Al86Ni7Y4.5Co1La1.5 （mole fraction, %） alloy powder was produced by argon gas atomization process. After high-energy ball milling, the powder was consolidated by vacuum hot press sintering and spark plasma sintering...Al86Ni7Y4.5Co1La1.5 （mole fraction, %） alloy powder was produced by argon gas atomization process. After high-energy ball milling, the powder was consolidated by vacuum hot press sintering and spark plasma sintering （SPS） under different process conditions. The microstructure and morphology of the powder and consolidated bulk sample were examined by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. It is shown that amorphous phase appears when ball milling time is more than 100 h, and the bulk sample consolidated by SPS can maintain amorphous/ nanocrystalline microstructure but has lower relative density. A compressive strength of 650 MPa of Al86Ni7Y4.5Co1La1.5 nanostructured samples is achieved by vacuum hot extrusion （VHE）.展开更多
基金Project(2012CB619503)supported by the National Basic Research Program of ChinaProject(2013AA031001)supported by the National High Technology Research and Development Program of ChinaProject(2012DFA50630)supported by the International Science&Technology Cooperation Program of China
文摘Al86Ni7Y4.5Co1La1.5 （mole fraction, %） alloy powder was produced by argon gas atomization process. After high-energy ball milling, the powder was consolidated by vacuum hot press sintering and spark plasma sintering （SPS） under different process conditions. The microstructure and morphology of the powder and consolidated bulk sample were examined by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. It is shown that amorphous phase appears when ball milling time is more than 100 h, and the bulk sample consolidated by SPS can maintain amorphous/ nanocrystalline microstructure but has lower relative density. A compressive strength of 650 MPa of Al86Ni7Y4.5Co1La1.5 nanostructured samples is achieved by vacuum hot extrusion （VHE）.