Silicon oxide(SiO_(x))has received remarkable attention as a next-generation battery material;however,the sudden decrease in the cycling retention constitutes a significant challenge in facilitating its application.Tr...Silicon oxide(SiO_(x))has received remarkable attention as a next-generation battery material;however,the sudden decrease in the cycling retention constitutes a significant challenge in facilitating its application.Tris(2,2,2-trifluoroethyl)phosphite(TTFP),which can control parasitic reactions such as the pulverization of SiO_(x)anode materials and electrolyte decomposition,has been proposed to improve the lifespan of the cell.The electrochemical reduction of TTFP results in solid-electrolyte interphase(SEI)layers that are mainly composed of LiF,which occur at a higher potential than the working potential of the SiO_(x)anode and carbonate-based solvents.The electrolyte with TTFP exhibited a substantial improvement in cycling retention after 100 cycles,whereas the standard electrolyte showed acutely decreased retention.The thickness of the SiO_(x)anode with TTFP also changed only slightly without any considerable delamination spots,whereas the SiO_(x)anode without TTFP was prominently deformed by an enormous volume expansion with several internal cracks.The cycled SiO_(x)anode with TTFP exhibited less increase in resistance after cycling than that in the absence of TTFP,in addition to fewer decomposition adducts in corresponding X-ray photoelectron spectroscopy(XPS)analyses between the cycled SiO_(x)anodes.These results demonstrate that TTFP formed SEI layers at the SiO_(x)interface,which substantially reduced the pulverization of the SiO_(x)anode materials;in addition,electrolyte decomposition at the interface decreased,which led to improved cycling retention.展开更多
基金This work was financially supported by the National Research Foundation of Korea financially(NRF)(No.NRF-2022R1F1A1069039)the Core Research Institute(CRI)Program,the Basic Science Research Program through the National Research Foundation of Korea(NRF),Ministry of Education(No.NRF-2017R1A6A1A06015181)the Technology Innovation Program(No.20011905)funded by the Ministry of Trade,Industry&Energy(MOTIE,Korea).
文摘Silicon oxide(SiO_(x))has received remarkable attention as a next-generation battery material;however,the sudden decrease in the cycling retention constitutes a significant challenge in facilitating its application.Tris(2,2,2-trifluoroethyl)phosphite(TTFP),which can control parasitic reactions such as the pulverization of SiO_(x)anode materials and electrolyte decomposition,has been proposed to improve the lifespan of the cell.The electrochemical reduction of TTFP results in solid-electrolyte interphase(SEI)layers that are mainly composed of LiF,which occur at a higher potential than the working potential of the SiO_(x)anode and carbonate-based solvents.The electrolyte with TTFP exhibited a substantial improvement in cycling retention after 100 cycles,whereas the standard electrolyte showed acutely decreased retention.The thickness of the SiO_(x)anode with TTFP also changed only slightly without any considerable delamination spots,whereas the SiO_(x)anode without TTFP was prominently deformed by an enormous volume expansion with several internal cracks.The cycled SiO_(x)anode with TTFP exhibited less increase in resistance after cycling than that in the absence of TTFP,in addition to fewer decomposition adducts in corresponding X-ray photoelectron spectroscopy(XPS)analyses between the cycled SiO_(x)anodes.These results demonstrate that TTFP formed SEI layers at the SiO_(x)interface,which substantially reduced the pulverization of the SiO_(x)anode materials;in addition,electrolyte decomposition at the interface decreased,which led to improved cycling retention.