In order to clean production of chromium compounds, it is a critical process to remove aluminates and utilize aluminum compounds from artificial chromate alkali solutions. The effects of Na2 Cr O4 on the neutralizatio...In order to clean production of chromium compounds, it is a critical process to remove aluminates and utilize aluminum compounds from artificial chromate alkali solutions. The effects of Na2 Cr O4 on the neutralization curve, Al（OH）3 precipitation efficiency and induction period of bayerite were investigated. The results indicate that the neutralization curve of the artificial chromate alkali solutions shows three distinct regions and its induction period is longer than that of pure sodium aluminate solutions at the same aluminum concentration. And the decreased temperature and volume fraction of CO2 enhance the particle size of bayerite β-Al（OH）3. Bayerite composed of agglomerates of rods and cone frustums was obtained from alkali metal chromate solutions with 28.5% CO2（volume fraction） at temperatures ranging from 50 °C to 70 °C. Coarse bayerite with particle size（d50） from 24.2 μm to 29.3 μm extremely has few impurities, which is suitable for comprehensive utilization.展开更多
基金Project(51125018)supported by the National Science Found for Distinguished Young Scholars of ChinaProject(2011BAC06B07)supported by the National Key Technologies R&D Program of China+2 种基金Project(2011AA060704)supported by the National Hi-tech Research and Development Program of ChinaProjects(51204153,21106167)supported by the National Natural Science Foundation of ChinaProjects(2012M510552,2013T60175)supported by Financial Grant from the China Postdoctoral Science Foundation
文摘In order to clean production of chromium compounds, it is a critical process to remove aluminates and utilize aluminum compounds from artificial chromate alkali solutions. The effects of Na2 Cr O4 on the neutralization curve, Al（OH）3 precipitation efficiency and induction period of bayerite were investigated. The results indicate that the neutralization curve of the artificial chromate alkali solutions shows three distinct regions and its induction period is longer than that of pure sodium aluminate solutions at the same aluminum concentration. And the decreased temperature and volume fraction of CO2 enhance the particle size of bayerite β-Al（OH）3. Bayerite composed of agglomerates of rods and cone frustums was obtained from alkali metal chromate solutions with 28.5% CO2（volume fraction） at temperatures ranging from 50 °C to 70 °C. Coarse bayerite with particle size（d50） from 24.2 μm to 29.3 μm extremely has few impurities, which is suitable for comprehensive utilization.