Studies were conducted on how the structure and property of magnesia castable was affected when the magnesia zirconia calcium composite was incorporated. The experimental result indicates that the component CaZrO 3 is...Studies were conducted on how the structure and property of magnesia castable was affected when the magnesia zirconia calcium composite was incorporated. The experimental result indicates that the component CaZrO 3 is easily decomposed by reacting with silica fume to form a low melting point material CMS and CaZr 4O 9 in the silica fume bonded MgO castable, resulting in occurrence of microcracks, which will improve the thermal shock resistance and strength at moderate temperature. In a word, CaZrO 3 improves slag infiltration resistance in spite of lowering the slag corrosion resistance, by absorbing and reacting with components in the slag like Al 2O 3, TiO 2 and FeO.展开更多
This work studied the characteristics of SiO2 distribution and structure of silicate phases in MgO-ZrO2 composites synthesizedby raw materials of light fired magnesite nd zircon,The results indicate that 30 wt%-40wt%...This work studied the characteristics of SiO2 distribution and structure of silicate phases in MgO-ZrO2 composites synthesizedby raw materials of light fired magnesite nd zircon,The results indicate that 30 wt%-40wt% SiO2 content in the system is existed in the form of crystalline of forsterite (M2S),the remaindering of SiO content (60wt%0-70wt%) is existed in the glass phase,The chemical composition of glass phase is well agreed with the chemical composition of monticellite(CMS).展开更多
This paper reviewed the present situation and development of Carbon-Containing castables,disussed the problems and difficulties in the R&D of Carbon-Containing castables.
文摘Studies were conducted on how the structure and property of magnesia castable was affected when the magnesia zirconia calcium composite was incorporated. The experimental result indicates that the component CaZrO 3 is easily decomposed by reacting with silica fume to form a low melting point material CMS and CaZr 4O 9 in the silica fume bonded MgO castable, resulting in occurrence of microcracks, which will improve the thermal shock resistance and strength at moderate temperature. In a word, CaZrO 3 improves slag infiltration resistance in spite of lowering the slag corrosion resistance, by absorbing and reacting with components in the slag like Al 2O 3, TiO 2 and FeO.
文摘This work studied the characteristics of SiO2 distribution and structure of silicate phases in MgO-ZrO2 composites synthesizedby raw materials of light fired magnesite nd zircon,The results indicate that 30 wt%-40wt% SiO2 content in the system is existed in the form of crystalline of forsterite (M2S),the remaindering of SiO content (60wt%0-70wt%) is existed in the glass phase,The chemical composition of glass phase is well agreed with the chemical composition of monticellite(CMS).
文摘This paper reviewed the present situation and development of Carbon-Containing castables,disussed the problems and difficulties in the R&D of Carbon-Containing castables.