A novel green lubricating oil additive(carbon quantum dot(CQD)particle‐doped nickel(Ni‐CQD))was synthesized from citric acid and nickel acetate.The effects of CQD and Ni‐CQD nanoparticles on the tribological behavi...A novel green lubricating oil additive(carbon quantum dot(CQD)particle‐doped nickel(Ni‐CQD))was synthesized from citric acid and nickel acetate.The effects of CQD and Ni‐CQD nanoparticles on the tribological behaviors of polyethylene glycol(PEG200)were investigated under different loads and reciprocation speeds.The results indicate that CQD and Ni‐CQD particles can both enhance the lubrication properties of PEG200.However,the Ni‐CQD nanoparticles enhanced the lubrication properties more than the plain CQD particles did.The average friction coefficient and wear rate of PEG200 containing 2 wt%Ni‐CQDs were reduced by 35.5%and 36.4%,respectively,compared to PEG200 containing pure CQDs under a load of 8 N and reciprocation speed of 25 mm/s over 60 min.The friction and wear mechanisms are attributed to the fact that friction induces the Ni‐CQDs to participate in the formation of a tribofilm,resulting in a low friction coefficient and wear rate.展开更多
基金Financial support from the National Natural Science Foundation of China(Grant No.51505121)Anhui University Outstanding Young Talents Foreign Visiting and Training Program(gxgwfx 2018069)+2 种基金Anhui Provincial Natural Science Foundation(Grant Nos.1608085QE119)Natural Science Foundation Project of the Anhui Education Committee(KJ2017A536)Some of the experimental equipment used in this study in the Birmingham Centre for Cryogenic Energy Storage was obtained with support from the Engineering and Physical Sciences Research Council under the Eight Great Technologies:Energy Storage theme(EP/L017725/1)
文摘A novel green lubricating oil additive(carbon quantum dot(CQD)particle‐doped nickel(Ni‐CQD))was synthesized from citric acid and nickel acetate.The effects of CQD and Ni‐CQD nanoparticles on the tribological behaviors of polyethylene glycol(PEG200)were investigated under different loads and reciprocation speeds.The results indicate that CQD and Ni‐CQD particles can both enhance the lubrication properties of PEG200.However,the Ni‐CQD nanoparticles enhanced the lubrication properties more than the plain CQD particles did.The average friction coefficient and wear rate of PEG200 containing 2 wt%Ni‐CQDs were reduced by 35.5%and 36.4%,respectively,compared to PEG200 containing pure CQDs under a load of 8 N and reciprocation speed of 25 mm/s over 60 min.The friction and wear mechanisms are attributed to the fact that friction induces the Ni‐CQDs to participate in the formation of a tribofilm,resulting in a low friction coefficient and wear rate.