The solubilities of carbon in Mn based alloys containing P have been measured at 1 400 ℃ based on X C=0.271 9-0.094 0 X Fe -1.195 4 X P. By means of thermodynamic derivation and calculation, th...The solubilities of carbon in Mn based alloys containing P have been measured at 1 400 ℃ based on X C=0.271 9-0.094 0 X Fe -1.195 4 X P. By means of thermodynamic derivation and calculation, the relative activity coefficients and interactive parameters were derived.展开更多
Samples of the cross section microstructures of galvannealed steel sheets that lack alloying were analyzed. X-ray diffraction （XRD） tests were carried out. The study discovers that the deficit of alloying was higher...Samples of the cross section microstructures of galvannealed steel sheets that lack alloying were analyzed. X-ray diffraction （XRD） tests were carried out. The study discovers that the deficit of alloying was higher on both sides of the steel sheet when compared to the center and the thickness of the coating on the sides was also higher than the center. The results of the XRD tests demonstrate that the microstructure of the coating with a lack of alloy is mainly composed of zinc,ζ and δ. They also indicate that the lack of alloying is mainly due to a lower galvannealing temperature and thicker coating. It is shown by the optical micrographs of coating that the δ phase forms first in a discontinuous manner at the interface and then rapidly pushes towards the coating and enlarges.展开更多
文摘The solubilities of carbon in Mn based alloys containing P have been measured at 1 400 ℃ based on X C=0.271 9-0.094 0 X Fe -1.195 4 X P. By means of thermodynamic derivation and calculation, the relative activity coefficients and interactive parameters were derived.
文摘Samples of the cross section microstructures of galvannealed steel sheets that lack alloying were analyzed. X-ray diffraction （XRD） tests were carried out. The study discovers that the deficit of alloying was higher on both sides of the steel sheet when compared to the center and the thickness of the coating on the sides was also higher than the center. The results of the XRD tests demonstrate that the microstructure of the coating with a lack of alloy is mainly composed of zinc,ζ and δ. They also indicate that the lack of alloying is mainly due to a lower galvannealing temperature and thicker coating. It is shown by the optical micrographs of coating that the δ phase forms first in a discontinuous manner at the interface and then rapidly pushes towards the coating and enlarges.