93W-4.9Ni-2.1Fe alloys strengthened by nanoscale ZrC particles were prepared by spark-plasma-sintering(SPS)and hot rotary swaging,separately.Results show that the addition of a small number of ZrC nanoparticles can re...93W-4.9Ni-2.1Fe alloys strengthened by nanoscale ZrC particles were prepared by spark-plasma-sintering(SPS)and hot rotary swaging,separately.Results show that the addition of a small number of ZrC nanoparticles can refine grains and increase the hardness of the WNiFe alloys,but hinder the formation of theγ-(Ni,Fe)phase during SPS.SPSed WNiFe and WNiFe-ZrC alloys are brittle at room temperature,while the swaged WNiFe and WNiFe-0.5ZrC(wt%)alloys are ductile.At 400°C,the swaged WNiFe-0.5ZrC alloy exhibits both higher tensile strength and better ductility than the swaged WNiFe.The nanoscale particles distributed in the W grains andγ-(Ni,Fe)phase provide a good pinning effect,which enhances the strength.The thermal conductivity of swaged WNiFe-0.5ZrC is only 71 W·m^(-1)·K^(-1)at room temperature,but it increases to about 100 W·m^(-1)·K^(-1)at 800°C,which is close to that of pure W(121 W·m^(-1)·K^(-1)).These results show the potential of WNiFe alloys as plasma-facing materials in fusion reactor.展开更多
基金National Key Research and Development Program of China(2022YFE03140002,2019YFE03110200)National Natural Science Foundation of China(52273320,52173303,52325103,52171084)+2 种基金Strategic Priority Research Program of the Chinese Academy of Sciences(XDB0470000)Anhui Provincial Natural Science Foundation(2308085J07)HFIPS Director's Fund(YZJJ202102,YZJJQY202306,YZJJKX202202)。
文摘93W-4.9Ni-2.1Fe alloys strengthened by nanoscale ZrC particles were prepared by spark-plasma-sintering(SPS)and hot rotary swaging,separately.Results show that the addition of a small number of ZrC nanoparticles can refine grains and increase the hardness of the WNiFe alloys,but hinder the formation of theγ-(Ni,Fe)phase during SPS.SPSed WNiFe and WNiFe-ZrC alloys are brittle at room temperature,while the swaged WNiFe and WNiFe-0.5ZrC(wt%)alloys are ductile.At 400°C,the swaged WNiFe-0.5ZrC alloy exhibits both higher tensile strength and better ductility than the swaged WNiFe.The nanoscale particles distributed in the W grains andγ-(Ni,Fe)phase provide a good pinning effect,which enhances the strength.The thermal conductivity of swaged WNiFe-0.5ZrC is only 71 W·m^(-1)·K^(-1)at room temperature,but it increases to about 100 W·m^(-1)·K^(-1)at 800°C,which is close to that of pure W(121 W·m^(-1)·K^(-1)).These results show the potential of WNiFe alloys as plasma-facing materials in fusion reactor.