In current research,Li_(2)O-Al_(2)O_(3)-SiO_(2)glass-ceramics were prepared by conventional meltquenching and subsequent heat treatment method.The effect of Al_(2)O_(3)content on microstructures,thermal properties,cry...In current research,Li_(2)O-Al_(2)O_(3)-SiO_(2)glass-ceramics were prepared by conventional meltquenching and subsequent heat treatment method.The effect of Al_(2)O_(3)content on microstructures,thermal properties,crystallization behaviours and mechanical properties were investigated.FTIR,Raman spectroscopy and nuclear magnetic resonance spectroscopy microstructure analysis showed that the silico-oxygen network was damaged,while the increase of[AlO_(4)]content repaired the glass network,and finally made the glass network have better connectivity,with the decrease of SiO_(2).The thermal analysis confirmed the increasing glass transition and crystallization temperatures from growing Al_(2)O_(3)content.In addition,different crystal phases can be precipitated in the glass matrix,such as LiAlSi_(4)O_(10),Li_(2)Si_(2)O_(5) in glass with low Al_(2)O_(3)content,the combination of Li_xAl_xSi_(1-x)O_(2),LiAlSi_(3)O_(8),Li_(2)SiO_(3)in glass with intermediate Al_(2)O_(3)content,and the combination of LiAlSi_(2)O_(6),SiO_(2)in glass with high Al_(2)O_(3)content.The hardness of as-prepared glass gradually increases with the increase of the Al_(2)O_(3)content.The Vickers hardness of the glass-ceramics is highly dependent on the Al_(2)O_(3)content in the glass and the heat treatment temperatures,reaching a maximum of 10.11 GPa.Scanning electron microscope images show that the crystals change from spherical to massive and finally to sheet.The change of glass structure,crystal phase and morphology is the main reason for the different mechanical properties.展开更多
基金Funded by the National Key Research Program(No.2024-1129-954-112)National Natural Science Foundation of China(No.52372033)Guangxi Science and Technology Major Program(No.AA24263054)。
文摘In current research,Li_(2)O-Al_(2)O_(3)-SiO_(2)glass-ceramics were prepared by conventional meltquenching and subsequent heat treatment method.The effect of Al_(2)O_(3)content on microstructures,thermal properties,crystallization behaviours and mechanical properties were investigated.FTIR,Raman spectroscopy and nuclear magnetic resonance spectroscopy microstructure analysis showed that the silico-oxygen network was damaged,while the increase of[AlO_(4)]content repaired the glass network,and finally made the glass network have better connectivity,with the decrease of SiO_(2).The thermal analysis confirmed the increasing glass transition and crystallization temperatures from growing Al_(2)O_(3)content.In addition,different crystal phases can be precipitated in the glass matrix,such as LiAlSi_(4)O_(10),Li_(2)Si_(2)O_(5) in glass with low Al_(2)O_(3)content,the combination of Li_xAl_xSi_(1-x)O_(2),LiAlSi_(3)O_(8),Li_(2)SiO_(3)in glass with intermediate Al_(2)O_(3)content,and the combination of LiAlSi_(2)O_(6),SiO_(2)in glass with high Al_(2)O_(3)content.The hardness of as-prepared glass gradually increases with the increase of the Al_(2)O_(3)content.The Vickers hardness of the glass-ceramics is highly dependent on the Al_(2)O_(3)content in the glass and the heat treatment temperatures,reaching a maximum of 10.11 GPa.Scanning electron microscope images show that the crystals change from spherical to massive and finally to sheet.The change of glass structure,crystal phase and morphology is the main reason for the different mechanical properties.
