To clarify the high temperature flow stress behavior and microstructures evolution of a V-5Cr-5Ti （mass fraction, %） alloy, the isothermal hot compression tests were conducted in the temperature range of 1423-1573 K...To clarify the high temperature flow stress behavior and microstructures evolution of a V-5Cr-5Ti （mass fraction, %） alloy, the isothermal hot compression tests were conducted in the temperature range of 1423-1573 K with strain rates of 0.01, 0.1, and 1 s-1. The results show that the measured flow stress should be revised by friction and the calculated values of friction coefficient m are in the range of 0.45-0.56. Arrhenius-type constitutive equation was developed by regression analysis. The comparison between the experimental and predicted flow stress shows that the R~ and the average absolute relative error （AARE） are 0.948 and 5.44%, respectively. The measured apparent activation energy Qa is in the range of 540-890 kJ/mol. Both dis-continuous dynamic recrystallization （DDRX） and continuous dynamic recrystallization （CDRX） mechanisms are observed in the deformed alloy, but dynamic recovery （DRV） is the dominant softening mechanism up to a true strain of 1.5.展开更多
基金Project(11105127) supported by the National Natural Science Foundation of China
文摘To clarify the high temperature flow stress behavior and microstructures evolution of a V-5Cr-5Ti （mass fraction, %） alloy, the isothermal hot compression tests were conducted in the temperature range of 1423-1573 K with strain rates of 0.01, 0.1, and 1 s-1. The results show that the measured flow stress should be revised by friction and the calculated values of friction coefficient m are in the range of 0.45-0.56. Arrhenius-type constitutive equation was developed by regression analysis. The comparison between the experimental and predicted flow stress shows that the R~ and the average absolute relative error （AARE） are 0.948 and 5.44%, respectively. The measured apparent activation energy Qa is in the range of 540-890 kJ/mol. Both dis-continuous dynamic recrystallization （DDRX） and continuous dynamic recrystallization （CDRX） mechanisms are observed in the deformed alloy, but dynamic recovery （DRV） is the dominant softening mechanism up to a true strain of 1.5.