High cyclic fatigue(HCF)behavior of an AA2139alloy belonging to Al-Cu-Mg-Ag system in T6and T840conditionswas examined.The T840treatment involving cold rolling with a40%reduction prior to peak ageing provides an incre...High cyclic fatigue(HCF)behavior of an AA2139alloy belonging to Al-Cu-Mg-Ag system in T6and T840conditionswas examined.The T840treatment involving cold rolling with a40%reduction prior to peak ageing provides an increase in tensilestrength compared with the T6condition.However,fatigue lifetime for two material conditions was nearly the same since there isweak effect of thermomechanical processing on micro-mechanisms of crack initiation and growth.展开更多
基金a joint project between USATU (Ufa State Aviation Technical University) and UMPO (Ufa Engine Industrial Association), which is entitled “Elaboration and industrial development of high-precision shaping coordinated technologies and superficial hardening of responsible details from Al-alloys with heightened constructional energy efficiency”. This project was implemented under contract No. 40/10-30976/NCh-NCh01-13-KhGthe Ministry of Education and Science of the Russian Federation (contract No.02.G25.31.0010 between UMPO and the Ministry of Education and Science of the Russian Federation) via the Resolution of the Russian Federation Government No.218 from April 9,2010
文摘High cyclic fatigue(HCF)behavior of an AA2139alloy belonging to Al-Cu-Mg-Ag system in T6and T840conditionswas examined.The T840treatment involving cold rolling with a40%reduction prior to peak ageing provides an increase in tensilestrength compared with the T6condition.However,fatigue lifetime for two material conditions was nearly the same since there isweak effect of thermomechanical processing on micro-mechanisms of crack initiation and growth.