Fe-based amorphous and nanocrystalline coatings were fabricated by air plasma spraying. The coatings were further treated by laser remelting process to improve their microstructure and properties. The corrosion resist...Fe-based amorphous and nanocrystalline coatings were fabricated by air plasma spraying. The coatings were further treated by laser remelting process to improve their microstructure and properties. The corrosion resistance of the as-sprayed and laser-remelted coatings in 3.5wt% NaC1 and 1 mol/L HCI solutions was evaluated by electrochemical polarization analysis. It was found that laser-remelted coating appeared much denser than the as-sprayed coating. However, laser-remelted coating contains much more nanocrystalline grains than the as-sprayed coatings, resulting from the lower cooling rate in laser remelting process compared with plasma spraying process. Electrochemical polarization results indicated that the laser-remelted coating has great corrosion resistance than the as-sprayed coating because of its dense structure.展开更多
The Fe-based amorphous coatings were produced by air plasma spraying. The as-sprayed coatings were heat-treated at the temperature of 573, 873, and 1 023 K, respectively. The crystallization and wear behavior of the h...The Fe-based amorphous coatings were produced by air plasma spraying. The as-sprayed coatings were heat-treated at the temperature of 573, 873, and 1 023 K, respectively. The crystallization and wear behavior of the heat-treated amorphous coatings were investigated. It was found that the amorphous- nanocrystalline transformation appeared when the as-sprayed coatings were treated at 853 K. The crystallization process had completed and a coating with microcrystallines was formed when the treatment temperature reached 1 023 K. The resultant amorphous and nanocrystalline composite coatings exhibited superior wear resistance compared to crystalline coating. It is attributed to fine grain strengthening of formed nanocrystallines.展开更多
Ni-Al_(2)O_(3)cermet supported tubular SOFC was fabricated by thermal spraying.Flame-sprayed Al_(2)O_(3)-Ni cermet coating plays dual roles of a support tube and an anode current collector.4.5mol.%yttria-stabilized zi...Ni-Al_(2)O_(3)cermet supported tubular SOFC was fabricated by thermal spraying.Flame-sprayed Al_(2)O_(3)-Ni cermet coating plays dual roles of a support tube and an anode current collector.4.5mol.%yttria-stabilized zirconia(YSZ)and 10mol.%scandia-stabilized zirconia(ScSZ)coatings were deposited by atmospheric plasma spraying(APS)as the electrolyte in present study.The electrical conductivity of electrolyte was measured using DC method.The post treatment was employed using nitrate solution infiltration to densify APS electrolyte layer for improvement of gas permeability.The electrical conductivity of electrolyte and the performance of single cell were investigated to optimize SOFC performance.The electrical conductivity of the as-sprayed YSZ and ScSZ coating is about 0.03 and 0.07 S·cm^(-1)at 1000℃,respectively.The ohmic polarization significantly influences the performance of SOFC.The maximum output power density at 1000℃increases from 0.47 to 0.76 W·cm^(-2)as the YSZ electrolyte thickness reduces from 100μm to 40μm.Using APS ScSZ coating of about 40μm as the electrolyte,the test cell presents a maximum power output density of over 0.89 W·cm^(-2)at 1000℃.展开更多
A composite layer was prepared on the surface of Ti-6Al-4V alloy by nitriding-sulfurizing composite treatment,and its microstructure and phase structure were examined by scanning electron microscopy(SEM)and X-ray diff...A composite layer was prepared on the surface of Ti-6Al-4V alloy by nitriding-sulfurizing composite treatment,and its microstructure and phase structure were examined by scanning electron microscopy(SEM)and X-ray diffraction(XRD),respectively.The tribological performance was measured to investigate its dependence on the nitriding-sulfurizing composite treatment process.The results indicated that the composite layer was mainly comprised of Ti2N,TiN,and TiS2.It was found that the composite layer exhibited superior tribological properties under dry friction and absolute sliding conditions due to the formation of sulfides with self-lubricating function.展开更多
基金Funded by the Special Found for Basic Scientific Research of Central Colleges,Chang'an University(2014G1311093)the AQSIQ Technology Program Project(2013QK111)
文摘Fe-based amorphous and nanocrystalline coatings were fabricated by air plasma spraying. The coatings were further treated by laser remelting process to improve their microstructure and properties. The corrosion resistance of the as-sprayed and laser-remelted coatings in 3.5wt% NaC1 and 1 mol/L HCI solutions was evaluated by electrochemical polarization analysis. It was found that laser-remelted coating appeared much denser than the as-sprayed coating. However, laser-remelted coating contains much more nanocrystalline grains than the as-sprayed coatings, resulting from the lower cooling rate in laser remelting process compared with plasma spraying process. Electrochemical polarization results indicated that the laser-remelted coating has great corrosion resistance than the as-sprayed coating because of its dense structure.
基金Funded by the Basic Scientific Research of Central Colleges,Chang’an University (No. CHD2011JC126)
文摘The Fe-based amorphous coatings were produced by air plasma spraying. The as-sprayed coatings were heat-treated at the temperature of 573, 873, and 1 023 K, respectively. The crystallization and wear behavior of the heat-treated amorphous coatings were investigated. It was found that the amorphous- nanocrystalline transformation appeared when the as-sprayed coatings were treated at 853 K. The crystallization process had completed and a coating with microcrystallines was formed when the treatment temperature reached 1 023 K. The resultant amorphous and nanocrystalline composite coatings exhibited superior wear resistance compared to crystalline coating. It is attributed to fine grain strengthening of formed nanocrystallines.
基金The present project was supported by Foundation of China Education Ministry for Talented Young ScholarEducation Promotion ProjectDoctoral Thesis Foundation of Xi'an Jiaotong University.
文摘Ni-Al_(2)O_(3)cermet supported tubular SOFC was fabricated by thermal spraying.Flame-sprayed Al_(2)O_(3)-Ni cermet coating plays dual roles of a support tube and an anode current collector.4.5mol.%yttria-stabilized zirconia(YSZ)and 10mol.%scandia-stabilized zirconia(ScSZ)coatings were deposited by atmospheric plasma spraying(APS)as the electrolyte in present study.The electrical conductivity of electrolyte was measured using DC method.The post treatment was employed using nitrate solution infiltration to densify APS electrolyte layer for improvement of gas permeability.The electrical conductivity of electrolyte and the performance of single cell were investigated to optimize SOFC performance.The electrical conductivity of the as-sprayed YSZ and ScSZ coating is about 0.03 and 0.07 S·cm^(-1)at 1000℃,respectively.The ohmic polarization significantly influences the performance of SOFC.The maximum output power density at 1000℃increases from 0.47 to 0.76 W·cm^(-2)as the YSZ electrolyte thickness reduces from 100μm to 40μm.Using APS ScSZ coating of about 40μm as the electrolyte,the test cell presents a maximum power output density of over 0.89 W·cm^(-2)at 1000℃.
文摘A composite layer was prepared on the surface of Ti-6Al-4V alloy by nitriding-sulfurizing composite treatment,and its microstructure and phase structure were examined by scanning electron microscopy(SEM)and X-ray diffraction(XRD),respectively.The tribological performance was measured to investigate its dependence on the nitriding-sulfurizing composite treatment process.The results indicated that the composite layer was mainly comprised of Ti2N,TiN,and TiS2.It was found that the composite layer exhibited superior tribological properties under dry friction and absolute sliding conditions due to the formation of sulfides with self-lubricating function.