Aiming at recovering iron from high-iron-content copper slag, this article introduced a combination technol- ogy of deep reduction and magnetic beneficiation, investigated the iron recovery efficiency and optimized th...Aiming at recovering iron from high-iron-content copper slag, this article introduced a combination technol- ogy of deep reduction and magnetic beneficiation, investigated the iron recovery efficiency and optimized the technical conditions. When coke powder with 86wt% fixed carbon was used as a reductant, iron was successfully extracted from the copper slag. Under the optimized condition of the coke powder content of 14wt%, the calcium-to-silicon mass ratio （Ca/Si） of 0.2, the roasting temperature of 1300℃, the roasting time of 3 h, the grinding time of 20 min, and the magnetic field intensity of 61 kA-m-1, the iron recovery rate of the copper slag can reach 91.82%, and the extracted iron powder has an iron grade of 96.21%. With the characteristics of high iron grade and low impurity content, the extracted iron powder can be used as high-quality raw materials of weathering steel.展开更多
基金the National High Technology Research and Development Program of China(No.2012AA062406)
文摘Aiming at recovering iron from high-iron-content copper slag, this article introduced a combination technol- ogy of deep reduction and magnetic beneficiation, investigated the iron recovery efficiency and optimized the technical conditions. When coke powder with 86wt% fixed carbon was used as a reductant, iron was successfully extracted from the copper slag. Under the optimized condition of the coke powder content of 14wt%, the calcium-to-silicon mass ratio （Ca/Si） of 0.2, the roasting temperature of 1300℃, the roasting time of 3 h, the grinding time of 20 min, and the magnetic field intensity of 61 kA-m-1, the iron recovery rate of the copper slag can reach 91.82%, and the extracted iron powder has an iron grade of 96.21%. With the characteristics of high iron grade and low impurity content, the extracted iron powder can be used as high-quality raw materials of weathering steel.