The high temperature high cycle fatigue behaviour of a directionally solidified Co-base superalloy was investigated. The alloy has saperior fatigue resistance at 900℃ and its fatigue strength is up to 295MPa. Its σ-...The high temperature high cycle fatigue behaviour of a directionally solidified Co-base superalloy was investigated. The alloy has saperior fatigue resistance at 900℃ and its fatigue strength is up to 295MPa. Its σ-Nf curve is characterized by three distinct zones. The stronger dependence of Nf on or in the high .and low stress zones results from multiple fatigue crock initiation sites produced by high stress and oxidation effect in a prolonged exposure, respectively.展开更多
The influence of Re addition and withdrawal rate on the solidification behavior of the first generation single crystal superalloy AM3 was investigated by directional solidification and quenching experiments.The primar...The influence of Re addition and withdrawal rate on the solidification behavior of the first generation single crystal superalloy AM3 was investigated by directional solidification and quenching experiments.The primary dendrite arm spacing and eutectic volume fraction were measured from directionally solidified superalloy AM3 with different Re contents.It is found that the primary dendrite arm spacing is determined by the withdrawal rate,and Re does not influence on the value.The eutectic fraction increases with increasing Re addition.Partition coeffcients of alloying elements were investigated with energy-dispersive X-ray spectrometry（EDS） analysis.The data was submitted to a statistical treatment to establish the solidification path,and the partition coeficients were measured by fitting the curve with a modified Scheil formula.It is shown that the addition of Re results in bigger microsegregation of alloying elements in directionally solidified AM3 superalloy.展开更多
Microstructural stability of a nickel base single crystal alloy DD8 has been investigated.Standard heat treated specimen showed good microstructural stability at 950℃.While under the as-cast condition,a kind of rod-l...Microstructural stability of a nickel base single crystal alloy DD8 has been investigated.Standard heat treated specimen showed good microstructural stability at 950℃.While under the as-cast condition,a kind of rod-like phase precipitated in the interdendritic region of as-cast specimen during thermal exposure.The phase,which has bcc structure,was enriched with Cr.Thermo-calc also predicted precipitation of a bcc phase at around 950℃.The Cr-rich bcc phase was considered asα-Cr and formed due to the segregation of Cr under the as-cast condition.展开更多
文摘The high temperature high cycle fatigue behaviour of a directionally solidified Co-base superalloy was investigated. The alloy has saperior fatigue resistance at 900℃ and its fatigue strength is up to 295MPa. Its σ-Nf curve is characterized by three distinct zones. The stronger dependence of Nf on or in the high .and low stress zones results from multiple fatigue crock initiation sites produced by high stress and oxidation effect in a prolonged exposure, respectively.
文摘The influence of Re addition and withdrawal rate on the solidification behavior of the first generation single crystal superalloy AM3 was investigated by directional solidification and quenching experiments.The primary dendrite arm spacing and eutectic volume fraction were measured from directionally solidified superalloy AM3 with different Re contents.It is found that the primary dendrite arm spacing is determined by the withdrawal rate,and Re does not influence on the value.The eutectic fraction increases with increasing Re addition.Partition coeffcients of alloying elements were investigated with energy-dispersive X-ray spectrometry（EDS） analysis.The data was submitted to a statistical treatment to establish the solidification path,and the partition coeficients were measured by fitting the curve with a modified Scheil formula.It is shown that the addition of Re results in bigger microsegregation of alloying elements in directionally solidified AM3 superalloy.
文摘Microstructural stability of a nickel base single crystal alloy DD8 has been investigated.Standard heat treated specimen showed good microstructural stability at 950℃.While under the as-cast condition,a kind of rod-like phase precipitated in the interdendritic region of as-cast specimen during thermal exposure.The phase,which has bcc structure,was enriched with Cr.Thermo-calc also predicted precipitation of a bcc phase at around 950℃.The Cr-rich bcc phase was considered asα-Cr and formed due to the segregation of Cr under the as-cast condition.