Three-pass friction stir processing(FSP)with different moving distances of the stirring tool between the two successivepasses,50%diameter of the pin(traditional way)and50%diameter of the shoulder(novel way),was conduc...Three-pass friction stir processing(FSP)with different moving distances of the stirring tool between the two successivepasses,50%diameter of the pin(traditional way)and50%diameter of the shoulder(novel way),was conducted on7B04-O Al alloy.The result shows that an improvement in the mechanical properties of the processed zone is accomplished due to grain and secondphase particles refinement.The hardness of the multi-pass FSP(M-FSP)sample is about HV40higher than that of the base metal.And the tensile strength of the M-FSP specimens is also significantly increased to about1.4times that of the base metal.Besides,theweak region of the processed zone is mainly dependent on the moving distance,where it is the previous pass stir zone in thetraditional way and the transitional zone in the novel way.Increasing the rotational speed narrows the weak region in the novel way,while it does not in the traditional way.展开更多
基金support received from the Ministry of Education and Science,Russia,(Belgorod State University project No.1533)is acknowledgedsupport from the National Science Foundation for Young Scientists of China(No.51501035)+1 种基金Chinese Postdoctoral Science Foundation(No.2016T90227)supported financially by the National Natural Science Foundation of China(No.51334006)
文摘Three-pass friction stir processing(FSP)with different moving distances of the stirring tool between the two successivepasses,50%diameter of the pin(traditional way)and50%diameter of the shoulder(novel way),was conducted on7B04-O Al alloy.The result shows that an improvement in the mechanical properties of the processed zone is accomplished due to grain and secondphase particles refinement.The hardness of the multi-pass FSP(M-FSP)sample is about HV40higher than that of the base metal.And the tensile strength of the M-FSP specimens is also significantly increased to about1.4times that of the base metal.Besides,theweak region of the processed zone is mainly dependent on the moving distance,where it is the previous pass stir zone in thetraditional way and the transitional zone in the novel way.Increasing the rotational speed narrows the weak region in the novel way,while it does not in the traditional way.