Effect of pre-induced twinning on the microstructure evolution and mechanical properties of extruded Mg-9.26Gd-2.08Y-0.36Zr(GW92K)alloy have been investigated during multi-direction forging with large strains at decre...Effect of pre-induced twinning on the microstructure evolution and mechanical properties of extruded Mg-9.26Gd-2.08Y-0.36Zr(GW92K)alloy have been investigated during multi-direction forging with large strains at decreasing temperature from 400℃ to 300℃.The results showed that,whether there pre-induced twinning existing in the initial microstructure by pre-deformation or not,a mixed microstructure of residual coarse grains and notably refined grains formed under both conditions,combing with some residual coarse grains with less deformation inside grains and lots of dispersed nano-precipitates distributed along refined grain boundaries.However,a significant improvement with the tensile ductility was obtained by the pre-induced twinning in the former alloy.It was suggested that,the pre-induced twinning largely contributed to the grain refinement and lead to an increase in the ratio of fine grain structure which would be responsible for the better properties.Furthermore,during subsequent forging deformation in the pre-deformed sample,the grain refinement mechanism by gradual grain orientation rotation around the surface section in residual coarse-grains was a little different from that by the macro-shear deformation in the as-extruded condition.展开更多
In this work a new nanoscale surface marking technique,namely electron beam damage induced surface marking(EBDISM),is developed and tested for the first time on a fine-grained pure Mg surface.This technique utilizes f...In this work a new nanoscale surface marking technique,namely electron beam damage induced surface marking(EBDISM),is developed and tested for the first time on a fine-grained pure Mg surface.This technique utilizes focused high-energy electron beam of a scanning electron microscope to“burn”dense arrays of nano-scale grid patterns on the sample surface,and it is proved to be very effective for identifying and measuring localised deformation behaviours.However,the surface marking deposited by EBDISM is not permanent and it tends to deteriorate overtime.Cheap,easy to use and versatile,the EBDISM technique has a huge potential for quantitative measurement of strain field and nano-scale deformation analysis.展开更多
基金The authors gratefully acknowledge financial support from the National Basic Research Program of China(973 Program)through project no.2013CB632202National Natural Science Foundation of China(NSFC)through project no.51105350.
文摘Effect of pre-induced twinning on the microstructure evolution and mechanical properties of extruded Mg-9.26Gd-2.08Y-0.36Zr(GW92K)alloy have been investigated during multi-direction forging with large strains at decreasing temperature from 400℃ to 300℃.The results showed that,whether there pre-induced twinning existing in the initial microstructure by pre-deformation or not,a mixed microstructure of residual coarse grains and notably refined grains formed under both conditions,combing with some residual coarse grains with less deformation inside grains and lots of dispersed nano-precipitates distributed along refined grain boundaries.However,a significant improvement with the tensile ductility was obtained by the pre-induced twinning in the former alloy.It was suggested that,the pre-induced twinning largely contributed to the grain refinement and lead to an increase in the ratio of fine grain structure which would be responsible for the better properties.Furthermore,during subsequent forging deformation in the pre-deformed sample,the grain refinement mechanism by gradual grain orientation rotation around the surface section in residual coarse-grains was a little different from that by the macro-shear deformation in the as-extruded condition.
基金support from the Australian Research Council(LP180100048)Baosteel Company。
文摘In this work a new nanoscale surface marking technique,namely electron beam damage induced surface marking(EBDISM),is developed and tested for the first time on a fine-grained pure Mg surface.This technique utilizes focused high-energy electron beam of a scanning electron microscope to“burn”dense arrays of nano-scale grid patterns on the sample surface,and it is proved to be very effective for identifying and measuring localised deformation behaviours.However,the surface marking deposited by EBDISM is not permanent and it tends to deteriorate overtime.Cheap,easy to use and versatile,the EBDISM technique has a huge potential for quantitative measurement of strain field and nano-scale deformation analysis.