The research involves the calcination of Sichuanshimian asbestos tailings with ammonium sulfate in order to extract magnesium. This paper studies the effect of different calcination conditions on the magnesium extract...The research involves the calcination of Sichuanshimian asbestos tailings with ammonium sulfate in order to extract magnesium. This paper studies the effect of different calcination conditions on the magnesium extraction rate, and it also studies the mechanism of calcination of asbestos tailings mixed with ammonium sulfate. The results were characterized by XRD, TGA and elemental analysis. The results showed that as the temperature rises the magnesium extraction rate first increases and then decreases. Optimal experimental conditions are calcination temperature of 600℃, calcination time of 1.5 h, the amount of sodium added of 20%, under which condition a magnesium extraction rate of 85.16% can be achieved.展开更多
Silica is the major component of the acid leaching residue of asbestos tailing.The waterglass solution can be prepared by the reaction of the residue with sodium hydroxide aqueous solution.Compared to the high tempera...Silica is the major component of the acid leaching residue of asbestos tailing.The waterglass solution can be prepared by the reaction of the residue with sodium hydroxide aqueous solution.Compared to the high temperature reaction method,this process is environmental friendly and low cost.In this paper,the reaction process of the residue and the sodium hydroxide aqueous solution is optimized.The optimum reaction process parameters are as follows:the usage of sodium hydroxide is 26.4 g/100 g acid leaching residue,the reaction temperature is 90℃,the reaction time is 1 h,and the ratio of the liquid/solid is 2.0.The significance sequence of the process parameters to the alkali leaching reaction effect is the usage of sodium hydroxide>the ratio of the liquid/solid>the reaction time>the reaction temperature.The significance sequence to the leaching ratio of SiO2 is the ratio of the liquid/solid>the usage of sodium hydroxide>the reaction time>the reaction temperature.The significance sequence to the modulus of the sodium silicate is the ratio of the liquid/solid>the usage of sodium hydroxide>the reaction time>the reaction temperature.Under the optimum conditions,the leaching ratio of the SiO2 is 77.5%,and the modulus of the sodium silicate is 3.15.The XRD analysis result indicates that the major components of the alkali leaching residue are serpentine,talc,quartz and some albite.展开更多
文摘The research involves the calcination of Sichuanshimian asbestos tailings with ammonium sulfate in order to extract magnesium. This paper studies the effect of different calcination conditions on the magnesium extraction rate, and it also studies the mechanism of calcination of asbestos tailings mixed with ammonium sulfate. The results were characterized by XRD, TGA and elemental analysis. The results showed that as the temperature rises the magnesium extraction rate first increases and then decreases. Optimal experimental conditions are calcination temperature of 600℃, calcination time of 1.5 h, the amount of sodium added of 20%, under which condition a magnesium extraction rate of 85.16% can be achieved.
基金Supported by the National Natural Science Foundation of China(Grant No.50674080)
文摘Silica is the major component of the acid leaching residue of asbestos tailing.The waterglass solution can be prepared by the reaction of the residue with sodium hydroxide aqueous solution.Compared to the high temperature reaction method,this process is environmental friendly and low cost.In this paper,the reaction process of the residue and the sodium hydroxide aqueous solution is optimized.The optimum reaction process parameters are as follows:the usage of sodium hydroxide is 26.4 g/100 g acid leaching residue,the reaction temperature is 90℃,the reaction time is 1 h,and the ratio of the liquid/solid is 2.0.The significance sequence of the process parameters to the alkali leaching reaction effect is the usage of sodium hydroxide>the ratio of the liquid/solid>the reaction time>the reaction temperature.The significance sequence to the leaching ratio of SiO2 is the ratio of the liquid/solid>the usage of sodium hydroxide>the reaction time>the reaction temperature.The significance sequence to the modulus of the sodium silicate is the ratio of the liquid/solid>the usage of sodium hydroxide>the reaction time>the reaction temperature.Under the optimum conditions,the leaching ratio of the SiO2 is 77.5%,and the modulus of the sodium silicate is 3.15.The XRD analysis result indicates that the major components of the alkali leaching residue are serpentine,talc,quartz and some albite.