The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for ...The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for lower costs and higher economic benefits in high-carbon ferrochrome production process.This study calculated the activity of CrO_(x)in slag and investigated the distribution behavior of Cr between slag and alloy.Theω(MgO)/ω(Al_(2)O_(3))was 1.0,and the w(CaO)/w(SiO_(2))was from 0.2 to 0.6 in this study.The calculation and experimental results showed that the main phases of the slag were chrome-containing spinel,magnesium-aluminum spinel,olivine and melilite.The content of spinel in slag decreased with the increasing w(CaO)/w(SiO_(2)),and the w(CrO_(x))in spinel also reduced,but the content of melilite increased.The distribution ratio of Cr between slag and alloy decreased with the increase of slag basicity at 1600℃,meansning that increasing the w(CaO)/w(SiO_(2))of slag can improve the recovery of Cr in chromite smelting process.展开更多
文摘焙烧是一种提高多金属金矿中金、银回收率的有效预处理方法,通过热力学计算,得到了多金属金矿NaOH焙烧过程主要化学反应的ΔG0T-T函数,并绘制了ΔG0T-T图.热力学分析结果表明NaOH焙烧能降低CuO.Fe2O3、ZnO.Fe2O3、PbO.SiO2、2ZnO.SiO2的生成几率,从而降低了以上物质对Au、Ag的包裹作用.多金属金矿NaOH焙烧的适宜温度为T≥834.33 K.
基金Project(2023XQLH055)supported by Central South University Graduate Research Innovation Project(University-Enterprise Joint Project),China。
文摘The high-carbon ferrochrome is an essential raw material for producing stainless steel,and the demand of it increases with the increase of stainless steel.So increasing Cr recovery rate from chromite is essential for lower costs and higher economic benefits in high-carbon ferrochrome production process.This study calculated the activity of CrO_(x)in slag and investigated the distribution behavior of Cr between slag and alloy.Theω(MgO)/ω(Al_(2)O_(3))was 1.0,and the w(CaO)/w(SiO_(2))was from 0.2 to 0.6 in this study.The calculation and experimental results showed that the main phases of the slag were chrome-containing spinel,magnesium-aluminum spinel,olivine and melilite.The content of spinel in slag decreased with the increasing w(CaO)/w(SiO_(2)),and the w(CrO_(x))in spinel also reduced,but the content of melilite increased.The distribution ratio of Cr between slag and alloy decreased with the increase of slag basicity at 1600℃,meansning that increasing the w(CaO)/w(SiO_(2))of slag can improve the recovery of Cr in chromite smelting process.