Nanometer sized SnO 2 particles were prepared by a sol gel method using inorganic salt as a precursor material. Its crystallization was investigated by means of TG DTA,IR absorption spectra, X ray diffractometry ...Nanometer sized SnO 2 particles were prepared by a sol gel method using inorganic salt as a precursor material. Its crystallization was investigated by means of TG DTA,IR absorption spectra, X ray diffractometry and TEM as well as its resistivity change and the gas sensitivity varied with temperature were measured in various reducing gas. The results indicate that well crystallized nano sized SnO 2 with size around 15nm can be obtained at annealing temperature 600℃. The activation energy for the growth of nano SnO 2 was calculated to be 26.55kJ.mol 1 when the annealing temperature was higher than 500℃. The measurements also show that there is a peculiar resistance change varied with temperature for nano SnO 2.It has relevance to the increase in surface adsorbed oxygen. The selective detectivities to C 4H 10 and petrol can be increased when ruthenium ion was doped in nano SnO 2 as a catalyst and so do the gas sensitivity to CO,CH 4,H 2 etc. when rhodium ion was doped in.The detection to the several reducing gas can be realized when the temperature ranged from 260℃ to 400℃.展开更多
文摘Nanometer sized SnO 2 particles were prepared by a sol gel method using inorganic salt as a precursor material. Its crystallization was investigated by means of TG DTA,IR absorption spectra, X ray diffractometry and TEM as well as its resistivity change and the gas sensitivity varied with temperature were measured in various reducing gas. The results indicate that well crystallized nano sized SnO 2 with size around 15nm can be obtained at annealing temperature 600℃. The activation energy for the growth of nano SnO 2 was calculated to be 26.55kJ.mol 1 when the annealing temperature was higher than 500℃. The measurements also show that there is a peculiar resistance change varied with temperature for nano SnO 2.It has relevance to the increase in surface adsorbed oxygen. The selective detectivities to C 4H 10 and petrol can be increased when ruthenium ion was doped in nano SnO 2 as a catalyst and so do the gas sensitivity to CO,CH 4,H 2 etc. when rhodium ion was doped in.The detection to the several reducing gas can be realized when the temperature ranged from 260℃ to 400℃.