In this study, the allotropic phase transition and its effect on the magnetic behavior of Fe Co–7 wt%V alloy were investigated. It was found that c phase is observed in the microstructure in the as-cast condition, an...In this study, the allotropic phase transition and its effect on the magnetic behavior of Fe Co–7 wt%V alloy were investigated. It was found that c phase is observed in the microstructure in the as-cast condition, and it diminishes after severe cold rolling（90% reduction）. After annealing at temperatures higher than 500 up to 750 ℃, the c phase is observed in the structure, again. But, this phase is disappeared by annealing at temperatures above 750 ℃ due to the formation of vanadium-rich precipitates. Thermocalc software was used in order to elucidate the influence of vanadium percent on the stability of c phase in Fe–Co alloys. Also, magnetic studies showed that the saturation induction is reduced by annealing at temperatures from 500 up to 750 ℃, which is related to the formation of residual non-magnetic γ phase.展开更多
This research aims to investigate the effect of pulsed Nd：YAG laser micro-welding on the microstructure,texture and magnetic properties of ultra-thin Fe-Co-7.15 wt%V magnetic alloy.Optical microscopy,scanning electro...This research aims to investigate the effect of pulsed Nd：YAG laser micro-welding on the microstructure,texture and magnetic properties of ultra-thin Fe-Co-7.15 wt%V magnetic alloy.Optical microscopy,scanning electron microscopy and electron backscattered diffraction techniques were used to study the microstructural evolutions.Also,vibrating sample magnetometry was used to characterize the magnetic properties.The results showed that the fractions of low Σ coincidence site lattice boundaries in the fusion zone are higher than those of the base metal.The welded samples experience a significant decrease in their magnetic properties.It was found that the formation of new fiber texture in the fusion zone and grain coarsening are the most important factors affecting the magnetic properties.展开更多
文摘In this study, the allotropic phase transition and its effect on the magnetic behavior of Fe Co–7 wt%V alloy were investigated. It was found that c phase is observed in the microstructure in the as-cast condition, and it diminishes after severe cold rolling（90% reduction）. After annealing at temperatures higher than 500 up to 750 ℃, the c phase is observed in the structure, again. But, this phase is disappeared by annealing at temperatures above 750 ℃ due to the formation of vanadium-rich precipitates. Thermocalc software was used in order to elucidate the influence of vanadium percent on the stability of c phase in Fe–Co alloys. Also, magnetic studies showed that the saturation induction is reduced by annealing at temperatures from 500 up to 750 ℃, which is related to the formation of residual non-magnetic γ phase.
文摘This research aims to investigate the effect of pulsed Nd：YAG laser micro-welding on the microstructure,texture and magnetic properties of ultra-thin Fe-Co-7.15 wt%V magnetic alloy.Optical microscopy,scanning electron microscopy and electron backscattered diffraction techniques were used to study the microstructural evolutions.Also,vibrating sample magnetometry was used to characterize the magnetic properties.The results showed that the fractions of low Σ coincidence site lattice boundaries in the fusion zone are higher than those of the base metal.The welded samples experience a significant decrease in their magnetic properties.It was found that the formation of new fiber texture in the fusion zone and grain coarsening are the most important factors affecting the magnetic properties.
