This work investigated the effect of pre-strain and microstructures and their interactions on hydrogen trapping behaviors in case of 1-GPa high-strength martensitic steel Fe-0.05C-0.30Si-1.10Mn-3.50Ni-0.53Cr-0.50Mo-0....This work investigated the effect of pre-strain and microstructures and their interactions on hydrogen trapping behaviors in case of 1-GPa high-strength martensitic steel Fe-0.05C-0.30Si-1.10Mn-3.50Ni-0.53Cr-0.50Mo-0.03 V(wt%).We found that the trapped reversible and trapped irreversible hydrogen contents increased significantly after applying a pre-strain of 5%,with an increase in the trapped reversible hydrogen content from 0.6 ppm in the original sample to 2.1 ppm.The hydrogen desorption activation energy also showed a slight increase.The microstructural evolution revealed that the concomitant dislocation cell-twin duplex microstructure with high-density tangled dislocations after pre-strain substantially increased the trapped reversible hydrogen contents.Additionally,the tangled dislocations pinned by the nanoprecipitates acted as deep irreversible hydrogen traps,increasing the trapped hydrogen at high temperatures after applying 5%pre-strain.These findings provide an expanded understanding of the hydrogen trapping behaviors of pre-strained microstructures.展开更多
基金The authors acknowledge the financial support received from the National Natural Science Foundation of China(Nos.52201060,51922002,and 52001182)the China Postdoctoral Science Foundation(Nos.BX20220035 and 2022M710347)the Science Center for Gas Turbine Project(No.P2022-B-IV-008-001).
文摘This work investigated the effect of pre-strain and microstructures and their interactions on hydrogen trapping behaviors in case of 1-GPa high-strength martensitic steel Fe-0.05C-0.30Si-1.10Mn-3.50Ni-0.53Cr-0.50Mo-0.03 V(wt%).We found that the trapped reversible and trapped irreversible hydrogen contents increased significantly after applying a pre-strain of 5%,with an increase in the trapped reversible hydrogen content from 0.6 ppm in the original sample to 2.1 ppm.The hydrogen desorption activation energy also showed a slight increase.The microstructural evolution revealed that the concomitant dislocation cell-twin duplex microstructure with high-density tangled dislocations after pre-strain substantially increased the trapped reversible hydrogen contents.Additionally,the tangled dislocations pinned by the nanoprecipitates acted as deep irreversible hydrogen traps,increasing the trapped hydrogen at high temperatures after applying 5%pre-strain.These findings provide an expanded understanding of the hydrogen trapping behaviors of pre-strained microstructures.