Precipitation condition and nucleation of Ti2O3 during solidification of clean steel have been studied. The behavior of Ti2O3 during solidification as well as possibility of using Ti2O3 to refine as-cast grains as het...Precipitation condition and nucleation of Ti2O3 during solidification of clean steel have been studied. The behavior of Ti2O3 during solidification as well as possibility of using Ti2O3 to refine as-cast grains as heterogeneous nucleation sites is discussed. It is shown that Ti2O3 can be formed provided that the steelmaking and solidification process is controlled strictly. And inoculating clean steel with Ti2O3 is an effective way to refine as-cast grains.展开更多
By using of electrolytic pure iron, the specimens containing different oxide content were made in a Mo wire furnace. The DTA method was employed to measure the undercooling of liquid iron during solidification. The re...By using of electrolytic pure iron, the specimens containing different oxide content were made in a Mo wire furnace. The DTA method was employed to measure the undercooling of liquid iron during solidification. The relations between the cleanness of liquid iron and undercooling, thermodynamic driving force of nucleation, the nucleus forming energy, as well as the critical radius of nucleus have been investigated. The results showed that with the increase of cleanness of liquid iron the undercooling and thermodynamic driving force increased, while the nucleus forming energy and critical radius of nucleus decreased.展开更多
基金Basic Research on New Generation Steel sponsored by National Key Basic Research and Development Programme of China(No.J1998061511-3).
文摘Precipitation condition and nucleation of Ti2O3 during solidification of clean steel have been studied. The behavior of Ti2O3 during solidification as well as possibility of using Ti2O3 to refine as-cast grains as heterogeneous nucleation sites is discussed. It is shown that Ti2O3 can be formed provided that the steelmaking and solidification process is controlled strictly. And inoculating clean steel with Ti2O3 is an effective way to refine as-cast grains.
基金sponsored by National 973 Research Program(No.J1998061511-2).
文摘By using of electrolytic pure iron, the specimens containing different oxide content were made in a Mo wire furnace. The DTA method was employed to measure the undercooling of liquid iron during solidification. The relations between the cleanness of liquid iron and undercooling, thermodynamic driving force of nucleation, the nucleus forming energy, as well as the critical radius of nucleus have been investigated. The results showed that with the increase of cleanness of liquid iron the undercooling and thermodynamic driving force increased, while the nucleus forming energy and critical radius of nucleus decreased.