Anisotropic MnBi/NdFeB （MnBi contents of 0 wt%, 20 wt%, 40 wt%, 60 wt%, 80 wt%, and 100 wt%） hybrid bonded magnets were prepared by molding compression using MnBi powders and commercial hydro-genation disproportiona...Anisotropic MnBi/NdFeB （MnBi contents of 0 wt%, 20 wt%, 40 wt%, 60 wt%, 80 wt%, and 100 wt%） hybrid bonded magnets were prepared by molding compression using MnBi powders and commercial hydro-genation disproportionation desorption and recombination （HDDR） NdFeB powders. Magnetic measurements at room temperature show that with MnBi content increasing, the magnetic properties of the MnBi/NdFeB hybrid bonded magnets all decrease gradually, while the density of the hybrid magnets improves almost linearly. In a temperature range of 293-398 K, the coercivity temperature coefficient of the hybrid magnets improves gradually from -0.59 %.K^-1 for the pure NdFeB bonded magnet to -0.32 %.K^-1 for the hybrid bonded magnet with 80 wt% MnBi, and the pure MnBi bonded magnet exhibits a positive coercivity temperature coefficient of 0.61%-K^-1.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51271005)the Beijing Municipal Natural Science Foundation(No.2122006)+2 种基金the Scientific Research Foundation for the Returned Overseas Chinese Scholars,State Education Ministry(No.32009001201301)the Project from Samsung Advanced Institute of Technology(No.46009001201402)the Fundamental Research Foundation of Beijing University of Technology(No.009000514313002)
文摘Anisotropic MnBi/NdFeB （MnBi contents of 0 wt%, 20 wt%, 40 wt%, 60 wt%, 80 wt%, and 100 wt%） hybrid bonded magnets were prepared by molding compression using MnBi powders and commercial hydro-genation disproportionation desorption and recombination （HDDR） NdFeB powders. Magnetic measurements at room temperature show that with MnBi content increasing, the magnetic properties of the MnBi/NdFeB hybrid bonded magnets all decrease gradually, while the density of the hybrid magnets improves almost linearly. In a temperature range of 293-398 K, the coercivity temperature coefficient of the hybrid magnets improves gradually from -0.59 %.K^-1 for the pure NdFeB bonded magnet to -0.32 %.K^-1 for the hybrid bonded magnet with 80 wt% MnBi, and the pure MnBi bonded magnet exhibits a positive coercivity temperature coefficient of 0.61%-K^-1.