MnBi compound is fabricated under a magnetic field of 1 T, and the c-axis of hexagonal MnBi crystal is aligned parallel to the magnetic field direction. The saturation magnetization Ms decreases with the increase of t...MnBi compound is fabricated under a magnetic field of 1 T, and the c-axis of hexagonal MnBi crystal is aligned parallel to the magnetic field direction. The saturation magnetization Ms decreases with the increase of temperature. At temperatures below 20OK, the coercive field Hc is about 150Oe, while the coercive field Hc increases with temperature above 200K. From 200K to 300K, the remnant magnetization Mr and the Mr/Ms increase with the temperature. Below 200K, Mr and Mr/M8 reach roughly a constant value. However, there is an abnormal increase at 100 K in He, Mr and Mr/Ms, which comes from a spin-reorientation in MnBi. Magnetization results show the spin-reorientation for MnBi at about 91 K due to the variations of the anisotropy constants.展开更多
Textured Bi and MnBi/Bi thin films are prepared by the pulsed laser deposition method. The highly c-axis textured MnBi films are obtained by annealing the bilayer consisting of textured Bi and Mn films. The eoerciviti...Textured Bi and MnBi/Bi thin films are prepared by the pulsed laser deposition method. The highly c-axis textured MnBi films are obtained by annealing the bilayer consisting of textured Bi and Mn films. The eoercivities of the MnBi/Bi film are 1.5 T and 2.35 T at room temperature and at 373K, respectively, showing a positive temperature coefficient. Microstructural investigations show that the textured MnBi film results from the orientated growth induced by the textured Bi under-layer.展开更多
基金Supported by the Shanghai Rising-Star Program under Grant Nos 07QA14026 and 09QA1406300, the National Natural Science Foundation of China under Grant Nos 10804072 and 50703029, the Science and Technology Commission of Shanghai Municipality under Grant Nos 0952nm02700, 2009025, 08JC1410400 and 09dz1202500, and the Innovation Program of Shanghai Municipal Education Commission under Grant No 11ZZ168.
文摘MnBi compound is fabricated under a magnetic field of 1 T, and the c-axis of hexagonal MnBi crystal is aligned parallel to the magnetic field direction. The saturation magnetization Ms decreases with the increase of temperature. At temperatures below 20OK, the coercive field Hc is about 150Oe, while the coercive field Hc increases with temperature above 200K. From 200K to 300K, the remnant magnetization Mr and the Mr/Ms increase with the temperature. Below 200K, Mr and Mr/M8 reach roughly a constant value. However, there is an abnormal increase at 100 K in He, Mr and Mr/Ms, which comes from a spin-reorientation in MnBi. Magnetization results show the spin-reorientation for MnBi at about 91 K due to the variations of the anisotropy constants.
基金Supported by the National Natural Science Foundation of China under Grant Nos 51171001,51371009 and 50971003the Foundation of Key Laboratory of Neutron Physics of CAEP under Grant No 2014BB02
文摘Textured Bi and MnBi/Bi thin films are prepared by the pulsed laser deposition method. The highly c-axis textured MnBi films are obtained by annealing the bilayer consisting of textured Bi and Mn films. The eoercivities of the MnBi/Bi film are 1.5 T and 2.35 T at room temperature and at 373K, respectively, showing a positive temperature coefficient. Microstructural investigations show that the textured MnBi film results from the orientated growth induced by the textured Bi under-layer.