With the miniaturization and high-frequency evolution of antennas in 5G/6G communications,aerospace,and transportation,polymer composite papers integrating superior wave-transparent performance and thermal conductivit...With the miniaturization and high-frequency evolution of antennas in 5G/6G communications,aerospace,and transportation,polymer composite papers integrating superior wave-transparent performance and thermal conductivity for radar antenna systems are urgently needed.Herein,a down-top strategy was employed to synthesize poly(p-phenylene benzobisoxazole)precursor nanofibers(prePNF).The prePNF was then uniformly mixed with fluorinated graphene(FG)to fabricate FG/PNF composite papers through consecutively suction filtration,hot-pressing,and thermal annealing.The hydroxyl and amino groups in prePNF enhanced the stability of FG/prePNF dispersion,while the increasedπ-πinteractions between PNF and FG after annealing improved their compatibility.The preparation time and cost of PNF paper was significantly reduced when applying this strategy,which enabled its large-scale production.Furthermore,the prepared FG/PNF composite papers exhibited excellent wave-transparent performance and thermal conductivity.When the mass fraction of FG was 40 wt%,the FG/PNF composite paper prepared via the down-top strategy achieved the wave-transparent coefficient(|T|2)of 96.3%under 10 GHz,in-plane thermal conductivity(λ_(∥))of 7.13 W m^(−1)K^(−1),and through-plane thermal conductivity(λ_(⊥))of 0.67 W m^(−1)K^(−1),outperforming FG/PNF composite paper prepared by the top-down strategy(|T|2=95.9%,λ_(∥)=5.52 W m^(−1)K^(−1),λ_(⊥)=0.52 W m^(−1)K^(−1))and pure PNF paper(|T|2=94.7%,λ_(∥)=3.04 W m^(−1)K^(−1),λ_(⊥)=0.24 W m^(−1)K^(−1)).Meanwhile,FG/PNF composite paper(with 40 wt%FG)through the down-top strategy also demonstrated outstanding mechanical properties with tensile strength and toughness reaching 197.4 MPa and 11.6 MJ m^(−3),respectively.展开更多
基金the support from the National Natural Science Foundation of China(52473083,52373089,52403085)Natural Science Basic Research Program of Shaanxi(2024JC-TBZC-04)+2 种基金the Innovation Capability Support Program of Shaanxi(2024RS-CXTD-57)Natural Science Basic Research Plan in Shaanxi Province of China(2024JC-YBMS-279)Natural Science Foundation of Chongqing,China(2023NSCQMSX2547)
文摘With the miniaturization and high-frequency evolution of antennas in 5G/6G communications,aerospace,and transportation,polymer composite papers integrating superior wave-transparent performance and thermal conductivity for radar antenna systems are urgently needed.Herein,a down-top strategy was employed to synthesize poly(p-phenylene benzobisoxazole)precursor nanofibers(prePNF).The prePNF was then uniformly mixed with fluorinated graphene(FG)to fabricate FG/PNF composite papers through consecutively suction filtration,hot-pressing,and thermal annealing.The hydroxyl and amino groups in prePNF enhanced the stability of FG/prePNF dispersion,while the increasedπ-πinteractions between PNF and FG after annealing improved their compatibility.The preparation time and cost of PNF paper was significantly reduced when applying this strategy,which enabled its large-scale production.Furthermore,the prepared FG/PNF composite papers exhibited excellent wave-transparent performance and thermal conductivity.When the mass fraction of FG was 40 wt%,the FG/PNF composite paper prepared via the down-top strategy achieved the wave-transparent coefficient(|T|2)of 96.3%under 10 GHz,in-plane thermal conductivity(λ_(∥))of 7.13 W m^(−1)K^(−1),and through-plane thermal conductivity(λ_(⊥))of 0.67 W m^(−1)K^(−1),outperforming FG/PNF composite paper prepared by the top-down strategy(|T|2=95.9%,λ_(∥)=5.52 W m^(−1)K^(−1),λ_(⊥)=0.52 W m^(−1)K^(−1))and pure PNF paper(|T|2=94.7%,λ_(∥)=3.04 W m^(−1)K^(−1),λ_(⊥)=0.24 W m^(−1)K^(−1)).Meanwhile,FG/PNF composite paper(with 40 wt%FG)through the down-top strategy also demonstrated outstanding mechanical properties with tensile strength and toughness reaching 197.4 MPa and 11.6 MJ m^(−3),respectively.
