A new technique was proposed to enhance the adhesive strength of ultrahigh molecular weight polyethylene （UHMWPE） fibers. Polar polymer was implanted into UHMWE gel fibers during extracting process and can then be t...A new technique was proposed to enhance the adhesive strength of ultrahigh molecular weight polyethylene （UHMWPE） fibers. Polar polymer was implanted into UHMWE gel fibers during extracting process and can then be trapped on the surface of the fibers after subsequent ultra-drawing. The physical and chemical changes in the fiber structure were examined with scanning electron microscopy （SEM） and Fourier transform infrared （FTIR） spectroscopy. The mechanical and interfacial adhesion properties of UHMWPE fibers were investigated with tensile testing. The results showed that there were polar groups on the smface of pretreated UHMWPE fiber. The interracial shear strength of UHMWPE fibers with epoxy resin was greatly improved without sacrificing the excellent mechanical p^perties of fibers. After pretreated with ethylene/vinyl acetate copolymer （EVA）, the shear strength of the interface between fiber and epoxy resin increased from 1.06 to 2.49 MPa, while the integrated mechanical properties d the pretreated UHMWPE fibers were still optimal.展开更多
文摘基于低能耗、少污染的要求,比较了助剂(如苏红退浆酶2000L、硫酸、氢氧化钠和双氧水)和退浆工艺步骤对退浆效果的影响,并优化了退浆工艺.结果表明:苏红退浆酶2000L对淀粉及其变性浆料具有良好的去除作用,其最佳实施流程为:预处理→酶处理→热水洗,最佳处理条件:酶0.8 g/L,JFC 0.5 g/L,pH为中性,浴比1∶20,70℃,45 min.
文摘A new technique was proposed to enhance the adhesive strength of ultrahigh molecular weight polyethylene （UHMWPE） fibers. Polar polymer was implanted into UHMWE gel fibers during extracting process and can then be trapped on the surface of the fibers after subsequent ultra-drawing. The physical and chemical changes in the fiber structure were examined with scanning electron microscopy （SEM） and Fourier transform infrared （FTIR） spectroscopy. The mechanical and interfacial adhesion properties of UHMWPE fibers were investigated with tensile testing. The results showed that there were polar groups on the smface of pretreated UHMWPE fiber. The interracial shear strength of UHMWPE fibers with epoxy resin was greatly improved without sacrificing the excellent mechanical p^perties of fibers. After pretreated with ethylene/vinyl acetate copolymer （EVA）, the shear strength of the interface between fiber and epoxy resin increased from 1.06 to 2.49 MPa, while the integrated mechanical properties d the pretreated UHMWPE fibers were still optimal.