This work focuses the effect of alkali-NaOH solution on the nature of synthesized zeolite from 2：1 Tunisian clays. This study was achieved using correlation between results obtained from X-ray diffraction （XRD） and...This work focuses the effect of alkali-NaOH solution on the nature of synthesized zeolite from 2：1 Tunisian clays. This study was achieved using correlation between results obtained from X-ray diffraction （XRD） and MAS-NMR analysis. Preliminary treatment was adopted to prepare the starting sample that is placed in contact with NaOH solution at variable concentration. A specific hydrothermal reactor, allowing the control ofpH 〉 9, temperature and a continuous stirring of the sample in the NaOH solution; was used to achieve these syntheses. The obtained results showed that, for concentration value ~IN, the final complex presented characteristic XRD and MAS-NMR line of zeolite P. For 3N solution concentration we obtained zeolite HS. All synthesize process are controlled by XRD and MAS-NMR investigation.展开更多
文摘This work focuses the effect of alkali-NaOH solution on the nature of synthesized zeolite from 2：1 Tunisian clays. This study was achieved using correlation between results obtained from X-ray diffraction （XRD） and MAS-NMR analysis. Preliminary treatment was adopted to prepare the starting sample that is placed in contact with NaOH solution at variable concentration. A specific hydrothermal reactor, allowing the control ofpH 〉 9, temperature and a continuous stirring of the sample in the NaOH solution; was used to achieve these syntheses. The obtained results showed that, for concentration value ~IN, the final complex presented characteristic XRD and MAS-NMR line of zeolite P. For 3N solution concentration we obtained zeolite HS. All synthesize process are controlled by XRD and MAS-NMR investigation.