress in CAS system Glass-ceramic were analyzed by the X-ray diffraction analysis.The experimental results show the compressive residual stress increass with thickness of glass-ceramic increasing.
基金the National Natural Science Foundation of China (No. 10131050)the Educational Ministry of China and the Shanghai Science and Technology Committee Foundation (No. 03QMH1407)
文摘This paper studies the asymptotic behavior of the diffractive interaction of pulses with two linear phases of length ε ≤ 1 in 2 × 2 semilinear strictly hyperbolic system with constant coefficiients. By a formal analysis, it derives problems of profiles in the expansion of the pulse like solution with respect to the length s, and obtains that the leading profile satisfies a nonlinear Schrodinger type system. The problems of profiles are solved, and the formal expansion is justified. It is observed that there is interaction between two phases starting at the third order profiles.
文摘The magnetic phase diagram (x,T) of the SmMn2(Ge1-xSix)2 system has been studied by susceptibility and magnetization measurement. With increasing silicon concentration the temperature region of ferromagnetic ordering decreases on the phaae diagram.
基金Supported by the Natural Science Foundation of Ningbo City,Zhejiang Province(2013A610188)the Self-designed Subject of "Modern Microorganism Technology and Application",the Priority Discipline of Zhejiang Province,China(ZS2013011)
文摘The characteristics of water quality had significant effects on the oxidative degradation of O_3/H_2O_2 system.In this study,iron supported on activated carbon catalyst was prepared firstly,and then the treatment of landfill leachate by O_3/H_2O_2/catalyst system was analyzed,especially the roles of H_2O_2 in the oxidation of landfill leachate by O_3/H_2O_2 system.The results showed that at room temperature,when the dosage of the catalyst was 1.0g,the removal rate of COD from the landfill leachate reached 79.8% after 50 ml of the landfill leachate(pH=3)was oxidized by O_3(its flow rate was 5g/h)for 50 min.If 0.3ml of H_2O_2 was added to the landfill leachate,the removal rate of COD increased from 79.8%to 88.7%.It showed that the landfill leachate with the characteristics of complex composition and difficult biodegradation could be effectively degraded by the O_3/H_2O_2 system.
文摘Eriochrome black T and Nitrosulfophenol S were advocated as the chemical models of carcinogenic non-aminoazo compounds. The main products of their oxidative cleavage in horseradish peroxidase/H2O2 system was identified as the benezenediazonium ion, the ultimate carcinogens, which could bind to DNA. The reaction conditions were investigated preliminarily. Some inhibitors and inducers of the reaction were discovered.
基金supported by the Doctoral Fund of Ministry of Education of China(No.20070141046)the Fund of Education Department of Liaoning Province(No.[2006]124)
文摘The promoting effect of ethanol on the synthesis of N-（2-methylphenyl）hydroxylamine from o-nitrotoluene in Zn/H2O/CO2 system was observed.By adding appropriate amount of ethanol,the selectivity of N-（2-methylphenyl）hydroxylamine increased from 71%to 90%when the reduction was carried out at 25℃under normal pressure of CO2.
基金financial support from the National Natural Science Foundation of China (Nos. 41473056 and 41472037)
文摘The pyrite-type FeO2 H-Fe O2 system has been experimentally confirmed to be stable in Earth's lowermost mantle but there is limited information about its physical properties at high pressures constraining our understanding of its potential geophysical implications for the deep Earth.Here,static calculations demonstrate that the pyrite-type FeO2 H-FeO2 system has a high density and Poisson's ratio and ultra-low seismic velocities at conditions of Earth's lowermost mantle.It provides a plausible mechanism for the origin of ultra-low velocity zones at Earth's D″layer.The incorporation of hydrogen in the pyrite-type FeO2H-FeO2 system tends to decrease the S wave velocity(VS)but increase the bulk sound velocity(VΦ),and can potentially explain the observed anti-correlation of VS and VΦin the lowermost mantle.Additionally,FeO2 H exhibits nearly isotropic whereas Fe O2 is highly anisotropic,which may help understand some seismic anisotropies at the core-mantle boundary.
