The density of liquid Incone1718 alloy was experimentally measured by electrostatic levitation technique, where the maximum undercooling of 100 K was realized for the commercial sample. The measured density of liquid ...The density of liquid Incone1718 alloy was experimentally measured by electrostatic levitation technique, where the maximum undercooling of 100 K was realized for the commercial sample. The measured density of liquid lnconel 718 alloy is 7.39 g cm^-3 at the liquidus temperature of 1663 K which was confirmed by DSC experiment, with the linear temperature coefficient of -6.89 × 10^-4 gcm^-3 K^-1. Correspondingly, four ternary Ni-Cr-Fe compositions were designed to simulate the density of liquid lnconel 718 alloy with 16000 atoms, from which the liquid structure is revealed by pair distribution function, The predicted result shows a remarkable enhancement with the decrease of temperature at the first neighbor distance.展开更多
The new technology and equipments used in alumina refinery in PINGGUO ALUMINUM COMPANY were introduced. Problems encountered during early period of its operation and improvements to the process and equipments were dis...The new technology and equipments used in alumina refinery in PINGGUO ALUMINUM COMPANY were introduced. Problems encountered during early period of its operation and improvements to the process and equipments were discussed. Current opemtion situation and pedect technical and economical figures were also introduced.展开更多
基金financially supported by the National Natural Science Foundation of China (Grant Nos. 51327901, 51474175, 51522102 and 51734008)
文摘The density of liquid Incone1718 alloy was experimentally measured by electrostatic levitation technique, where the maximum undercooling of 100 K was realized for the commercial sample. The measured density of liquid lnconel 718 alloy is 7.39 g cm^-3 at the liquidus temperature of 1663 K which was confirmed by DSC experiment, with the linear temperature coefficient of -6.89 × 10^-4 gcm^-3 K^-1. Correspondingly, four ternary Ni-Cr-Fe compositions were designed to simulate the density of liquid lnconel 718 alloy with 16000 atoms, from which the liquid structure is revealed by pair distribution function, The predicted result shows a remarkable enhancement with the decrease of temperature at the first neighbor distance.
文摘The new technology and equipments used in alumina refinery in PINGGUO ALUMINUM COMPANY were introduced. Problems encountered during early period of its operation and improvements to the process and equipments were discussed. Current opemtion situation and pedect technical and economical figures were also introduced.