Quantum dot(QD)-based fluorescent inks offer high potential due to their tunable emission and high quantum yield,but their practical application suffers from poor environmental stability,aggregation,and challenges in ...Quantum dot(QD)-based fluorescent inks offer high potential due to their tunable emission and high quantum yield,but their practical application suffers from poor environmental stability,aggregation,and challenges in scalable flexible fabrication.In this study,a high-stability fluorescent ink was developed by incorporating QDs into a polydimethylsiloxane(PDMS)colloidal matrix.High-performance patterned films were then obtained via systematic optimization of screen-printing parameters,with film quality governed by substrate type(131μm PDMS),QD concentration(1.5 mg/mL),and screen mesh count(420 mesh).The optimized films exhibit outstanding environmental and photostability,retaining 75.6% of their fluorescence intensity after immersion in deionized water and 63.8% in 75%ethanol at 25℃ for 100 minutes.Under UV irradiation(365 nm,9 W,100 min),fluorescence intensity decreases by less than 20%.Utilizing their daylight transparency and UV-excitable luminescence,various patterns including QR codes and Code 93 standard barcodes were fabricated via screen printing with high pattern fidelity and machine readability.This study presents a scalable and reliable strategy for the fabrication of flexible,high-stability fluorescent films,supporting their integration into next-generation optoelectronic devices,advanced displays,and secure anti-counterfeiting.展开更多
文摘Quantum dot(QD)-based fluorescent inks offer high potential due to their tunable emission and high quantum yield,but their practical application suffers from poor environmental stability,aggregation,and challenges in scalable flexible fabrication.In this study,a high-stability fluorescent ink was developed by incorporating QDs into a polydimethylsiloxane(PDMS)colloidal matrix.High-performance patterned films were then obtained via systematic optimization of screen-printing parameters,with film quality governed by substrate type(131μm PDMS),QD concentration(1.5 mg/mL),and screen mesh count(420 mesh).The optimized films exhibit outstanding environmental and photostability,retaining 75.6% of their fluorescence intensity after immersion in deionized water and 63.8% in 75%ethanol at 25℃ for 100 minutes.Under UV irradiation(365 nm,9 W,100 min),fluorescence intensity decreases by less than 20%.Utilizing their daylight transparency and UV-excitable luminescence,various patterns including QR codes and Code 93 standard barcodes were fabricated via screen printing with high pattern fidelity and machine readability.This study presents a scalable and reliable strategy for the fabrication of flexible,high-stability fluorescent films,supporting their integration into next-generation optoelectronic devices,advanced displays,and secure anti-counterfeiting.