The Mn_(1.95-x)Co_(0.21)Ni_(0.84)Sr_(x)O_(4)(MCNS)(0≤x≤0.15)based negative temperature coefficient(NTC)materials are prepared by co-precipitation method.The replacement of Mn by Sr plays a critical role in controlli...The Mn_(1.95-x)Co_(0.21)Ni_(0.84)Sr_(x)O_(4)(MCNS)(0≤x≤0.15)based negative temperature coefficient(NTC)materials are prepared by co-precipitation method.The replacement of Mn by Sr plays a critical role in controlling the lattice parameter,relative density,microstructure,and electrical properties.The lattice parameter and relative density increase with the increase of Sr content.A small amount of Sr restrains the grain growth and increases the bulk density.Moreover,the room resistivityρ25,material constant B25/50,activation energy Ea,and temperature coefficientαvalues of MCNS ceramics are influenced by the Sr content and ranged in 1535.0–2053.6Ω·cm,3654–3709 K,0.3149–0.3197 eV,and(–4.173%)–(–4.111%),respectively.The X-ray photoelectron spectroscopy(XPS)results explain the transformation of MCNS ceramics from n-to p-type semiconductors.The conduction could arise from the hopping polaron between Mn3+/Mn4+and Co^(2+)/Co^(3+) in the octahedral sites.The impedance data analysis also discusses the conduction mechanism of the MCNS ceramic,whereas grain resistance dominates the whole resistance of the samples.Furthermore,the aging coefficient(△R/R)of MCNS ceramics is found to be<0.2%,which indicates the stable distribution of cations in the spinel.Finally,the MCNS ceramics demonstrate excellent thermal durability with<1.3%of resistance shift after 100 thermal shock cycles.展开更多
基金supported by Xinjiang Key Laboratory of Electronic Information Materials and Devices Foundation(Grant No.2018D04006)Tianshan Cedar Project of Xinjiang Uygur Autonomous Region(Grant No.2018XS09)the National Natural Science Foundation of China(Grant No.51872326)。
文摘The Mn_(1.95-x)Co_(0.21)Ni_(0.84)Sr_(x)O_(4)(MCNS)(0≤x≤0.15)based negative temperature coefficient(NTC)materials are prepared by co-precipitation method.The replacement of Mn by Sr plays a critical role in controlling the lattice parameter,relative density,microstructure,and electrical properties.The lattice parameter and relative density increase with the increase of Sr content.A small amount of Sr restrains the grain growth and increases the bulk density.Moreover,the room resistivityρ25,material constant B25/50,activation energy Ea,and temperature coefficientαvalues of MCNS ceramics are influenced by the Sr content and ranged in 1535.0–2053.6Ω·cm,3654–3709 K,0.3149–0.3197 eV,and(–4.173%)–(–4.111%),respectively.The X-ray photoelectron spectroscopy(XPS)results explain the transformation of MCNS ceramics from n-to p-type semiconductors.The conduction could arise from the hopping polaron between Mn3+/Mn4+and Co^(2+)/Co^(3+) in the octahedral sites.The impedance data analysis also discusses the conduction mechanism of the MCNS ceramic,whereas grain resistance dominates the whole resistance of the samples.Furthermore,the aging coefficient(△R/R)of MCNS ceramics is found to be<0.2%,which indicates the stable distribution of cations in the spinel.Finally,the MCNS ceramics demonstrate excellent thermal durability with<1.3%of resistance shift after 100 thermal shock cycles.