TiO 2 nanowires were synthesized successfully in a large quantity by thermal evaporation using titanium monoxide powder as precursor. X-ray diffraction results showed that all the products were pure rutile phase of Ti...TiO 2 nanowires were synthesized successfully in a large quantity by thermal evaporation using titanium monoxide powder as precursor. X-ray diffraction results showed that all the products were pure rutile phase of TiO 2 . According to microstructural observations, the nanowires have two typical morphologies, a long straight type and a short tortuous type. The straight nanowires were obtained at a wide temperature range of 900–1050 ℃, while the tortuous ones were formed below 900 ℃. Transmission electron microscopy characterization revealed that both the straight and the tortuous nanowires are single-crystal rutile TiO 2 . The preferential growth direction of the nanowires was determined as [110] orientation according to electron diffraction and high-resolution image analyses. The morphological change of TiO 2 nanowires was discussed by considering the different atomic diffusion rates of Ti atoms caused by the phase transformation in Ti substrate at around 900 ℃.展开更多
基金supported by the Hundred Talents Program of the Chinese Academy of Sciences,Shenyang Science and Technology Project (Grant No.F11-264-1-65)the National Basic Research Program of China (Grant No. 2010CB631006)the Major National Science and Technology Program of China (GrantNo. 2011ZX02602)
文摘TiO 2 nanowires were synthesized successfully in a large quantity by thermal evaporation using titanium monoxide powder as precursor. X-ray diffraction results showed that all the products were pure rutile phase of TiO 2 . According to microstructural observations, the nanowires have two typical morphologies, a long straight type and a short tortuous type. The straight nanowires were obtained at a wide temperature range of 900–1050 ℃, while the tortuous ones were formed below 900 ℃. Transmission electron microscopy characterization revealed that both the straight and the tortuous nanowires are single-crystal rutile TiO 2 . The preferential growth direction of the nanowires was determined as [110] orientation according to electron diffraction and high-resolution image analyses. The morphological change of TiO 2 nanowires was discussed by considering the different atomic diffusion rates of Ti atoms caused by the phase transformation in Ti substrate at around 900 ℃.