V-Pd/γ-Al2O3-TiO2 catalysts with different vanadium contents were prepared by a combined sol-gel and impregnation method. X-ray diffraction （XRD）, N2 adsorption-desorption （BET）, X-ray photoelectron spectroscopy ...V-Pd/γ-Al2O3-TiO2 catalysts with different vanadium contents were prepared by a combined sol-gel and impregnation method. X-ray diffraction （XRD）, N2 adsorption-desorption （BET）, X-ray photoelectron spectroscopy （XPS） and catalytic removal of ethanol, acetaldehyde and nitrogen oxides at low temperature （〈300 ？C） were used to assess the properties of the catalysts. The results showed that the sample with 1wt% vanadium exhibited an excellent catalytic performance for simultaneous removal of ethanol, acetaldehyde and nitrogen oxides. The conversions of ethanol, acetaldehyde and nitrogen oxides at 250 ？C were 100%, 74.4% and 98.7%, respectively. V-Pd/γ-Al2O3-TiO2 catalyst with 1 wt% vanadium showed the largest surface area and higher dispersion of vanadium oxide on the catalyst surface, and possessed a larger mole fraction of V4＋ species and unique PdO species on the surface, which can be attributed to the strong synergistic effect among palladium, vanadium and the carriers. The higher activity of V-Pd/γ-Al2O3-TiO2 catalyst is related to the V4＋ and Pd2＋ species on the surface, which might be favorable for the formation of active sites.展开更多
基金supported by the National Natural Science Foundation of China (No. 21073131)the Shanxi Natural Science Foundation(No. 2009011011-3)
文摘V-Pd/γ-Al2O3-TiO2 catalysts with different vanadium contents were prepared by a combined sol-gel and impregnation method. X-ray diffraction （XRD）, N2 adsorption-desorption （BET）, X-ray photoelectron spectroscopy （XPS） and catalytic removal of ethanol, acetaldehyde and nitrogen oxides at low temperature （〈300 ？C） were used to assess the properties of the catalysts. The results showed that the sample with 1wt% vanadium exhibited an excellent catalytic performance for simultaneous removal of ethanol, acetaldehyde and nitrogen oxides. The conversions of ethanol, acetaldehyde and nitrogen oxides at 250 ？C were 100%, 74.4% and 98.7%, respectively. V-Pd/γ-Al2O3-TiO2 catalyst with 1 wt% vanadium showed the largest surface area and higher dispersion of vanadium oxide on the catalyst surface, and possessed a larger mole fraction of V4＋ species and unique PdO species on the surface, which can be attributed to the strong synergistic effect among palladium, vanadium and the carriers. The higher activity of V-Pd/γ-Al2O3-TiO2 catalyst is related to the V4＋ and Pd2＋ species on the surface, which might be favorable for the formation of active sites.