This study investigated the mechanical properties and microstructural characteristics of fiberboard composite produced by naturally-bonded Malaysian bamboo fiber(Bambusa vulgaris).The components that obtained through ...This study investigated the mechanical properties and microstructural characteristics of fiberboard composite produced by naturally-bonded Malaysian bamboo fiber(Bambusa vulgaris).The components that obtained through soda pulping of bamboo culms such as fiber and black liquor,were used for the preparation of high-density fibreboard composite at two target densities of 850 and 950 kg/m^(3).The bamboo fiberboard composite(BFC)were then produced at 200°C and two pressing parameters of 125 and 175 s/mm.The mechanical properties,e.g.,flexural strength and internal bonding(IB)of BFC samples were evaluated according to BS EN 310:1993 and BS EN 319:1993,respectively.It was found that the mechanical performance of the composite with 850 kg/m^(3)density was significantly higher than 950 kg/m^(3)ones,especially for the samples with 125 s/mm pressing parameter.Microstructure characteristic of the BFC samples illustrated that the fiber linkages were cracked in the composites with higher density,e.g.,the composite with the density of 950 kg/m^(3)and also black liquor were slightly degraded at longer pressing time,which led to the reduction in mechanical properties,especially in IB strength.展开更多
基金the Fundamental Research Grant Scheme(FRGS),Ministry of Higher Education Malaysia(Project Code:600-IRDC/ST/FRGS.5/3/1156)entitled“Strength Properties of Environmental-Friendly Binderless Bamboo Medium Density Fibreboard(bBMDF)”.
文摘This study investigated the mechanical properties and microstructural characteristics of fiberboard composite produced by naturally-bonded Malaysian bamboo fiber(Bambusa vulgaris).The components that obtained through soda pulping of bamboo culms such as fiber and black liquor,were used for the preparation of high-density fibreboard composite at two target densities of 850 and 950 kg/m^(3).The bamboo fiberboard composite(BFC)were then produced at 200°C and two pressing parameters of 125 and 175 s/mm.The mechanical properties,e.g.,flexural strength and internal bonding(IB)of BFC samples were evaluated according to BS EN 310:1993 and BS EN 319:1993,respectively.It was found that the mechanical performance of the composite with 850 kg/m^(3)density was significantly higher than 950 kg/m^(3)ones,especially for the samples with 125 s/mm pressing parameter.Microstructure characteristic of the BFC samples illustrated that the fiber linkages were cracked in the composites with higher density,e.g.,the composite with the density of 950 kg/m^(3)and also black liquor were slightly degraded at longer pressing time,which led to the reduction in mechanical properties,especially in IB strength.