A dynamic measuring apparatus was developed to investigate the infiltration process of liquid metal into the fibrous preform. 10% （volume fraction） chopped carbon fiber preforms were infiltrated with magnesium alloy...A dynamic measuring apparatus was developed to investigate the infiltration process of liquid metal into the fibrous preform. 10% （volume fraction） chopped carbon fiber preforms were infiltrated with magnesium alloy under different infiltration pressures. The threshold pressure and flow behavior of liquid metal infiltrating into the preforms were calculated and measured. The microstructure of obtained Ct4Mg composites was observed. The results indicate that the measured threshold pressure for infiltration was 0.048 MPa, which was larger than the calculated value. The infiltration rate increased with the increase of infiltration pressure, but the increase amplitude decreased gradually. The tiny pores in the composites could be eliminated by increasing the infiltration pressure. When the infiltration pressure rose to 0.6 MPa, high quality C1/Mg composite was obtained.展开更多
基金National Natural Science Foundation of China(51134003)National Science and Technology Support Standard(2012BAC02B05)Shaanxi Science and Technology Co-ordination(2012K72B03-01-04)
基金Projects(51221001,51275417)supported by the National Natural Science Foundation of ChinaProject(2013AA8011004B)supported by National High Technology Research and Development Program of ChinaProject(CX201011)supported by the Doctorate Foundation of Northwestern Polytechnical University,China
文摘A dynamic measuring apparatus was developed to investigate the infiltration process of liquid metal into the fibrous preform. 10% （volume fraction） chopped carbon fiber preforms were infiltrated with magnesium alloy under different infiltration pressures. The threshold pressure and flow behavior of liquid metal infiltrating into the preforms were calculated and measured. The microstructure of obtained Ct4Mg composites was observed. The results indicate that the measured threshold pressure for infiltration was 0.048 MPa, which was larger than the calculated value. The infiltration rate increased with the increase of infiltration pressure, but the increase amplitude decreased gradually. The tiny pores in the composites could be eliminated by increasing the infiltration pressure. When the infiltration pressure rose to 0.6 MPa, high quality C1/Mg composite was obtained.