为分析影响热变形钕铁硼磁体矫顽力的因素,制备了3种不含Dy,Ga热变形磁体,磁体成分分别为Nd_(10.5)Pr_(2.5)Fe_(80)Nb_(1)B_(6),Nd_(11.5)Fe_(81.8)B_(6.0)Nb_(0.7)+6%Nd_(67)Cu_(33)及Nd_(10.5)Pr_(2.5)Fe_(80)Nb_(1)B_(6)+6%Nd_(67)Cu...为分析影响热变形钕铁硼磁体矫顽力的因素,制备了3种不含Dy,Ga热变形磁体,磁体成分分别为Nd_(10.5)Pr_(2.5)Fe_(80)Nb_(1)B_(6),Nd_(11.5)Fe_(81.8)B_(6.0)Nb_(0.7)+6%Nd_(67)Cu_(33)及Nd_(10.5)Pr_(2.5)Fe_(80)Nb_(1)B_(6)+6%Nd_(67)Cu_(33),由Nd-Fe-B三元相图计算了富稀土晶界相体积分数v,实验结果表明:v对富稀土钕铁硼热变形磁体矫顽力的贡献为98.10 k A·m^(-1)·%^(-1),比v对贫稀土钕铁硼混粉热变形磁体矫顽力的贡献低36%~44%;由v=1-a^(3)/[(a+h)^(2)(a+3h)]计算了富稀土晶界相厚度h,发现在v相同条件下热变形钕铁硼磁体晶界相厚度h随主相片状晶等效平均晶粒尺寸a的减小虽然减薄,但a占主导作用导致磁体的矫顽力仍然提高;在片状晶等效平均晶粒尺寸a相近的条件下,热变形钕铁硼磁体晶界相厚度随晶界相体积分数v的增加而变厚,主相片状晶的磁绝缘效果提高导致热变形磁体的矫顽力上升。展开更多
文摘为分析影响热变形钕铁硼磁体矫顽力的因素,制备了3种不含Dy,Ga热变形磁体,磁体成分分别为Nd_(10.5)Pr_(2.5)Fe_(80)Nb_(1)B_(6),Nd_(11.5)Fe_(81.8)B_(6.0)Nb_(0.7)+6%Nd_(67)Cu_(33)及Nd_(10.5)Pr_(2.5)Fe_(80)Nb_(1)B_(6)+6%Nd_(67)Cu_(33),由Nd-Fe-B三元相图计算了富稀土晶界相体积分数v,实验结果表明:v对富稀土钕铁硼热变形磁体矫顽力的贡献为98.10 k A·m^(-1)·%^(-1),比v对贫稀土钕铁硼混粉热变形磁体矫顽力的贡献低36%~44%;由v=1-a^(3)/[(a+h)^(2)(a+3h)]计算了富稀土晶界相厚度h,发现在v相同条件下热变形钕铁硼磁体晶界相厚度h随主相片状晶等效平均晶粒尺寸a的减小虽然减薄,但a占主导作用导致磁体的矫顽力仍然提高;在片状晶等效平均晶粒尺寸a相近的条件下,热变形钕铁硼磁体晶界相厚度随晶界相体积分数v的增加而变厚,主相片状晶的磁绝缘效果提高导致热变形磁体的矫顽力上升。