Cryogenic steels,i.e.,steels with maximum toughness at particularly low temperature,are increasingly becoming the focus of research.Cryogenic steels are usually alloyed with 5%–9%nickel.Ni can also be substituted by ...Cryogenic steels,i.e.,steels with maximum toughness at particularly low temperature,are increasingly becoming the focus of research.Cryogenic steels are usually alloyed with 5%–9%nickel.Ni can also be substituted by manganese as an austenite former.These high-manganese cryogenic grades are a cost-effective alternative to nickel-alloyed steels for use in liquefied natural gas storage tanks.The Mn content can then be more than 20 wt.%and lead to problems in production,particularly in the continuous casting process.In continuous casting of high-Mn-grades,quality issues and even breakout may result from the initial solidification behavior of the steel grades at high temperatures.Hot cracks form when a critical load is exceeded during solidification,close to the solidus temperature of the steel.A selected high-Mn-steel grade was characterized with respect to liquidus and solidus temperatures by means of thermal analysis and computational thermodynamics.In addition,so-called submerged split chill tensile tests were carried out to further understand the crack sensitivity of the solidifying shell for high-manganese cryogenic steels.The results reveal the presence of coarse hot tears,and also,a high frequency of hot cracks was observed at the location with the maximum accumulated strain,which is in line with the applied cracking criterion of Pierer and Bernhard for this investigation.In summary,the initial solidification phase of continuous casting poses a high risk of cracking for high-manganese cryogenic steel.展开更多
High manganese steels can damage the differential thermal analysis （DTA） instrument due to the manganese evaporation during high temperature experiments. After analyzing the relationship between residual oxygen and ...High manganese steels can damage the differential thermal analysis （DTA） instrument due to the manganese evaporation during high temperature experiments. After analyzing the relationship between residual oxygen and manganese evaporation, tanta- lum metal was employed to modify the crucible of DTA, and zirconium getter together with strict gas purification measures were applied to control the volatilization of manganese. By these modifications, problems of thermocouple damage and DTA instrument contamination were successfully resolved. Cobalt samples were adopted to calibrate the accuracy of DTA instruments under the same trial condition of high manganese steel samples, and the detection error was confirmed to be less than 1 ℃. Liquidus and soli- dus temperatures of high Mn steels were measured by improved DTA method. It was found that the liquidus temperatures of sam- ples tested by experiments increased linearly with the heating rates. To eliminate the effects of the heating rate, equilibrium liquidus temperature was determined by fitting the liquidus temperatures at different heating rates, and referred as real liquidus temperature. No clear relationship between solidus temperatures and heating rates was found, and the solidus temperature was finally set as the average value of several experimental data.展开更多
基金supported by National Natural Science Foundation of China(Grant Nos.52174324,51974213 and 52204351)the China Postdoctoral Science Foundation(2022M722487)+1 种基金Open fund project(Grant No.FMRUlab23-05)supported by Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Educationsupport under the scope of the COMET program within the K2 Center“Integrated Computational Material,Process and Product Engineering(IC-MPPE)”(Project No.886385).
文摘Cryogenic steels,i.e.,steels with maximum toughness at particularly low temperature,are increasingly becoming the focus of research.Cryogenic steels are usually alloyed with 5%–9%nickel.Ni can also be substituted by manganese as an austenite former.These high-manganese cryogenic grades are a cost-effective alternative to nickel-alloyed steels for use in liquefied natural gas storage tanks.The Mn content can then be more than 20 wt.%and lead to problems in production,particularly in the continuous casting process.In continuous casting of high-Mn-grades,quality issues and even breakout may result from the initial solidification behavior of the steel grades at high temperatures.Hot cracks form when a critical load is exceeded during solidification,close to the solidus temperature of the steel.A selected high-Mn-steel grade was characterized with respect to liquidus and solidus temperatures by means of thermal analysis and computational thermodynamics.In addition,so-called submerged split chill tensile tests were carried out to further understand the crack sensitivity of the solidifying shell for high-manganese cryogenic steels.The results reveal the presence of coarse hot tears,and also,a high frequency of hot cracks was observed at the location with the maximum accumulated strain,which is in line with the applied cracking criterion of Pierer and Bernhard for this investigation.In summary,the initial solidification phase of continuous casting poses a high risk of cracking for high-manganese cryogenic steel.
基金Sponsored by National Natural Science Foundation of China(51374023)
文摘High manganese steels can damage the differential thermal analysis （DTA） instrument due to the manganese evaporation during high temperature experiments. After analyzing the relationship between residual oxygen and manganese evaporation, tanta- lum metal was employed to modify the crucible of DTA, and zirconium getter together with strict gas purification measures were applied to control the volatilization of manganese. By these modifications, problems of thermocouple damage and DTA instrument contamination were successfully resolved. Cobalt samples were adopted to calibrate the accuracy of DTA instruments under the same trial condition of high manganese steel samples, and the detection error was confirmed to be less than 1 ℃. Liquidus and soli- dus temperatures of high Mn steels were measured by improved DTA method. It was found that the liquidus temperatures of sam- ples tested by experiments increased linearly with the heating rates. To eliminate the effects of the heating rate, equilibrium liquidus temperature was determined by fitting the liquidus temperatures at different heating rates, and referred as real liquidus temperature. No clear relationship between solidus temperatures and heating rates was found, and the solidus temperature was finally set as the average value of several experimental data.