基金supported by an NSERC-Discovery grant(to Chi)in part by the Knowledge Innovation Program of Chinese Academy of Sciences(SIDSSE201302)
文摘Raman peaks of various hydrates in the H20-NaCl-CaCl2 system have been previously identified, but a quantitative relationship between the Raman peaks and XNaCl （i.e.,NaCl/ （NaCl＋CaCl2）） has not been established, mainly due to the difficulty to freeze the solutions. This problem was solved by adding alumina powder to the solutions to facilitate nucleation of crystals. Cryogenic （-185℃） Raman spectroscopic studies of alumina-spiced solutions indicate that XNaCl is linearly correlated with the total peak area fraction of hydrohalite. Capsules of solutions made from silica capillary were prepared to simulate fluid inclusions. Most of these artificial fluid inclusions could not be totally frozen even at temperatures as low as -185℃, and the total peak area fraction of hydrohalite is not correlated linearly with XNaCI. However, the degree of deviation （△XNaCl） from the linear correlation established earlier is related to the amount of residual solution, which is reflected by the ratio （r） of the baseline ＂bump＂ area, resulting from the interstitial unfrozen brine near 3435 cm^-1, and the total hydrate peak area between 3350 and 3600 cm^-1. A linear correlation between △XNaCl and r is established to estimate XNaCl from cryogenic Raman spectroscopic analysis for fluid inclusions.
基金Supported by the National Natural Science Foundation of China(51009115)Shaanxi Provincial Department of Education Key Laboratory Project(13JS067)+2 种基金the Hall of Shaanxi Province Science and Technology(2013JK0881)the Research Plan Project of Water Resources Department of Shaanxi Province(2013slkj-07)the Innovation of Science and Technology Fund of Xi'an University of Technology(211302)
文摘Fe3O4 magnetic nanoparticles(MNPs) were synthesised, characterised, and used as a peroxidase mimetic to accelerate levofloxacin sono-degradation in an ultrasound(US)/H2O2 system. The Fe3O4 MNPs were in nanometre scale with an average diameter of approximately 12 to 18 nm. The introduction of Fe3O4 MNPs increased levofloxacin sono-degradation in the US/H2O2 system. Experimental parameters, such as Fe3O4 MNP dose, initial solution p H, and H2O2 concentration, were investigated by a one-factor-at-a-time approach. The results showed that Fe3O4 MNPs enhanced levofloxacin removal in the p H range from 4.0 to 9.0. Levofloxacin removal ratio increased with Fe3O4 MNP dose up to 1.0 g·L-1and with H2O2 concentration until reaching the maximum. Moreover, three main intermediate compounds were identified by HPLC with electrospray ionisation tandem mass spectrometry, and a possible degradation pathway was proposed. This study suggests that combination of H2O2, Fe3O4 MNPs and US is a good way to improve the degradation efficiency of antibiotics.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject(BE2010194) supported by Science&Technology Pillar Program of Jiangsu Province, China+1 种基金Project(KF201103) supported by the State Key Laboratory of New Ceramic and Fine Processing, Tsinghua University, ChinaProject supported by the Priority Academic Development of Jiangsu Higher Education Institutions, China
文摘CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.
文摘Previous cryogenic Raman spectroscopic analysis of H_2O-NaCl-CaCl_2 solutions has identified the Raman peaks of various hydrates of NaCl and CaCl_2,and established a linear relationship between Raman band intensity of the hydrates and the composition of the solution（NaCl/（NaCl＋CaCl_2） molar ratio,or X_（NaC1）） using synthetic fluids,which created the opportunity to quantitatively determine the solute composition of aqueous fluid inclusions with cryogenic Raman spectroscopy.This paper aims to test the feasibility of this newly established method with natural fluid inclusions.Twenty-five fluid inclusions in quartz from various occurrences which show a high degree of freezing during the cooling processes were carefully chosen for cryogenic Raman analysis.X_（Na）Cl was calculated using their spectra and an equation established in a previous study.These inclusions were then analyzed with the thermal decrepitation-SEM-EDS method.The X_（NaCl） values estimated from the two methods show a 1：1 correlation,indicating that the new,non-destructive cryogenic Raman spectroscopic analysis method can indeed be used for fluid inclusion compositional study.
文摘GdF3 was synthesized with Gd2O3 and NH4HF2 under atmospheric pressure and vacuum. The effects of pressure,temperature,and reactant ratio on the reaction process were investigated. A new mechanism for the synthesis of GdF3 was proposed. Powdered Gd2O3 started to react with NH4HF2 at low temperature,and the products were GdNH4F4,NH4F,NH3,and H2O. GdNH4F4 decomposed to GdF3 and NH4F after further high-temperature treatment,accompanying the volatilization and decomposition of NH4F. The whole process could be divided into three steps： synthesis,decomposition,and deamination. The initial and final reaction temperatures decreased under vacuum condition. An optimized process for the preparation of GdF3 was obtained： synthesis under atmospheric pressure at low temperature and decomposition and deamination under vacuum at high temperature.