The synthesis of sodium ferrite and its desulfurization performance in S2 -bearing sodium aluminate solutions were investigated. The thermodynamic analysis shows that the lowest temperature is about 810 K for synthesi...The synthesis of sodium ferrite and its desulfurization performance in S2 -bearing sodium aluminate solutions were investigated. The thermodynamic analysis shows that the lowest temperature is about 810 K for synthesizing sodium ferrite by roasting the mixture of ferric oxide and sodium carbonate. The results indicate that the formation process of sodium ferrite can be completed at 1173 K for 60 min, meanwhile raising temperature and reducing NazCO3 particle size are beneficial to accelerating the formation of sodium ferrite. Sodium ferrite is an efficient desulfurizer to remove the S2- in aluminate solution, and the desulfurization rate can reach approximately 70% at 373 K for 60 min with the molar ratio of iron to sulfur of 1：1-1.5：1. Furthermore, the desulfurization is achieved by NaFeS2·2H2O precipitation through the reaction of Fe（OH）4 and S^2- in aluminate solution, and the desulfurization efficiency relies on the Fe（OH）4^- generated by dissolving sodium ferrite.展开更多
基金Project(51374239)supported by the National Natural Science Foundation of China
文摘The synthesis of sodium ferrite and its desulfurization performance in S2 -bearing sodium aluminate solutions were investigated. The thermodynamic analysis shows that the lowest temperature is about 810 K for synthesizing sodium ferrite by roasting the mixture of ferric oxide and sodium carbonate. The results indicate that the formation process of sodium ferrite can be completed at 1173 K for 60 min, meanwhile raising temperature and reducing NazCO3 particle size are beneficial to accelerating the formation of sodium ferrite. Sodium ferrite is an efficient desulfurizer to remove the S2- in aluminate solution, and the desulfurization rate can reach approximately 70% at 373 K for 60 min with the molar ratio of iron to sulfur of 1：1-1.5：1. Furthermore, the desulfurization is achieved by NaFeS2·2H2O precipitation through the reaction of Fe（OH）4 and S^2- in aluminate solution, and the desulfurization efficiency relies on the Fe（OH）4^- generated by dissolving sodium ferrite.