Sea urchin-like cuprous oxide with hollow glass microsphere as core was prepared using sodium sulfite as the reducing agent and sodium acetate-acetic acid as buffer solution in copper sulfate solution. Methyl orange w...Sea urchin-like cuprous oxide with hollow glass microsphere as core was prepared using sodium sulfite as the reducing agent and sodium acetate-acetic acid as buffer solution in copper sulfate solution. Methyl orange was selected as degradation target for photocatalytic experiments. The photocatalytic activities were investigated by visible spectro- photometer. Photocatalytic kinetics parameters were studied by the Langmuir-Hinshelwood model and Arrhenius formula. It was observed that the sea urchin-like morphology dramatically improved the photocatalytic activity of cuprous oxide. The photo-degradation belongs to the first-order reaction and the maximum degradation rate could reach 94.37%. The activation energy and pre-exponential factor are 41.18 KJ·mol-1 and 1.07 × 106, respectively. After seven times recycling, the sample still showed high photo-catalytic efficiency and stability.展开更多
文摘Sea urchin-like cuprous oxide with hollow glass microsphere as core was prepared using sodium sulfite as the reducing agent and sodium acetate-acetic acid as buffer solution in copper sulfate solution. Methyl orange was selected as degradation target for photocatalytic experiments. The photocatalytic activities were investigated by visible spectro- photometer. Photocatalytic kinetics parameters were studied by the Langmuir-Hinshelwood model and Arrhenius formula. It was observed that the sea urchin-like morphology dramatically improved the photocatalytic activity of cuprous oxide. The photo-degradation belongs to the first-order reaction and the maximum degradation rate could reach 94.37%. The activation energy and pre-exponential factor are 41.18 KJ·mol-1 and 1.07 × 106, respectively. After seven times recycling, the sample still showed high photo-catalytic efficiency and stability.