Powder metallurgy（PM） Ti–22Al–24Nb–0.5Mo（at.%） alloys were prepared by hot isostatic pressing. In order to study the feasibility of PM ＋ ring rolling combined process for preparing Ti_2AlNb rings, thermal mech...Powder metallurgy（PM） Ti–22Al–24Nb–0.5Mo（at.%） alloys were prepared by hot isostatic pressing. In order to study the feasibility of PM ＋ ring rolling combined process for preparing Ti_2AlNb rings, thermal mechanical simulation tests of PM Ti_2AlNb alloys were conducted and two rectangular PM rings（150 mm in height, 75 mm in thickness,350 mm in external diameter） were rolled as a validation experiment. Experimental results show that the flow stress of Ti_2AlNb alloys exhibited a significant drop at the very beginning of the deformation（true strain／0.1）, and became stable with the increase in strain. Stress instability phenomenon of PM Ti_2AlNb alloys was more obvious than that of wrought alloy. Flow stress fluctuation at the initial stage of deformation is related to phase transition of Ti_2AlNb alloys which strongly depends on heat treatment and thermal mechanical deformation process. Processing windows during initial stage of ring rolling process is very crucial. A sound PM Ti_2AlNb rectangular ring blank（height = 150 mm, thickness = 30 mm, external diameter = 750 mm） was successfully rolled in two passes by using the improved heat preservation method and optimized rolling parameters. Tensile properties of PM Ti_2AlNb alloy were improved, and the porosity was reduced after ring rolling.展开更多
The synthesis process TiAl based alloy by mechanical milling, warm pressing and reactive sintering was investigated. The microstructure of Ti-Al mixture powders milled was analyzed by backscattering electron image （...The synthesis process TiAl based alloy by mechanical milling, warm pressing and reactive sintering was investigated. The microstructure of Ti-Al mixture powders milled was analyzed by backscattering electron image （BSE）. Then, the powders were warmly pressed in a vacuum hot-pressing device and reactively sintered at different temperatures for different times, the microstructures of TiAl based alloys after sintering were analyzed by scanning electron microscopy（SEM）, energy dispersive spectroscopy（EDS） and optical microscopy（OM）. The compositions of all stages were also analyzed by X-ray diffraction（XRD）. The results show that warm pressing can increase the relative densities of Ti-Al powder billets obviously. The billets warmly pressed with high relative density can be transformed into near fully-densified TiAl based alloy through pre-sintering at low temperature and sintering at high temperature for appropriate time, and the microstructure of the TiAl based alloy is the typical lamellar structure composed of γ-TiAl and α2-Ti3Al.展开更多
文摘Powder metallurgy（PM） Ti–22Al–24Nb–0.5Mo（at.%） alloys were prepared by hot isostatic pressing. In order to study the feasibility of PM ＋ ring rolling combined process for preparing Ti_2AlNb rings, thermal mechanical simulation tests of PM Ti_2AlNb alloys were conducted and two rectangular PM rings（150 mm in height, 75 mm in thickness,350 mm in external diameter） were rolled as a validation experiment. Experimental results show that the flow stress of Ti_2AlNb alloys exhibited a significant drop at the very beginning of the deformation（true strain／0.1）, and became stable with the increase in strain. Stress instability phenomenon of PM Ti_2AlNb alloys was more obvious than that of wrought alloy. Flow stress fluctuation at the initial stage of deformation is related to phase transition of Ti_2AlNb alloys which strongly depends on heat treatment and thermal mechanical deformation process. Processing windows during initial stage of ring rolling process is very crucial. A sound PM Ti_2AlNb rectangular ring blank（height = 150 mm, thickness = 30 mm, external diameter = 750 mm） was successfully rolled in two passes by using the improved heat preservation method and optimized rolling parameters. Tensile properties of PM Ti_2AlNb alloy were improved, and the porosity was reduced after ring rolling.
文摘The synthesis process TiAl based alloy by mechanical milling, warm pressing and reactive sintering was investigated. The microstructure of Ti-Al mixture powders milled was analyzed by backscattering electron image （BSE）. Then, the powders were warmly pressed in a vacuum hot-pressing device and reactively sintered at different temperatures for different times, the microstructures of TiAl based alloys after sintering were analyzed by scanning electron microscopy（SEM）, energy dispersive spectroscopy（EDS） and optical microscopy（OM）. The compositions of all stages were also analyzed by X-ray diffraction（XRD）. The results show that warm pressing can increase the relative densities of Ti-Al powder billets obviously. The billets warmly pressed with high relative density can be transformed into near fully-densified TiAl based alloy through pre-sintering at low temperature and sintering at high temperature for appropriate time, and the microstructure of the TiAl based alloy is the typical lamellar structure composed of γ-TiAl and α2-Ti3Al.